研究了火花等离子烧结工艺与YG10、YG12两种纳米硬质合金性能的关系.然后采用火花等离子烧结技术制备了硬质合金功能梯度材料,该材料由纳米WC/10%Co、纳米WC/12%Co、微米WC/15%Co混合粉以及不锈钢圆片烧结而成.显微硬度压痕显示该材料各层间的应力较小.     

Influences of sub-micrometer Ta and Co dopants on microstructure and properties of tungsten heavy alloys

Tungsten heavy alloys are aggregates of particles of tungsten bonded with Ni/Fe or Ni/Cu via liquidphase sintering. The sub-micrometer Ta Co powder was added to this aggregate to strengthen the bonding phase. It is found that the main fracture pattern of the alloys is cleavage of tungsten grains and ductile rupture of bond phase,leading to improved tensile strength and elongation. Dopant Ta can act as grain size inhibitor in tungsten heavy alloys.     

基于磁通门磁强计平行分量法的深层涡流检测

采用磁场平行分量法,用磁通门磁强计进行深层涡流检测,该方法通过测量方向与本底磁场垂直的涡流磁场平行分量的方式,能有效避免较强的本底磁场干扰,并能清晰分辨线缺陷与十字形缺陷的特征,对多层铝板的检测深度至少达到14mm,并发现十字形缺陷的涡流磁场信号幅度比线缺陷的涡流磁场信号幅度更强,且随着缺陷深度的增加,其信号幅度衰减速率更慢。     

纳米晶W粉和W-Ni-Fe预合金粉的制备

采用高能球磨法制备纳米晶W粉和W-Ni-Fe预合金粉，研究了不同的球磨材质包括硬质合金球(CCB)、钨球(TAB)和球磨转速、球料比及球磨时间等条件对球磨后粉末性能的影响。利用XRD，TEM和EDX分析球磨后粉末的晶粒尺寸、晶格畸变、形貌、结构变化及颗粒成分变化。结果表明：高能球磨法可制得10nm～80nm的W粉和W-Ni-Fe预合金粉，纳米级颗粒含量达80％以上。相同材质的钨球制得的纳米粉末综合性能较好。球磨过程中，粉末保持颗粒状结构，纳米级粉末颗粒形状最终趋于等轴化。     

火花等离子烧结技术制备的WC／Co为纳米硬质合金

研究了火花等离子烧结工艺与YG10、YGl2两种纳米硬质合金性能的关系。然后采用火花等离子烧结技术制备了硬质合金功能梯度材料，该材料由纳米WC/10％Co、纳米WC／12％C。、微米WC／15％Co混合粉以及不锈钢圆片烧结而成。显微硬度压痕显示该材料各层间的应力较小。     

添加Co,La元素对90W-Ni-Fe合金性能和组织的影响

采用扫描电镜（SEM）、X射线能谱仪（EDS）等，研究在氢气保护、真空烧结条件下添加不同含量的Co、La合金元素对90W-Ni—Fe合金显微组织及性能的影响。结果表明：加入适量的Co、La元素，可以改善粘结相与钨颗粒间的润湿性，La以固溶强化的方式强化钨颗粒及粘结相，从而提高了合金性能。当Co、La元素含量为1．1％（质量分数）时，合金中出现了La的富集与氧的偏析，导致合金性能降低；当添加0．7％的Co、La时，试样强度及伸长率出现极大值，分别为930MPa和24．0％；添加0．5％的Co、La时，试样相对密度出现99．30％的极大值。