芯棒是限动芯棒连轧钢管机组中最重要的热变形工具,其使用效果决定着钢管生产成本的高低。针对芯棒用H13型钢的材料特性,通过对机组变形工艺的分析,提出了使用附加孔型对芯棒使用工艺进行优化的办法,以解决报废芯棒再利用的问题。 相似文献
2.
Aging precipitation and solid solution heat treatment were carried out on three steels which have chromium content of 18%,
manganese content of 12%, 15%, 18%, and nitrogen content of 0.43%, 0.53%, 0.67%, respectively. The mechanisms of precipitation
and solid solution of high nitrogen austenitic stainless steel were studied using the scanning electron microscopy, transmission
electron microscopy, electron probe micro analysis and mechanical testing. The results show that, Cr2N is the primary precipitate in the tested stainless steels instead of Cr23C6. Cr2N nucleates at austenitic grain boundaries and grows towards inner grains with a lamellar morphology. By means of pre-precipitation
of Cr2N at 800 °C, the microstructure of the steels at solid solution state can be refined, thus improving the strength and plasticity.
After the proposed treatment, the tensile strength, the proof strength and the elongation of the tested steel reach 881 MPa,
542 MPa and 54%, respectively. 相似文献
3.
4.
介绍了武钢大型厂生产重轨BS75A时,利用现有设备,通过不断研究,找到了一条提高重轨(BS75A)生产成材率的方法,并取得了较好的经济效益. 相似文献
5.
一种细晶强化金属材料新方法的研究 总被引:1,自引:1,他引:0
晶粒细化是提高金属材料综合力学性能的重要手段之一,通常采用的方法有添加细化剂、快速凝固、振动凝固等铸造方法,以及等通道挤压、累积叠轧焊、异步轧制等塑性变形方法。本文提出一种将剪切变形与传统挤压变形合二为一的挤压方法——不对称挤压方法,即将挤压模口设置在偏离中心的位置上,利用挤压时的较大静水压力和不对称挤压时的剪切变形来细化金属的组织。试验以2A12和2A50铝合金为研究对象,分析研究了不对称挤压前后试样的内部组织、力学性能以及制品的表面质量,考察不对称挤压法的可行性,从而探讨一种可工业化生产的细化组织、提高强度、改善韧性的新的挤压方法。 相似文献
6.
7.
研究了2519铝合金薄板经180℃不同时效状态的性能。结果表明:时效前,合金经冷轧预变形处理后,硬度提高,且随预变形量的增加,合金到达峰值时效的时间缩短;当冷轧变形量在0%~25%之间时,预变形量越大,晶内析出物CuAl2越细小、弥散。固溶温度为530℃,变形量25%,时效温度180℃,时间2.5h时,薄板的力学性能最好。 相似文献