TiAl/Ti/V/Cu/40Cr钢扩散连接界面组织结构对接头强度的影响

研究了TiAl/Ti/V/Cu/40Cr钢的扩散连接，结果显示：在TiAl/Ti界面处形成了对接头强度有利的Ti3Al TiAl双相层及Ti固溶体层，而Ti/V/Cu/40Cr界面处未出现金属间化合物及其它脆性相，接头最高拉伸强度可达420MPa，接近TiAl母材。     

电火花强化过程中两极间质量过渡规律

电火花强化过程中旋转的电极(阳极)向基体材料(阴极)过渡,并与基体材料发生冶金反应,形成新的合金强化层。通过对强化过程中两极重量变化的测定,获得了不同电极材料间的过渡规律及其MTC值;还发现存在着基体材料向电极过渡现象。对不同厚度强化层表面主要化学成分的定量分析,发现大部分电极材料向基体方向过渡。但两极材料的冶金学特性对其过渡过程影响很大。     

FATIGUE CRACK GSOWTH AND CRACK CLOSURE OF SIMULATED OVER-MATCHED WELDED JOINTS

1.~onItiswellknownthatthefatigUefailureisoneofthecornmonfailuresinmetalstructuresincludingweldedstmctures.VariousformulaehavebeensuggestedtopredictfatigUecrackgrowthrates,andthosewidelyusedinpracticeareasfollows:da/dN=cI(AK)acda/dN=c2(ACOD)?/dN=c3(AJ)%FortnulaeaboverelatedfatigUecrackgrowthrate(da/dN)eitherwiththerangeofstressintensityfactor(isK),orwiththerangeofcrackopeningdisplacement(ACOD),orwiththerangeofJ--intendvalue(6J)ofafatigUeloadcycle.However,sincethediscoverybyW.Elb..['…     

THE DESIGN OF AN INTEGRATED SYSTEM FOR PREDICTING AND ANALYZING SOLDER JOINT SHAPE AND RELIABILITY IN SMT

1.IntroductionOnecriticalaspectinelectronicpackagingisthefatigUe/creep--inducedfailureinsolder(tin--leadbasedalloy)interconnections.previouswork,[l--ZJhaveprovedthatthesolderjointreliabilitydependsonthesolderjointshape(amongotherparameters).Manyissueshavefocusedontheresearchaboutsolderjointshapesince90.However,asystematicmethodofpredictingandanalyzingsolderjointshapeandreliability,whichcanheusedindirectingpracticalengineering,isstillnotgiven.Basedontheobject--orientedaPPmach,anintendedsystem…     

焊接速度对铝锂合金搅拌摩擦焊接头断裂特性的影响

对铝锂合金搅拌摩擦焊接头断裂模式随焊接速度提高的变化规律进行了深入的研究。断口实验结果表明 ,在焊接速度低于υ =10 0mm/min时 ,接头断裂模式为沿晶 +穿晶混合型断裂 ;焊接速度提高到υ =2 0 0mm/min时 ,接头断裂模式为韧脆混合型断裂 ;当υ >2 0 0mm/min时 ,随着焊接速度的提高 ,接头断口形貌由存在部分塑性断裂特征变化到完全为脆性断裂特征 ,但接头整体断裂模式为沿晶 +穿晶混合型断裂。力学性能测试结果表明 ,随着焊接速度的提高 ,延伸率先增加 ,并在υ =2 0 0mm/min时达到最大值 ,继续提高焊接速度 ,延伸率下降。     

NUMERICAL SIMULATION OF STRESS-STRAIN DISTRIBUTIONS FOR WELD METAL SOLIDIFICATION CRACKING IN STAINLESS STEEL

1.ItisknownthatweldsolidificationcrackingresultsfromthecompetitionbetweentheInaterialresistancetOcrackingandthemechAncaldrivingforceinthecon-rseofsolidificationOfweldmetal['--sJ.Essentially,weldmetalsolidificationcrackoccurswhenthemechanicaldrivingforceexceedsthematerialresistance.ThedrivingforceisthemechanicaltensilestainthatisdevelOPedinthetrailOfaweldPOolduetOweldmetalsolidificationshrinkage,thennalcontractionoftheparentmetalandtheexternalrestraintoftheweldedstructure.HoWever,analyzing…     

NUMERICAL SIMULATION OF TEMPERATURE FIELDS FOR WELD METAL SOLIDIFICATION CRACKING IN STAINLESS STEELS

1.IntroducsonItisknownthattheweldmetalsolidificationcarkingresultsfromcompetitionbetweenthematerialresistanceandthemechanicaldrivingforceduringthecourseofsolidificationoftheweldmetalllJ.Weldmetalsolidificationcrackingoccurswhenthemechanicaldrivingforceexceedsthematerialresistance.ThematerialresistanceismainlydetendnedbymetallurgicalfactorsandcanbeobtainedbyweldabilitytestssuchastheTrans--VarestraintTest.However,thestudiesonmechAncaldrivingforce,themechAncalstraininthetrailofweldPOOl,areles…     

基于B/S的焊接工艺评定报告管理系统

利用ASP技术设计了一个基于浏览器／服务器(B／S)的焊接工艺评定报告管理系统，实现了焊接工艺评定报告在线编制、查询、浏览、打印和删除等基本功能，使焊接工艺评定报告在internet或intranet上得以共享。     

交流点焊工艺参数对AZ31B镁合金接头性能的影响

研究了AZ31B镁合金交流点焊中焊接电流、电极压力及焊接时间等工艺参数对接头拉剪力的影响规律，确定了最佳工艺参数为焊接电流17000A，电极压力2475N，焊接时间为10个周波，预压时间为20个周波，该条件下接头达到最大拉剪强度为l980N；同时试验得出表面状态对接头性能有着显著的影响。     

激光表面改性Ni基合金/γ-TiAl合金的扩散连接

采用激光表面熔覆技术研究了Ni基合金激光表面熔覆涂层制备工艺及拟连接表面显微组织特征，探讨了TiAl基合金／Ni基合金的超塑扩散连接。研究结果表明，采用激光表面熔覆技术可在Ni基合金表层形成细小的由α2和γ相组成的枝晶组织，其与γ-TiAl合金快速熔凝组织具有相同的组织特征。激光熔覆TiAl合金涂层改善了TiAl基合金与Ni基合金的连接效果，在连接温度900℃、连接压力60MPa和连接时间1h条件下，即可实现TiAl基合金与Ni基合金的连接。