Highly active sites of low spin FeⅡN4species:The identification and the ORR performance

Over recent years,catalytic materials of Fe-N-C species have been recognized being active for oxygen reduction reaction(ORR).However,the identification of active site remains challenging as it generally involves a pyrolysis process and mixed components being obtained.Herein Fe₃C/C and Fe₂N/C samples were synthesized by temperature programmed reduction of Fe precursors in 15%CH₄/H₂and pure NH₃,respectively.By acid leaching of Fe₂N/C sample,only single sites of FeN₄species were presented,providing an ideal model for identification of catalytic functions of the single sites of FeN₄in ORR.A correlation was conducted between the concentration of Fe^ⅡN₄in low spin state by Mossbauer spectra and the kinetic current density at 0.8 V in alkaline media,and such a structure-performance correlation assures the catalytic roles of low spin Fe^ⅡN₄ species as highly active sites for the ORR.     

The formation of fibrous structure of polyamide 6 induced by the three-step forming process and its prominent reinforcement in nitrile rubber

Nitrile rubber (NBR) blends with excellent performance have always been a hot research topic in petroleum field. Due to the excellent performance and compatibility of polyamide 6 (PA6), it provides an opportunity for the preparation of high-performance NBR/PA6 blends. In this article, NBR/PA6 blends were prepared by the three-step molding process. Experimentally, it was found that PA6 has a prominent reinforcement effect in NBR matrix. The variation of this mechanical property was investigated from different aspects of the crystal structure, crystallinities, phase morphology, and so on. It can be cleared that the formation of fibrous structure of PA6 phase is the main factor for reinforcement of the polymer blends. Meanwhile, the formation mechanism of the special phase structure induced by the three-step process is deeply expounded and its structural evolution schematic is established. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47472.     

餐饮废油生物柴油低温流动性的改进研究

使用气-质联用仪测定餐饮废油生物柴油(WCME)和-10号柴油(-10PD)的组成,使用冷滤点试验器和运动黏度试验器测定WCME的低温流动性,同时使用调合、添加低温流动性改进剂的方法改进WCME的低温流动性。实验结果表明,WCME主要由饱和脂肪酸甲酯和不饱和脂肪酸甲酯组成,质量分数分别为27.63%和71.81%;WCME冷滤点为0℃,运动黏度(40℃)为4.41mm2/s;WCME与-10PD调合后,冷滤点降低,其中B20的冷滤点最低,为-13℃,运动黏度随着WCME的体积分数的减少,逐渐接近-10PD的运动黏度。通过添加低温流动性改进剂,WCME,B10,B20的冷滤点分别从0,-8,-13℃降至-4,-26,-25℃。     

Evaluation of bismuth doped La2-xBixNiO4+δ (x = 0, 0.02 and 0.04) as cathode materials for solid oxide fuel cells

Bismuth doped La_2-xBi_xNiO_4+δ (x = 0, 0.02 and 0.04) oxides are investigated as SOFC cathodes. The effects of Bi doping on the phase structure, thermal expansion, electrical conduction behavior as well as electrochemical performance are studied. All the samples exist as a tetragonal Ruddlesden-Popper structure. Bi-doped LBNO-0.02 and LBNO-0.04 have good chemical and thermal compatibility with LSGM electrolyte. The average TEC over 20–900°С was 13.4 × 10^?6 and 14.2 × 10^?6 K^?1 for LBNO-0.02 and LBNO-0.04, respectively. The electrical conductivity was decreasing with the rise of Bi doping content. EIS measurement indicates Bi doping can decrease the ASR values. At 750 °C, the obtained ASR for LBNO-0.04 is 0.18 Ωcm², which is 56% lower than that of the sample without Bi doping, suggesting Bi doping is beneficial to the electrochemical catalytic activity of LBNO cathodes.     

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.