Mixed oxide supported hydrodesulfurization catalysts—a review

Support effects form important aspect of hydrodesulfurization (HDS) studies and mixed oxide supports received maximum attention in the last two decades. This review will focus attention on studies on mixed oxide supported Mo and W catalysts. For convenience of discussion, these are divided into Al₂O₃ containing mixed oxide supports, TiO₂ containing mixed oxide supports, ZrO₂ containing mixed oxide supports and other mixed oxide supports containing all the rest. TiO₂ containing mixed oxides received maximum attention, especially TiO₂–Al₂O₃ supported catalysts. A brief discussion about their prospects for application to ultradeep desulfurization is also included. An overview of the available literature with emphasis on research carried out in our laboratory form the contents of this publication.     

Analysis of spring softening effect on the collapse voltage of capacitive MEMS ultrasonic transducers

Microsystem Technologies - This paper explained the dependency of collapse voltage on semiconductor device structural features (membrane diameter, membrane thickness and the vertical distance...     

Effect of phosphorus on activity of hydrotreating catalyst of Maya heavy crude

The effect of phosphorus on physical properties of the catalyst and on activity of hydrotreating of Maya crude was studied in this work. Catalysts were prepared by the co-impregnation method. Alumina-titania binary oxide was used as a support material. The presence of phosphorus in the catalyst decreases the percentage of micropores, and it results in a decrease of specific surface area. Temperature program reduction (TPR) shows that phosphates reduce metal support interaction. It leads to the formation of polymolybdate phases in expense of strongly bonded tetrahedral molybdates. At higher P loading, polymolybdates may be present with quasi crystalline MoO₃. However, the TPR experiment is not sufficiently sensitive to distinguish several phases present on the catalysts used by the authors. A slight increment of HDM activity is observed, but HDS activity is lower in the P containing catalyst compared with the P free catalyst. The changes of physical properties of the spent catalysts are mainly due to the coke formation on the catalyst. The presence of phosphorus on hydrotreating catalysts inhibits coke formation during the hydrotreating reaction.     

Unconventional Field Dependence of Magnetoresistance of (TMTSF)2ClO4 Studied by 46-T Pulsed Magnetic Field System

A new TTP donor, Me-DH-TTP (2-methyl-5-(1,3-dithiolan-2-yliden)-1,3,4,6-tetrathiapentalene), was designed to realize a system with large on-site Coulomb repulsion as compared with the previously known bis-fused type TTP donors. Probably as a consequence, (Me-DH-TTP)₂AsF₆ exhibits semiconducting behavior from room temperature to liquid helium temperature. By increasing pressure, metallic behavior appears below 300 K, and with distinct metal-insulator (M-I) transition up to 2.2 GPa. This M-I transition suddenly disappears beyond 2.5 GPa, and metallic state is stabilized down to 2.6 K. We discuss the possibility of quantum critical point around 2.4 GPa.     

Electrical conductivity of a novel cast 6351 Al–Al4SiC4 in situ composite

In this research work, electrical conductivity of a novel cast 6351 Al–Al₄SiC₄ composite has been studied for varying Al₄SiC₄ particle content (2–7 vol%). Analytical models were developed on the basis of free electron theory and local resistance approach in order to predict electrical conductivity of metal matrix composites. The electrical conductivity of cast 6351 Al–Al₄SiC₄ composite was found to decrease with increasing Al₄SiC₄ content. Overprediction of results and more % deviation of the predicted electrical conductivity from experimental value were observed for local-resistance-approach-based model. However, the model developed on the basis of electron theory considering scattering of electrons at particle–matrix interface accurately predicted the experimental electrical conductivity data.     

Phase Transformation of Metastable ZnSnO3 Upon Thermal Decomposition by In‐Situ Temperature‐Dependent Raman Spectroscopy

Temperature‐dependent in‐situ Raman spectroscopy is used to investigate the phase transformation of zinc metastannate (ZnSnO₃) to zinc orthostannate (Zn₂SnO₄) induced upon annealing in the ambient. ZnSnO₃ microcubes (MCs) were synthesized at room temperature using a simple aqueous synthesis process, followed by characterization using electron microscopy, X‐ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and thermogravimetric analysis (TGA). Annealing of the ZnSnO₃ MCs was carried out up to 1000°C, while recording the Raman spectra in‐situ at regular intervals. Phase transformation from metastannate to orthostannate was found to begin around 500°C with an activation energy of ~0.965 eV followed by the recrystallization into the inverse spinel orthostannate phase at ~750°C. Results from this study provide detailed understanding of the phase transformation behavior of perovskite ZnSnO₃ to inverse spinel Zn₂SnO₄ upon thermal annealing.     

Comparative study on the structural make-up and mechanical behavior of silicon and silver doped amorphous carbon films

Silicon - Silicon (Si) and silver (Ag) doped amorphous carbon (a-C) thin film were deposited on chrome nitrided 316 LVM stainless steel using filtered cathodic vacuum arc (FCVA) deposition...     

Possibility to Use Hydrothermally Synthesized CuFeS<Subscript>2</Subscript> Nanocomposite as an Acceptor in Hybrid Solar Cell

Here we have approached the plausible use of CuFeS₂ nanocomposite as an acceptor in organic–inorganic hybrid solar cell. To produce CuFeS₂ nanocomposite, hydrothermal strategy was employed. The room-temperature XRD pattern approves the synthesized material as CuFeS₂ with no phase impurity (JCPDS Card no: 37-0471). The elemental composition of the material was analyzed from the TEM-EDX data. The obtained selected area electron diffraction (SAED) planes harmonized with the XRD pattern of the synthesized product. Optical band gap (4.14 eV) of the composite from UV–Vis analysis depicts that the synthesized material is belonging to wide band gap semiconductor family. The HOMO (? 6.97 eV) and LUMO (? 2.93 eV) positions from electrochemical study reveal that there is a possibility of electron transfer from MEH-PPV to CuFeS₂. The optical absorption and photoluminescence spectra of MEH-PPV:CuFeS₂ (donor:acceptor) composite were recorded sequentially by varying weight ratios. The monotonic blue shifting of the absorption peak position indicated the interaction between donor and acceptor materials. The possibility of electron transfer from donor (MEH-PPV) to acceptor (CuFeS₂) was approved with photoluminescence analysis. Subsequently, we have fabricated a hybrid solar cell by incorporating CuFeS₂ nanocomposite with MEH-PPV in open atmosphere and obtained 0.3% power conversion efficiency.     

Effect of Cooling Rate on Microstructure and Mechanical Properties of Eutectoid Steel Under Cyclic Heat Treatment

A systematic study has been carried out to ascertain the effect of cooling rate on structure and mechanical properties of eutectoid steel subjected to a novel incomplete austenitization-based cyclic heat treatment process up to 4 cycles. Each cycle consists of a short-duration holding (6 min) at 775 °C (above A₁) followed by cooling at different rates (furnace cooling, forced air cooling and ice-brine quenching). Microstructure and properties are found to be strongly dependent on cooling rate. In pearlitic transformation regime, lamellar disintegration completes in 61 h and 48 min for cyclic furnace cooling. This leads to a spheroidized structure possessing a lower hardness and strength than that obtained in as-received annealed condition. On contrary, lamellar disintegration does not occur for cyclic forced air cooling with high air flow rate (78 m³ h^?1). Rather, a novel microstructure consisting of submicroscopic cementite particles in a ‘interweaved pearlite’ matrix is developed after 4 cycles. This provides an enhancement in hardness (395 HV), yield strength (473 MPa) and UTS (830 MPa) along with retention of a reasonable ductility (%Elongation = 19) as compared to as-received annealed condition (hardness = 222 HV, YS = 358 MPa, UTS = 740 MPa, %Elongation = 21).