Evaluation of mass loss of weld-deposited hardfacing with cored wire Ti-FeCrC alloy

In this article, we have studied the mass loss of hardfacing applied by flux-cored arc welding. Heat input, shielding gas and number of layers of coating were changed to application of Fe–Cr–Ti–C self-shielded tubular wire. Overlapping beads were deposited on plates of carbon steel AISI 1020 to analyse the mass loss, hardness and microstructure. For the analysis of mass loss, beads were deposited forming overlapping layers of coatings. Hardness measurements were performed on the surface of the specimens of wear. A rubber wheel abrasion tester was used to access the mass loss of coatings. The coatings had retained austenite and martensite microstructure with carbides finely dispersed in the matrix. The main factors that contributed to the increase in mass loss were the cracks due to higher cooling rate of the samples deposited with low heat input, the dilution in the first layer of all samples also contributed to the increase in mass loss. The smallest mass losses were those deposited coatings with high heat input, the second and fourth layers, the samples AC2, AC4 and AS2. The volume fraction of titanium carbides contributed to the decrease in the mean free path between the particles of carbides and increased the wear resistance of the coatings.     

Mass loss and wear mechanisms of HVOF-sprayed multi-component white cast iron coatings

In this work, multi-component white cast iron was applied by HVOF thermal spray process as alternative to other manufacture processes. Effects of substrate type, substrate pre-heating and heat treatment of coating on mass loss have been determined by rubber wheel apparatus in accordance with ASTM G-65. Furthermore, influence of heat treatment of coating on wear mechanisms was also determined by scanning electron microscopy analysis. Heat-treated coatings presented mass loss three times lower than as-sprayed coatings. Furthermore, wear mechanisms of as-sprayed coating are micro-cutting associated with cracks close to unmelted particles and pores. In heat-treated coating, lesser mass loss is due to sintering.     

Influence of parameters of the HVOF thermal spray process on the properties of multicomponent white cast iron coatings

High velocity oxi-fuel (HVOF) thermal spray process has been used in order to deposit a new alloy known as multicomponent white cast iron. The coatings were characterized in terms of macrostructure, phase composition, porosity and hardness. Coating characteristics and properties were found to be dependent on the particles size range, spray distance, gases flow rate and oxygen to propane ratio. For set of parameters utilized in this job a narrow particle size range between 20 and 45 μm with a spray distance of 200 mm and oxygen to propane ratio of 4.6 are the preferred coating parameters. Coating porosity of 0.9% and hardness of 766 HV were obtained under these conditions.     

Bond Strength of Multicomponent White Cast Iron Coatings Applied by HVOF Thermal Spray Process

Multicomponent white cast iron is a new alloy that belongs to system Fe-C-Cr-W-Mo-V, and because of its excellent wear resistance it is used in the manufacture of hot rolling mills rolls. To date, this alloy has been processed by casting, powder metallurgy, and spray forming. The high-velocity oxyfuel process is now also considered for the manufacture of components with this alloy. The effects of substrate, preheating temperature, and coating thickness on bond strength of coatings have been determined. Substrates of AISI 1020 steel and of cast iron with preheating of 150 °C and at room temperature were used to apply coatings with 200 and 400 μm nominal thickness. The bond strength of coatings was measured with the pull-off test method and the failure mode by scanning electron microscopic analysis. Coatings with thickness of 200 μm and applied on substrates of AISI 1020 steel with preheating presented bond strength of 87 ± 4 MPa.