Transient liquid phase sintering of high-purity mullite for high-temperature structural ceramics

High-purity mullite ceramics, promising engineering ceramics for high-temperature applications, were fabricated using transient liquid phase sintering to improve their high-temperature mechanical properties. Small amounts of ultrafine alumina or silica powders were uniformly mixed with the mullite precursor depending on the silica-alumina ratio of the resulting ceramics to allow for the formation of a transient liquid phase during sintering, thus, enhancing densification at the early stage of sintering and mullite formation by the reaction between additional alumina and the residual glassy phase (mullitization) at the final stage of sintering. The addition of alumina powder to the silica-rich mullite precursor resulted in a reaction between the glassy silica and alumina phases during sintering, thereby forming a mullite phase without inhibiting densification. The addition of fine silica powder to the mullite single-phase precursor led to densification with an abnormal grain growth of mullite, whereas some of the added silica remained as a glassy phase after sintering. The resulting mullite ceramics prepared using different powder compositions showed different sintering behaviors, depending on the amount of alumina added. Upon selecting an optimum process and the amount of alumina to be added, the pure mullite ceramics obtained via transient liquid phase sintering exhibited high density (approximately 99%) and excellent high-temperature flexural strength (approximately 320 MPa) at 1500 °C in air. These results clearly demonstrate that pure mullite ceramics fabricated via transient liquid phase sintering with compositions close to those of stoichiometric mullite could be a promising process for the fabrication of high-temperature structural ceramics used in an ambient atmosphere. The transient liquid phase sintering process proposed in this study could be a powerful processing tool that allows for the preparation of superior high-temperature structural ceramics used in the ambient processing atmosphere.     

Re-evaluation of Radiation-Energy Transfer to an Extraction Solvent in a Minor-Actinide-Separation Process Based on Consideration of Radiation Permeability

ABSTRACT

Absorbed-dose estimation is essential for evaluation of the radiation tolerance of minor-actinide-separation processes. We propose a dose-evaluation method based on radiation permeability, with comparisons of heterogeneous structures seen in the solvent-extraction process, such as emulsions forming in the mixture of the organic and aqueous phases. A demonstration of radiation-energy-transfer simulation is performed with a focus on the minor-actinide-recovery process from high-level liquid waste with the aid of the Monte Carlo radiation-transport code PHITS. The simulation results indicate that the dose absorbed by the extraction solvent from alpha radiation depends upon the emulsion structure, and that from beta and gamma radiation depends upon the mixer-settler-apparatus size. Non-negligible contributions of well-permeable gamma rays were indicated in terms of the plant operation of the minor-actinide-separation process.     

Dynamic probe of ZnTe(110) surface by scanning tunneling microscopy

The reconstructed surface structure of the II–VI semiconductor ZnTe (110), which is a promising material in the research field of semiconductor spintronics, was studied by scanning tunneling microscopy/spectroscopy (STM/STS). First, the surface states formed by reconstruction by the charge transfer of dangling bond electrons from cationic Zn to anionic Te atoms, which are similar to those of IV and III–V semiconductors, were confirmed in real space. Secondly, oscillation in tunneling current between binary states, which is considered to reflect a conformational change in the topmost Zn–Te structure between the reconstructed and bulk-like ideal structures, was directly observed by STM. Third, using the technique of charge injection, a surface atomic structure was successfully fabricated, suggesting the possibility of atomic-scale manipulation of this widely applicable surface of ZnTe.     

Radiophotoluminescence phenomenon in copper-doped aluminoborosilicate glass

Radiophotoluminescence phenomena have been widely investigated on various types of materials for dosimetry applications. We report that an aluminoborosilicate glass containing 0.005 mol% copper exhibits intense photoluminescence in the visible region induced by X-ray and γ-ray irradiation. The luminescence is assigned to the 3d⁹4s¹ → 3d¹⁰ transition of Cu⁺. The proportionality of the intensity of the induced photoluminescence to the irradiation dose was confirmed up to 0.5 kGy using ⁶⁰Co γ-ray irradiation. Based on the spectroscopic results, a potential mechanism was proposed for the enhancement of the photoluminescence. The exposure to the ionizing radiation generates electron-hole pairs in the glass, and the electrons are subsequently captured by the Cu²⁺ ions, which are converted to Cu⁺ and emit the luminescence. For the glass containing 0.01 mol% copper, the pronounced enhancement of the photoluminescence was not observed because the reverse reaction, ie, the capture of the holes by the Cu⁺ ions, becomes prominent. The photoluminescence induced by the irradiation was stably observed for the glasses kept at room temperature and even for the glasses heat-treated at 150°C. However, the induced photoluminescence could be eliminated by the heat treatment at a temperature at 500°C, and the glass returned to the initial pre-irradiation state. The Cu-doped aluminoborosilicate glass is a potential candidate for use in dosimetry applications.     

Supramolecular Zn(II)-Dipicolylamine-Azobenzene-Aminocyclodextrin-ATP Complex: Design and ATP Recognition in Water

Cyclodextrins (CyDs) are water-soluble host molecules possessing a nanosized hydrophobic cavity. In the realm of molecular recognition, this cavity is used not only as a recognition site but also as a reaction medium, where a hydrophobic sensor recognizes a guest molecule. Based on the latter concept, we have designed a novel supramolecular sensing system composed of Zn(II)-dipicolylamine metal complex-based azobenzene (1-Zn) and 3A-amino-3A-deoxy-(2AS,3AS)-γ-cyclodextrin (3-NH₂-γ-CyD) for sensing adenosine-5′-triphosphate (ATP). 1-Zn showed redshifts in the UV-Vis spectra and induced circular dichroism (ICD) only when both ATP and 3-NH₂-γ-CyD were present. Calculations of equilibrium constants indicated that the amino group of 3-NH₂-γ-CyD was involved in the formation of supramolecular 1-Zn/3-NH₂-γ-CyD/ATP. The Job plot of the ICD spectral response revealed that the stoichiometry of 1-Zn/3-NH₂-γ-CyD/ATP was 2:1:1. The pH effect was examined and 1-Zn/3-NH₂-γ-CyD/ATP was most stable in the neutral condition. The NOESY spectrum suggested the localization of 1-Zn in the 3-NH₂-γ-CyD cavity. Based on the obtained results, the metal coordination interaction of 1-Zn and the electrostatic interaction of 3-NH₂-γ-CyD were found to take place for ATP recognition. The “reaction medium approach” enabled us to develop a supramolecular sensing system that undergoes multi-point interactions in water. This study is the first step in the design of a selective sensing system based on a good understanding of supramolecular structures.     

Distribution of carbon contamination in MgAl2O4 spinel occurring during spark-plasma-sintering (SPS) processing: I – Effect of heating rate and post-annealing

Carbon contamination from the carbon paper/dies during spark-plasma-sintering (SPS) processing was examined in the MgAl₂O₄ spinel. The carbon contamination sensitively changes with the heating rate during the SPS processing. At the high heating rate of 100 °C/min, the carbon contamination having organized structures occurred over almost the entire area from the surface to deep inside the SPSed spinel disk. In contrast, at the slow heating rate of 10 °C/min, the carbon contamination having disordered structures occurred only around the surface area. The carbon phases transform into high pressure CO/CO₂ gases by post-annealing in air and lead to pore formation along the grain junctions. The pore formation significantly occurs at the high heating rate due to the large amount of the contaminant carbon phases. This suggests that if once the carbon contamination was formed in the materials, it is very difficult to remove the carbon phases from the materials.     

Eu@C86 isomers: Calculated relative populations

Abstract

Relative populations of four energy-lowest IPR (isolated-pentagon-rule) isomers of Eu@C₈₆ are computed using the Gibbs energy based on characteristics from density functional theory calculations (M06-2X/3-21G?～?SDD entropy term, M06-2X/6-31G*～SDD or B2PLYP(D)/6-31G*～SDD energetics). The calculations confirm that the recently isolated Eu@C₁(7)-C₈₆ species is a major isomer in a relevant temperature region. Relationship to the empty C₈₆ cages is discussed, too.     

Matrix influence on the piezoelectric properties of piezoelectric ceramic/polymer composite exhibiting particle alignment

This study was addressed to the influence of an electric field strength applied at fabrication process and matrix properties, such as the dielectric constant and the Young's modulus, on “pseudo‐1‐3 piezoelectric ceramic/polymer composite” in order to further enhance the piezoelectricity of that. The pseudo‐1‐3 piezoelectric ceramic/polymer composite consists of linearly ordered piezoelectric ceramic particles in polymer material. Silicone gel, silicone rubber, urethane rubber, and poly‐methyl‐methacrylate, which exhibit different dielectric constants and Young's modulus, were used as matrices to evaluate the matrix influence. The piezoelectricity of the pseudo‐1‐3 piezoelectric ceramic/polymer composite was evaluated using the piezoelectric strain constant d₃₃. The d₃₃ is one of the indices of the piezoelectric properties for piezoelectric materials. As a result, it was confirmed that d₃₃ of the pseudo‐1‐3 piezoelectric ceramic/polymer composite increased with the increase of the electric filed strength applied at fabrication process, though, it reached a constant value at a certain strength value. Further it was confirmed that dielectric constant of the matrix had a small influence on d₃₃ of the pseudo‐1‐3 piezoelectric ceramic/polymer composite, however, in case of matrix of lower Young's modulus, d₃₃ was increase. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41817.