You Zhi-yong Jiang Ao-xue Duan Zhuang-zheng Qiao Gang-ping Gao Jing-lei Guo Ling-bing 《中国铸造》2020,17(3):219-226
Semi-solid AZ91D magnesium alloy billets were prepared by near-liquidus heat holding. Semi-solid squeeze casting was conducted at 575, 585 and 595 ℃, respectively, with 1 mm·s~(-1) squeeze speed. The semisolid squeeze casting AZ91D samples were heat treated by T4(solution at 415 ℃ for 24 h) and T6(solution at 415 ℃ for 24 h + 220 ℃ for 8 h) processes, respectively. The microstructure and mechanical properties of the alloy in different states were investigated by means of OM, SEM and tensile testing machine. The results show that compared to as-cast alloy, the grain size of the semi-solid squeezed AZ91D decreased significantly, and with the increase of semi-solid squeeze temperature, the grain size of AZ91D increased. The grains of the alloy were refined by T4 treatment, and further refined by T6 treatment. T6 treatment greatly improved the tensile strength, elongation, and hardness, but did not significantly improve yield strength. After 575 ℃ squeeze casting and T6 treatment, the ultimate tensile strength(UTS) reached 285 MPa, the elongation reached 13.36%, and the hardness also reached the maximum(106.8 HV), but the yield strength(YS) was only 180 MPa. During the process of semi-solid squeeze casting and heat treatment, the matrix grain was refined and a large number of precipitated and secondary precipitated phases of Mg_(17)Al_(12) appeared. Both the average size of matrix grain and secondary precipitated phase decreased, while the volume fraction of secondary precipitated phase increased. All these resulted in high tensile strength, elongation and hardness. 相似文献
2.
Ao-xue Jiang Zhi-yong You Zhuang-zheng Duan Gang-ping Qiao Jin-shan Zhang Ling-bing Guo 《中国铸造》2021,18(6):565-573
AZ91D and 8.5vol.% SiCp/AZ91D magnesium matrix composites were fabricated by a semi-solid extruded processing method,and treated with solution and aging heat treatment.The effects of SiCp on the microstructures of the semi-solid extruded AZ91D magnesium alloy during recrystallization were studied by observing and analyzing the microstructure evolution during extrusions and heat treatments.The results show that the addition of SiCp inhibits the dynamic recrystallization of AZ91D during the semi-solid extrusion with only 26% of the volume fraction of recrystallization.Furthermore,the addition of SiCp refines the sizes of grains and second phases,and upgrades the volume fraction of second phase.After solution and aging treatment,the recrystallization continues,and the addition of SiCp promotes the recrystallization and the recrystallized microstructure is much more stable.Meanwhile,the sizes of grains and second phases continue to be refined,and the volume fraction of second phases continues to increase. 相似文献
3.
为了获得综合力学性能良好的镁基复合材料,采用近液相线保温法制备10 μm 15%SiC/AZ91D(质量分数)半固态坯料进行半固态挤压后得到其复合材料,再经过415℃固溶处理24 h(T4)和进一步220℃时效处理8 h(T6).结果表明:随着固溶时效的进行,晶界处的层片状和点状Mg17Al12相溶解,然后在晶粒中二次... 相似文献