Fabrication of barium titanate ceramics via digital light processing 3D printing by using high refractive index monomer

A digital light processing (DLP) technology has been developed for 3D printing lead-free barium titanate (BTO) piezoelectric ceramics. By comparing the curing and rheological properties of slurries with different photosensitive monomer, a high refractive index monomer acryloyl morpholine (ACMO) was chosen, and a design and preparation method of BTO slurry with high solid content, low viscosity and high curing ability was proposed. By further selecting the printing parameters, the single-layer exposure time was reduced and the forming efficiency has been greatly improved. Sintered specimens were obtained after a nitrogen-air double-step debinding and furnace sintering process, and the BTO ceramics fabricated with 80 wt% slurry shows the highest relative density (95.32 %) and piezoelectric constant (168.1 pC/N). Furthermore, complex-structured BTO ceramics were prepared, impregnated by epoxy resin and finally assembly made into hydrophones, which has significance for the future design and manufacture of piezoelectric ceramic-based composites that used in functional devices.     

Facile preparation and strong adhesive strength of honeycomb polyurethane films with small pore diameter

With the continuous development of bionics, such as, geckos and virginia creeper with both superhydrophobic and super-adhesive, the surface wetting and super-adhesive properties of various porous materials have attracted extensive attention of the scientific and medical communities. Here, the honeycomb polyurethane (PU) porous films with strong adhesion were successfully prepared by microphase separation method and the effects of growth parameters on their microstructure and adhesive strength to ice were investigated. It was found that a high relative humidity (e.g., 100%) and a low solution concentration (e.g., 2%) facilitated the formation of ordered honeycomb PU porous films, and as-prepared PU pores with average pore diameter as small as 5 μm are better ordered and more uniform than these in related documents. Although the contact angle of water droplets on the surface of PU porous films increased from the premodification value of 85–130° to more than 160° after surface modification with polydopamine (PDA), the corresponding rolling angle remained approximately constant (180°), indicating that the surface of PU porous films has strong adhesion similar to geckos and virginia creeper. Furthermore, at lower temperature, the PU porous films exhibited the high adhesive strength of 142.13 kPa on ice, which was strongly dependent on the porous microstructures and surface compositions. The improved adhesive behavior to ice of honeycomb PU porous films modified with PDA provides new strategies for surface modification of materials and potential applications in medical domain.     

Organic Semiconducting Luminophores for Near-Infrared Afterglow,Chemiluminescence, and Bioluminescence Imaging

Optical imaging has played a pivotal role in deciphering in vivo bioinformatics but is limited by shallow penetration depth and poor imaging performance owing to interfering tissue autofluorescence induced by concurrent photoexcitation. The emergence of near-infrared (NIR) self-luminescence imaging independent of real-time irradiation has timely addressed these problems. There are two main kinds of self-luminescent agents, namely inorganic and organic luminophores. Inorganic luminophores usually suffer from long-term biotoxicity concerns resulting from potential heavy-metal ions leakage and nonbiodegradability, which hinders their further translational application. In contrast, organic luminophores, especially organic semiconducting luminophores (OSLs) with good biodegradable potential, tunable design, and outstanding optical properties, are preferred in biological applications. This review summarizes the recent progress of OSLs used in NIR afterglow, chemiluminescence, and bioluminescence imaging. Molecular manipulation and nanoengineering approaches of OSLs are discussed, with emphasis on strategies that can extend the emission wavelength from visible to NIR range and amplify luminescence signals. This review concludes with a discussion of current challenges and possible solutions of OSLs in the self-luminescence field.     

The surface carboxyl group of carbonaceous microspheres effects on the synthesis and structure of SiOC ceramics

In this study, C/SiOC and C/SiO₂ composites were prepared by using carbonaceous microspheres with different surface functional groups. Carbonaceous microspheres based on hydrothermal reaction of glucose contains hydroxyl group, while the surface carboxyl group increases after NaOH etching. The hydroxyl group increases the oxygen-enriched structural units of SiOC ceramics, and the C spheres are closely enwrapped in SiOC matrix after pyrolysis at 900 °C. However, the interfacial reaction of surface carboxyl with Si–OH results in the formation of cristobalite SiO₂, and C spheres are not only encased inside the SiOC matrix, but also dispersed outside of SiOC ceramics. After removal of C via calcination at 500 °C for 5 h, C/SiOC and C/SiO₂ composites are transformed into amorphous SiO₂ and cristobalite SiO₂, respectively. The thermogravimetric analysis indicates the oxidation resistance of SiOC is superior to that of C and SiO₂.     

One step method of structure engineering porous graphitic carbon nitride for efficient visible-light photocatalytic reduction of Cr(Ⅵ)

Porous g-C3N4 nanosheets (PCN) were prepared by the nickel-assisted one-step thermal polymerization method.Hydrogen (H2) which was produced by the reaction between nickel (Ni) foam and ammonia (NH3) defined the structure and properties of PCN.During the formation of PCN,the participation of H2 not only enhanced the spacing between layers but also boosted the specific surface area that more active sites were exposed.Additionally,H2 promoted pores formation in the nanosheets,which was beneficial to the transfer of photons through lamellar structure and improved the absorption efficiency of visible light.Remarkably,the obtained PCN possessed better Cr(Ⅵ) photocatalytic reduction efficiency than pure g-C3N4.The reaction rate constant (k) of PCN (0.013 min-1) was approximately twice that of bare g-C3N4 (0.007 min-1).Furthermore,the effects of original pH and concentration of Cr(Ⅵ)-containing solution on removal efficiency of Cr(Ⅵ) were explored.A possible photocatalytic mechanism was proposed based on the experiments of radical scavengers and photoelectrochemical characterizations.     

一株产羧酸酯酶菌的鉴定及酯酶特征的研究

目的:鉴定中国白酒发酵过程中的微生物种类，研究关键酶的特征与作用机制有利于提高白酒的优质品率。方法:本研究用形态学和生理学、16S rRNA、gyr B基因和antiSMASH分析的方法对酒曲中的一株微生物进行了验证；对该菌株的特性进行了研究，采用分子建模的方法获得了羧酸酯酶的3D模型，用分子对接的方法探讨了该菌株的羧酸酯酶的机理。结果:该菌株为产羧酸酯酶的革兰氏阴性菌Pb1（MW580690）；该菌株呈现典型的S型生长曲线，产物曲线为S型，羧酸酯酶活化最优pH范围为5.0~9.0。分子对接结果显示Phe21A为该酶具有催化活性的主要氨基酸，水解三丁酸甘油酯为丁酸和甘油。分子对接结果显示三丁酸甘油酯经过构象变化被转移到催化中心后，进一步被加工；酶的亲水性和疏水性的相互作用表面有利于配体向下转移，进而从疏水性通道释放产物到的酶表面。结论:产羧酸酯酶的菌株为贝莱斯芽胞杆菌，并为羧酸酯酶水解三丁酸甘油酯类物质的底物识别、转移和催化机理提供了新的见解。     

iRGD-reinforced,photo-transformable nanoclusters toward cooperative enhancement of intratumoral penetration and antitumor efficacy

Nano Research - Insufficient intratumoral penetration greatly hurdles the anticancer performance of nanomedicine. To realize highly efficient tumor penetration in a precisely and spatiotemporally...     

济阳坳陷下古生界潜山油气藏特征及成藏模式

济阳坳陷下古生界潜山具有多样性、复杂性的特点，潜山差异性的形成演化、油气成藏主控因素和控藏模式不明确，严重制约了该区潜山油气勘探。在潜山分类的基础上，综合利用系统恢复、分类对比和典型解剖等方法，揭示了济阳坳陷下古生界不同类型潜山的形成演化过程和油气成藏主控因素差异性，分类建立了油气成藏模式。研究表明，济阳坳陷下古生界主要发育高位新盖侵蚀残丘潜山、中位古盖拉张断块潜山、中位新古盖拉张剪切断块潜山、中位中古盖挤压拉张断块潜山和低位古盖拉张滑脱断块潜山5种潜山类型。不同类型潜山的形成演化和油气成藏各具特色，其中，高位新盖侵蚀残丘潜山的发育受隆升、侵蚀作用控制，油气成藏主要受控于油源和盖层条件，表现为"单向供烃、砂体-不整合岩溶体联合输导、残丘控藏"的成藏模式；中位古盖拉张断块潜山的发育受掀斜、断裂作用控制，油气成藏主要受控于储集条件，表现为"单向供烃、顺向断层输导、反向断层控藏"的成藏模式；中位新古盖拉张剪切断块潜山的发育受反转、翘倾和走滑切割作用控制，油气成藏主要受控于输导条件，表现为"多源供烃、断溶体立体输导、断裂控藏"的成藏模式；中位中古盖挤压拉张断块潜山的形成受强烈挤压、拉张滑脱作用控制，油气成藏主要受控于储集条件，表现为"多源供烃、断缝体输导、断褶控藏"的成藏模式；低位古盖拉张滑脱断块潜山的形成受强烈拉张滑脱作用控制，油气成藏主要受控于输导条件，表现为"顶部供烃、断缝体输导、断裂控藏"的成藏模式。