中模数锥齿轮整体多次预热的高频淬火

一、问题的提出我公司为安阳钢厂及孝义钢厂生产的辊道锥齿轮,模数ｍ为１２,齿数为１４,要求齿面硬度ＨＲＣ４２－４８。对于锥齿轮的表面硬化,大多采用化学热处理或感应加热淬火。由于感应设备的频率不一样,又分成整体加热（包全齿）淬火工艺和沿齿沟或单齿淬火工艺,而对中模数的锥齿轮,用中频整体加热淬火工艺较为理想。由于我公司没有中频设备,为达到齿面硬度要求,我公司在高频设备上进行整体多次预热的高频淬火工艺试验和实践,取得较好的效果。二、整体多次预热高频淬火工艺及设备锥齿轮的整体结构如图１所示。由于高频淬火集…     

高效液相色谱与电喷雾质谱联用鉴定罗布麻叶中的黄酮类化合物

Identification of the flavonoids from natural plant of Apocynum venetum leaves with HPLC-ESI-MS was established. The compositions of its extract were detected by the high-performance liquid chromatography, and eight chromatography peaks obviously were tested. Then the sample of crude extract was measured by HPLC-ESI-MS, eight compounds was examined. The characteristic ions and fragment reaction were analyzed. HPLC-ESI-MS was a rapid and effective method for identifying compounds from natural plant.     

消除灰铸铁白口的等温正火热处理工艺

在灰铸铁零件的生产过程中 ,由于铸造工艺或操作控制不当 ,产生硬度高、脆性大的白口有时是难以避免的。这种白口在金相显微镜下可见大量的自由渗碳体、大块状的莱氏体组织。我公司为热电厂生产的风门 ,就曾多次出现铸件白口的情况。该零件是用 HT15- 30铸造的 ,其化学成分 ( w,% )为 :3.2～ 3.4 C,2 .0～ 2 .3Si,0 .8～ 1.0 Mn,≤ 0 .3P,≤ 0 .12 S;要求硬度 170～ 2 10HB,抗拉强度 >15MPa,抗弯强度 >15MPa。由于出现白口而无法进行机械加工。为了改善加工性能采取传统的退火工艺 ,一方面工艺成本高 ,另一方面无法彻底消除白口而报废…     

建筑施工中混凝土裂缝控制技术的探讨

当今时代,在建筑施工的过程中混凝土裂缝是最严重的困难和形势,要想整个项目顺利的完成,就必须要解决混凝土裂缝问题。本文主要首先简明阐述了混凝土,然后针对建筑施工中混凝土裂缝产生的原因做出了具体的补救措施。     