Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

In situ Raman spectroscopic study towards the growth and excellent HER catalysis of Ni/Ni(OH)2 heterostructure

The electrochemical water splitting to produce H₂ in high efficiency with earth-abundant-metal catalysts remains a challenge. Here, we describe a simple “cyclic voltammetry + ageing” protocol at room temperature to activate Ni electrode (AC-Ni/NF) for hydrogen evolution reaction (HER), by which Ni/Ni(OH)₂ heterostructure is formed at the surface. In situ Raman spectroscopy reveals the gradual growth of Ni/Ni(OH)₂ heterostructure during the first 30 min of the aging treatment and combined with polarization measurements, it suggests a positive relation between the Ni/Ni(OH)₂ amount and HER performance of the electrode. The obtained AC-Ni/NF catalyst, with plentiful Ni–Ni(OH)₂ interfaces, exhibits remarkable performance towards HER, with the low overpotential of only 30 mV at a H₂-evolving current density of 10 mA/cm² and 153 mV at 100 mA/cm², as well as a small Tafel slope of 46.8 mV/dec in 1 M KOH electrolyte at ambient temperature. The excellent HER performance of the AC-Ni/NF could be maintained for at least 24 h without obvious decay. Ex situ experiments and in situ electrochemical-Raman spectroscopy along with density functional theory (DFT) calculations reveal that Ni/Ni(OH)₂ heterostructure, although partially reduced, can still persist during HER catalysis and it is the Ni–Ni(OH)₂ interface reducing the energy barrier of H1 adsorption thus promoting the HER performance.     

负载型复合载体及其镍基催化剂的性能

采用溶胶-凝胶法制备了负载型ZrO_2/Al_2O_3和ZrO_2/Al_2O_3-SiO_2复合载体,研究了不同复合载体对Ni基催化剂CO_2重整甲烷反应和性能的影响,并用XRD、IR、TPR、TPD和BET等方法对复合载体及催化剂进行了表征。结果表明,ZrO_2负载在基载体后比表面积、碱性、活性组分Ni的分散度和Ni与ZrO_2的相互作用增大。NiO在复合载体表面的分散容量与ZrO_2的负载量有关,ZrO_2的负载量为37．5%时NiO的分散容量达最高值(24．0%)。与Ni/ZrO_2相比,Ni/ZrO_2/Al_2O_3-SiO_2和Ni/ZrO_2/Al_2O_3催化剂对CO_2的吸附能力增大,CO_2吸附量增加,酸强度降低,CO_2重整CH_4反应活性提高,其中以Ni/ZrO_2/Al_2O_3催化剂的活性最好。     

热声制冷机及其改进实验研究

热声制冷作为一种很有前途的制冷方法，在国内外相关领域引起了极大兴趣。热声制冷机由声发生器、共振管、板叠及高、低温换热器等部分组成。对声驱动器的振动膜及其冷却系统、气体弹簧系统、高、低温换热器进行了初步改进，使制冷机冷端温降从原来的12℃提高到27℃左右，这是目前国内报道的最大温降。     

类胡萝卜素的命名

本根据国际理论与应用化学协会(IUPAC)所制定的命名规则和国际上认可的习惯名称，对类胡萝卜素的命名进行了详细的说明。     

应用于生物医学的光声光谱技术的改进和实验研究

改进的光声光谱归一化技术，避免了普通的分光法归一化光声光谱技术中分束镜以及锁相放大器动态范围的影响和限制，实现宽光谱范围内准确的光谱测量。氙灯光源功率起伏用修正项修正，误差在5％以内，实现各次实验数据的可比性。     

可再生烟气脱硫吸收剂及工艺研究

开发了一种新型可再生烟气脱硫吸收剂、解吸助剂及工艺。合成的吸收剂LDS对烟气中的SOx 具有良好的吸收和解吸能力 ,烟气中SOx 含量在 10 0 0～ 5 0 0 0 0 μg L范围内 ,脱硫率均可达 95 %以上 ;解吸助剂LDS A能有效提高主吸收剂LDS的解吸能力 ,提高单位吸收剂的吸收效率。试验表明 :该工艺脱硫率高 ,烟气净化效果好 ,与传统的烟气脱硫工艺相比 ,SOx 可回收利用 ,不产生二次污染     

花坝二级电站引水隧洞混凝土裂缝成因与对策

混凝土的裂缝问题是一个普遍存在而又难于解决的工程实际问题，现对花坝二级电站引水隧洞工程中衬砌混凝土出现裂缝的原因进行分析，并针对出现的混凝土裂缝的具体情况，提出一些简单的预防和处理对策。     

井下原地溶浸技术试验研究

结合东同矿业公司井下原地溶浸的试验研究情况,分析了细菌浸出-萃取-电积工艺过程中存在的问题并提出了解决方法,探讨了该工艺应用研究的发展方向与前景。     

我国内螺纹铜管的生产技术与发展方向

本文论述了我国内螺纹铜管业生产、工艺、产品技术条件、齿型及市场现状 ,提出了内螺纹铜管的研发方向。