Transparency and toughness characterization of epoxy resins modified with liquid chloroprene rubber

Transparent epoxy resins modified with liquid chloroprene rubber (LCR), containing in a category of rubber-toughened resin were found. Transparency and toughness characterization of the modified epoxy resins were investigated as a function of LCR content. Epoxy resins modified with 0–10 vol % LCR showed complete phase-separation microstructure. However, these modified resins were transparent, because the refractive index of LCR was compatible with that of the epoxy resin matrix at room temperature. On the other hand, it was observed that above 10 vol % LCR, a certain amount of LCR dissolved into the epoxy matrix. In this case, the glass transition temperature decreased with increasing LCR content. It was also found that the critical stress intensity factor, K _c, of the modified epoxy resins exhibited a maximum between 10 and 15 vol % LCR.     

Structure of microporous polypropylene sheets containing CaCO3 filler

The microporous polypropylene sheets were prepared by biaxially stretching polypropylene sheets containing CaCO₃ filler (particle size, 0.08–3.0 μm), when the CaCO₃ filler content was 59% by weight and the stretching ratio was 2.8 × 1.8. The microstructure of the sheets were investigated in relation to the CaCO₃ particle size by a N₂ gas permeation method. (1) Effective porosity increases with decreasing mean particle size of filler. (2) The tortuosity factor of the pore is in the range of 25–40 and becomes relatively smaller with decreasing mean particle size of filler. (3) The equivalent pore size becomes relatively smaller with decreasing mean particle size of filler.     

Finite element analysis of the transient motion of stratified viscous fluids under gravity

The present paper deals with the finite element analysis of two-dimensional two-layer density flows in a gravitational field. A fluid in each layer is replaced with a large number of discrete particles, and the motion and deformation of each layer is represented by moving those particles in a Lagrangian manner. The velocity distribution in the whole fluid region is given as the finite element solution of the Navier-Stokes equations and the equation of continuity. In the finite element calculation, free-slip conditions are used on solid wall boundaries because no-slip conditions may cause sticking of some particles to walls. Then, a new technique for the implementation of free-slip conditions on arbitrary curved boundaries is presented. As numerical examples, density flows in a rectangular closed container and Rayleigh-Taylor instability in the container with a circular cross-section have been computed.     

Functions and applications of monostable-bistable transition logicelements (MOBILE's) having multiple-input terminals

The MOBILE is a logic gate exploiting the monostable-bistable transition of a circuit that consists of two resonant tunneling transistors connected in series. It has several advantages including multiple inputs and multiple functions. This paper describes the output characteristics of multiple-input MOBILE's and discusses their applications. For a two-input MOBILE, it is demonstrated that both NAND and NOR operations are possible with the appropriate control voltage. This implies the possibility of a variable function logic gate. Furthermore, the threshold logic operations for a weighted sum of input signals are demonstrated for a three-input MOBILE with a weight ratio of 4:2:1. The applications of MOBILE's in parallel processing architectures such as cellular automata and cellular neural networks are discussed based on the above results. Circuit simulations using a simple model of resonant tunneling transistors successfully reproduce the basic characteristics of MOBILE's, and demonstrate the usefulness of MOBILE's in such applications     

Twin-Related Tetragonal Variants in Yttria Partially Stabilized Zirconia

Crystals of yttria partially stabilized zirconia were grown by the arc-image floating-zone technique and studied by transmission electron microscopy. Crystals annealed at 1700°C consist of tetragonal precipitates and a cubic matrix. The platelike domains in a precipitate are twin-related tetragonal variants stacked alternately parallel to the (011) twin plane. The axial relations between the tetragonal precipitate and the cubic matrix are [100]_tetragonal|[100]_cubic, [011]_tetragonal|[011]_cubic.     

Preparation of spherical fine ZnO particles by the spray pyrolysis method using ultrasonic atomization techniques

An ultrasonic atomizer was used in the spray pyrolysis method to prepare fine, spherical and uniform ZnO particles. Almost spherical particles were obtained successfully which had a mean particle size of 0.15 m and had a very narrow particle size distribution. By using alcohol as the solvent, it was found that the particles do not have hollow shell layers which could usually be observed in the spray pyrolysis process by using water as the solvent. The morphology of the ZnO particles was strongly affected by the concentration of the starting solution.     

Formation of monodispersed Ta2O5 powders

The Ta₂O₅ powders synthesized by the hydrolysis of tantalum pentaethoxide, Ta(OC₂H₅)₅ in alcoholic solution were monodispersed fine oxide particles, which were a uniform, spherical shape, non-agglomerate, and had a narrow size distribution. They grew to 1.2m after ageing for 1 h after hydrolysis. Powder X-ray diffraction and differential thermal analysisthermogravimetric analysis showed the particles were amorphous and hydrated. These particles lost the water at 290° C and gave well-crystalline Ta₂O at 740° C. Throughout these thermal processes, the particle morphology was kept almost the same.     

Effect of Silicon Dioxide on the Thermal Diffusivity of Aluminum Nitride Ceramics

The thermal diffusivity of AlN ceramics was significantly decreased by the addition of SiO₂. The AlN ceramics with 4 wt% SiO₂ could not be densified by pressureless sintering in the temperature range 1400° to 1800°C. The thermal diffusivity of these samples was very low because of their porous structure. The AlN ceramics containing 2, 4, and 8 wt% SiO₂ were densified by hot-pressing and also had low thermal diffusivity. In these samples, the grains of the 27R polytype that resulted from the reaction between AlN and SiO₂ were dispersed, obstructing the conduction of heat. The relation between the amount of 27R polytype and the thermal diffusivity of the AlN ceramics was determined.     

Interactions oftrans-cinnamic acid,its related phenolic allelochemicals,and abscisic acid in seedling growth and seed germination of lettuce

Phenolic compounds have been identified as the most common allelochemicals produced by higher plants. Inhibitions of cinnamic acid, its related phenolic derivatives, and abscisic acid (ABA) on seedling growth and seed germination of lettuce were studied.trans-Cinnamic acid, ando-,m-, andp-coumaric acids inhibited the growth of etiolated seedlings of lettuce at concentrations higher than 10^–4 M and seed germination above 10^–3 M. Coumarin inhibited seedling growth and seed germination at 10^–5 M or above. Chlorogenic acid inhibited seedling growth above 10^–4 M, but did not inhibit seed germination at 10^–5–5×10^–3 M. Low concentrations (below 10^–3 M) of caffeic and ferulic acids promoted the elongation of hypocotyls, but higher concentrations (over 10^–3 M) inhibited seedling growth and seed germination. These phenolic compounds and abscisic acid had additive inhibitory effects both on seedling growth and seed germination. The inhibition on lettuce was reversed by caffeic and ferulic acids at concentrations lower than 10^–3 M except for the inhibition of germination by coumarin. These results suggest that in naturetrans-cinnamic acid,o-, m-, p-coumaric acids, coumarin, and chlorogenic acid inhibit plant growth regardless of their concentration. However, caffeic and ferulic acids can either promote or inhibit plant growth according to their concentration.