Preparation and properties of PAn/ATTP/PE conductive composites

Polyaniline/Attapugite/PE（PAn-ATTP/PE）composites containing particles with core-shell structure were obtained via the two-step blending processs. The experimental condition is as follows： Organo-attapulgite and PAn was obtained by modifying attapulgite with laury benzenesulfonic acid sodium salt and, then added to PE. The electrical conductivity, structure and properties of the composites were studied. Under the function of shear stress, core-shell structure particles with ATTP as the core and PAn as the shell were formed in the composites. The structure of PAn-ATTP/PE composites were characterized by FTIR,XRD,SEM, etc, respectively. The effects of concentration of doping agent on the conductivity and mechanical property of the composites were investigated. The mechanical properties and impact fracture surface of the ternary composites were studied by means of the tensile tester, SEM, etc. The results show that polyaniline encapsulated ATTP enhances the strength of the PE. And the conductivity of PAn-ATTP/PE composites of is improved effectively when polyaniline encapsulated ATTP is added. The composite have good conductivity when 10% polyaniline encapsulated ATTP is added.     

PTA和CHDM改性聚丁二酸丁二醇酯的性能比较研究

将含有苯环的对苯二甲酸(PTA)和六元环的1,4-环己烷二甲醇(1,4-CHDM)引入PBS分子主链中,得到PBS-co-PTA和PBS-co-CHDM的无规共聚物.1 H-NMR鉴定了共聚物为预期产物,并对共聚物的热性能、结晶性和力学性能进行了对比研究.结果表明:PTA和1,4-CHDM改性后共聚物的结晶度变化截然不同,随着PTA含量的增加,PBS-co-PTA的结晶度、结晶尺寸逐渐增大,同时Tg逐渐降低;而随1,4-CHDM含量的增加,PBS-co-CHDM的结晶度和结晶尺寸却减小,Tg逐渐上升.当1,4-CHDM增至30%时,其断裂伸长率可达到PBS的3倍,证明了共聚物PBS-co-CHDM比PBS-co-PTA具有更好的柔韧性.     

金属离子对脂肪族聚酯降解性能的影响

在土壤培养液中添加不同种类的金属离子,研究了它们对可生物降解聚酯聚乳酸（PLA）、聚丁二酸丁二酯（PBS）膜降解性能的影响。采用傅里叶变换红外光谱仪表征了PLA和PBS膜降解前后的化学结构。结果表明：所有降解后的膜表面均有明显被侵蚀的痕迹;在土壤培养液中的Mg^2＋,Zn^2＋,Ca^2＋对PLA的降解性能有促进作用,对PBS的降解性能则影响不大;降解后PLA膜的玻璃化转变温度有所升高,但PBS膜变化不大。     

阴离子改性膨润土对水中亚甲基蓝吸附性能研究

以阴离子表面活性刑十二烷基磺酸钠(SDS)为改性剂制备了阴离子改性膨润土,研究了亚甲基蓝溶液在SDS-Bt上的吸附行为,并从热力学和动力学角度探讨了吸附作用机理.FI-IR、XRD分析表明:插层剂已进入膨润土层间,改性膨润土层间距由1.04nm增加到3.52nm.吸附实验表明,亚甲基蓝在SDS-Bt上的吸附符合Langmuir和Tempkin等温吸附方程,吸附焓变和熵变分别-25.44 kJ·mol-1和-50.74 J·mol-1·K-1,吸附表现为自发的表面物理吸附,且遵循伪二级动力学方程,吸附活化能为3.34 kJ·mol-1.     

化学合成生物降解高分子材料的研究现状

综述了国内外近年来通过化学方法合成的各种可生物降解高分子材料,对其合成方法、降解原理、研究现状及研究热点进行了简单的概述,旨在为可生物降解材料的发展作铺垫。     

平凉钙基膨润土干法钠化工艺研究

采用干法工艺,对甘肃平凉膨润土进行钠化改性,分别从不同钠化剂(碳酸钠、氯化钠、氢氧化钠)的选择和配比、钠化高混时间、自然放置时间等因素对钠化土性能的影响进行了研究.用FT IR和XRD对钠化土进行分析,结果表明,钠化土在不改变原土结构的同时发生了阳离子交换,层间距明显增大.     

Co-Phen-HAA/MMT催化分子氧氧化苯乙烯及其动力学研究

采用离子交换和配位合成方法,通过配位链将配体引入金属蒙脱土层间,制备了Co-Phen-HAA/MMT负载型催化材料,采用IR,XRD、SEM的现代分析测试技术,分析了催化材料的结构,XRD显示蒙脱土层间距增大0.577nm,表明配体进入金属蒙脱土的片层间;在分子氧的氧化作用下,考察了反应温度、时间、溶剂等因素对苯乙烯环氧化反应的影响.实验结果表明,最佳反应温度82℃,反应时间8 h,苯乙烯的转化率为93.9%,反应活化能41.35 kJ/mol.     

聚苯胺/二氧化硅复合薄膜的制备及其防腐性能

采用电化学辅助自组装法(Electrochemically assisted self-assembly,EASA)在304不锈钢(304SS)电极上制得二氧化硅(SiO_2)薄膜,然后以循环伏安法(CV)在其上制得了具有防腐性能的聚苯胺/二氧化硅(PANI-SiO_2)薄膜。通过透射电镜(TEM)研究了SiO_2薄膜的孔径,采用扫描电镜(SEM)研究了复合薄膜的形貌,采用Tafel极化曲线、电化学交流阻抗(EIS)研究了复合薄膜在5%氨基磺酸(SA)溶液中的耐蚀性能。结果表明:制得的SiO_2孔径约为2.5nm,相对于聚苯胺,复合薄膜排列较为规则,具有较高的腐蚀电位(-0.248 V)和较低的腐蚀电流密度(1.505×10~(-5) A·cm~(-2))。     

涂料用有机硅低聚体的合成与应用研究

研究了一类以甲基三乙氧基硅烷、正硅酸乙酯等为单体、溶液缩聚的有机硅低聚体建筑表面处理材料。探讨了pH值对反应过程的影响及单体用量对材料性能的影响,并进行了红外分析和透气性测试。结果表明：所研制的有机硅低聚体能够满足建筑材料的表面处理要求。     

马来酸酐辐照接枝三元乙丙橡胶的研究

采用辐照技术,用马来酸酐(MAH)对三元乙丙橡胶(EPDM)进行接枝改性,测定接枝物的交联度和接枝率.分析了辐照剂量、马来酸酐用量以及阻交联剂用量对接枝物交联度和接枝率的影响.同时,采用正交试验优化了试验参数.结果表明,当辐照强度为0.3 kGy/h、辐照剂量为0.15 kGy、MAH与EPDM的质量比为0.025:1以及阻交联剂的质量分数为0.02%时,接枝率达到1.35%.