Characterization of anisotropic gas permeability and thermomechanical properties of highly textured porous alumina

Porous alumina with a highly textured microstructure was fabricated by pulse electric current sintering (PECS) using alumina platelets. Highly oriented porous alumina with a porosity of 3%–50% was obtained by a pressure-controlled method of PECS. The properties of the highly textured porous alumina were measured in two directions. The nitrogen gas permeance and thermal conductivity at room temperature were higher in the direction along the platelet length due to the higher continuity of pores and the connectivity of alumina platelets, respectively. The anisotropy of the thermal conductivity at room temperature was investigated and explained by the effect of grain size of platelets as well as morphology and orientation of pores. The bending strength was higher with the loading direction along the platelet thickness. The thermal shock strength was clearly different in the two directions. The difference in the thermal shock strength was investigated by the measurement of properties and thermal stress analysis.     

Electrical Breakdown Properties and Space Charge Formation in High Temperature Region in Ultraviolet Ray Irradiated PVC

Polyvinyl chloride (PVC) is the most popular insulating material for electric wiring instruments. However, an exothermic reaction above 150 °C may cause deterioration of the insulating properties of PVC. Therefore, it is important to clarify the heat degradation in PVC, not only to investigate the ignition of electrical wiring products but also to use electrical products safely. It is known that ultraviolet (UV) irradiation causes chemical deterioration of PVC and an increase in its conductivity. Generally, it has been thought that the electrical breakdown properties, electrical conduction, and insulating performance are affected by space charge accumulation in an insulating material. A high temperature pulsed electroacoustic (PEA) system usable up to 250 °C has been developed, and the PEA system can measure the space charge distribution and conduction current in the high temperature range simultaneously. In this investigation, the space charge distribution and conduction current were measured up to electrical breakdown in a non‐UV irradiated sample (normal PVC) and in 353 nm and 253 nm UV‐irradiated PVC samples in the range from room temperature to 200 °C in a DC electric field. In the short wavelength UV irradiated PVC sample (253 nm, 300 h), a deterioration of breakdown strength at 90 °C to 150 °C and negative packet‐like charges were observed at 60 °C and 100 °C, a positive charge accumulated in front of both the anode and cathode above 90 °C, and a higher electric field near the cathode side because the positive charge of the cathode side was greater.     

Efficiency of repeated batch penicillin fermentation using two fermentors. Computer simulation and optimisation

Repeated batch operation using two fermentors (RBTF) to penicillin fermentation was demonstrated by computer simulation to improve productivity. Three operation modes were compared: chemostat, repeated batch operation using a single fermentor (RBSF) and RBTF; in each case account was made of the lag period before growth. The simulated fermentor performances were assessed on the basis of the penicillin productivity and concentration; the simulation was based on published batch fermentation data. It was shown that RBTF was superior to RBSF and chemostat. The advantage of RBTF increased as the lag period became greater.     

Improved visible-light responsive photocatalytic activity of N and Si co-doped titanias

Thermal reaction of titanium tetraisopropoxide and tetraethyl orthosilicate in 1,4-butanediol afforded nanocrystalline silica-modified titanias having large surface area and superior thermal stability. In this study, the thus-obtained silica-modified titanias were treated in an NH₃ flow at high temperatures, and their physical and photocatalytic properties were investigated. Compared with NH₃-treated TiO₂ without silica modification, the NH₃-treated silica-modified titanias showed a stronger absorption in the visible region (400–500 nm) and had a larger peak at 396 eV in the N 1s XPS spectrum. These results indicate that a larger amount of nitrogen was stably doped in the silica-modified titania. The obtained products exhibited a high photocatalytic activity for degradation of Rhodamine B and decomposition of acetaldehyde under visible light irradiation. Electronic supplementary material The online version of this article (doi:) contains supplementary material, which is available to authorized users.     

Comparison of activities in selective catalytic reduction of NOx by C3H8 over Co/MFI, Fe/MFI, and H/MFI zeolite catalysts

The Co/MFI(SiO₂/Al₂O₃ = 30) were prepared by a precipitation method with NaOCl in alkali solutions exhibited high activities to N₂ at 250 °C for the selective catalytic reduction (SCR) of NO_x. These catalysts showed two UV–vis bands at 700 and 400 nm, indicating the presence of octahedral Co(III) as well as tetrahedral Co(II). The high SCR activity over such Co(III, II)/MFI(30) seems to come from Co(III)---O moieties. The Co(II)MFI(30) catalysts prepared from Co(II)Cl₂ exhibited low SCR activities due to the presence of tetrahedral Co(II) ions in MFI. Less CO formation occurred over Co/MFI catalysts. The Fe/MFI(30) catalyst exhibited high activity due to the presence of some Fe---O species in MFI but more amount of CO were produced during SCR. H/MFI(30) catalyst exhibited a good SCR activity. However, more amount of carbonaceous deposits were produced on it. The correlation between acid concentration and SCR activity was discussed over H/MFIs.     

Preferential Oxidation of CO in H2-Rich Gas at Low Temperatures over Au Nanoparticles Supported on Metal Oxides

We investigated Au catalysts supported on TiO₂, Fe₂O₃, and ZnO for their preferential oxidation of CO in a H₂-rich atmosphere. Both full conversion and selectivity were achieved over Au/Fe₂O₃ and Au/ZnO around room temperature, but at higher temperatures the CO conversion was suppressed due to competition between CO and H₂.     

An expert system for XPLE cable deterioration diagnosis and life forecasting

The recent increase in the demand for power in urban areas has caused changes in the way power is supplied. Underground distribution systems have been introduced for convenience in urban areas and to prevent injuries in case of a crisis. As a result, many new types of power cables are being used. One type, XPLE cables (also called CV cables) have been rapidly taking the place of conventional cables such as OF or SL cables since the 1960s because of their relatively easy installation and maintainability. However, distribution cables used under severe environmental conditions deteriorate rapidly (due mainly to water treeing), and some cables experience insulation breakdown. Therefore, many diagnostic methods have been developed, though they have not been very effective. By combining methods, a high reliability can be achieved in comparison to the use of a single method. However, processing the data is difficult for on-site personnel, so many experts are required. But there is a lack of qualified experts, hence we have turned to the development of expert systems.     

Analysis of the IgE-epitope of Der f 2, a major mite allergen, by in vitro mutagenesis

Der f 2 is a major mite allergen composed of 129 amino acid residues. To determine the major epitopes on Der f 2 recognized by human IgE antibodies, artificial mutations were introduced to Der f 2 protein. The IgE-binding activity of Der f 2 was significantly decreased by deletion of 10 amino acids at the N-terminus or nine amino acids at the C-terminus. Site-directed mutagenesis with a single amino acid replacement by Ala or Leu in both N- and C-terminal regions as well as a central portion was performed to generate 42 single-site mutations. Amino acid replacement around a disulfide bond of Cys8-Cys119 caused a marked decrease in IgE-binding activity. Furthermore, a distinct decrease in IgE-binding was also caused by Ala-substitution close to a disulfide bond of Cys73-Cys78 and by mutations of a few charged residues. From these results, it was concluded that the two disulfide-forming regions of Der f 2 and several charged residues are important for forming major epitope structures recognized by human IgE antibodies.     

Preparation of SiB4±x and SiB6 plates by chemical vapour deposition of SiCl4 + B2H6 system

SiB_4±x and SiB₆ plates were prepared by chemical vapour deposition (CVD) using SiCl₄, B₂H₆ and H₂ gases under the conditions of deposition temperatures (T _dep) from 1323–1773 K, total gas pressures (P _tot) from 4–40 kPa and B/Si source gas ratio (m _B/Si=2B₂H₆/SiCl₄) from 0.2–2.8. The effects of CVD conditions on the morphology, structure and composition of the deposits were examined. High-purity and high-density SiB_4±x and SiB₆ plates about 1 mm thick were obtained at the deposition rates of 71 and 47 nm s⁻¹, respectively. The lattice parameter, composition and density of CVD SiB_4±x plates were dependent on their non-stoichiometry. The lattice parameter,a, was 0.6325 nm, butc ranged from 1.262–1.271 nm.The B/Si atomic ratio ranged from 3.1–5.0, and the density ranged from 2.39–2.45×10³ kg m⁻³. The CVD SiB₆ plates showed constant values of lattice parameters (a=1.444 nm,b=1.828 nm,c=0.9915 nm), composition (B/Si=6.0) and density (2.42×10³ kg m⁻³), independent of CVD conditions.     

Ormosil coatings of high hardness

Organically modified silicates (ormosils) of two systems were coated on polyethyleneterephthalate (PET) substrates. One was the tetraethoxysilane (TEOS)-vinyltriethoxysilane (VTES) system and the other was the TEOS-tetraisopropyltitanate (TIPT)-VTES system. The reactions among the alkoxides were examined by liquid state ²⁹Si nuclear magnetic resonance (NMR) spectroscopy. The chemical bonds between TEOS and VTES, between TEOS and TIPT, and between VTES and TIPT are shown in the spectra and the reaction schemes are proposed. Vickers hardnesses of the ormosil coatings were obtained by using the models developed by Jönsson and Hogmark, and the theoretical models developed by the authors were valuable to predict the hardness values. The ormosil coatings obtained in the present study were much harder than the hardest transparent plastics, and thus are very useful for hard or protective coatings on organic polymers.