Synthesis of boron nitride from triammoniadecaborane and hydrazine under pressure

Boron nitride (BN) of low crystallinity was synthesized from triammoniadecaborane (TAD) and hydrazine at 125 MPa below 650° C. TAD itself was pyrolysed at 600° C and 125 MPa to form a mixture of amorphous boron and boron nitride containing BH and NH bonds. The infrared spectrum of the pyrolysed product of TAD itself at 600° C and 125 MPa showed the BNB absorption at 800cm^–1 due to the formation of B₃N₃ structures. The X-ray diffraction (XRD) of the reaction product from TAD and hydrazine at 600° C had broad diffractions centred at 2=25.5° and 43.0° (CuK). The BH absorption at 2500cm^–1 decreased in intensity on increasing the N/B ratio from 0.3 to 0.85, and disappeared finally at a ratio of N/B=1.3. The reaction product at 125 MPa had a porous structure. The electron diffraction of the specimen changed from faint rings to spots on circular rings after heat treatment at 800° C for 10 h. The heat-treated specimen, however, did not give sharp reflections corresponding to hexagonal BN in the XRD profile. BN of low crystallinity was transferred to cubic BN at 1200° C and 6.5 GPa in a 90% yield, which was higher than that of well-crystallized BN in the presence of AIN.     

Preparation of TiB2 sintered compacts by hot pressing

A sintered compact of titanium diboride (TiB₂) was prepared by hot pressing of the synthesized TiB₂ powder, which was obtained by a solid-state reaction between TiN and amorphous boron. Densification of the sintered compact occurred at 20 MPa and 1800° C for 5 to 60 min with the aid of a reaction sintering, including the TiB₂ formation reaction between excess 20 at % amorphous boron in the as-synthesized powder (TiB₂ + 0.2B) and intentionally added 10 at % titanium metal. A homogeneous sintered compact of a single phase of TiB₂, which was prepared by hot pressing for 30 min from the starting powder composition [(TiB₂ + 0.2B) + 0.1 Ti], had a fine-grained microstructure composed of TiB₂ grains with diameters of 2 to 3 m. The bulk density was 4.47 g cm^–3, i.e. 98% of the theoretical density. The microhardness, transverse rupture strength and fracture toughness of the TiB₂ sintered compact were 2850 kg mm^–2, 48 kg mm^–2 and 2.4 MN m^–3/2, respectively. The thermal expansion coefficient increased with increasing temperature up to 400° C and had a constant value of 8.8 x 10^–6 deg^–1 above 500° C.     

In Situ Synthesis and Microstructures of Tungsten Carbide-Nanoparticle-Reinforced Silicon Nitride-Matrix Composites

A W₂C-nanoparticle-reinforced Si₃N₄-matrix composite was fabricated by sintering porous Si₃N₄ that had been infiltrated with a tungsten solution. During the sintering procedure, nanometer-sized W₂C particles grew in situ from the reaction between the tungsten and carbon sources considered to originate mainly from residual binder. The W₂C particles resided in the grain-boundary junctions of the Si₃N₄, had an average diameter of ∼60 nm, and were polyhedral in shape. Because the residual carbon, which normally would obstruct sintering, reacted with the tungsten to form W₂C particles in the composite, the sinterability of the Si₃N₄ was improved, and a W₂C–Si₃N₄ composite with almost full density was obtained. The flexural strength of the W₂C–Si₃N₄ composite was 1212 MPa, ∼34% higher than that of standard sintered Si₃N₄.     

Microwave holographic imaging method with improved resolution

A multifrequency holographic microwave imaging method with high resolving capability in both azimuth and range directions, is described. The method incorporates a synthetic aperture approach in pulse radar systems, originally designed for the pulse-echo imaging, in order to improve azimuth resolution. The imaging technique places no constraint on the waveform of a transmitted signal in use and allows the three-dimensional imaging. This paper develops 1) the general formula, which describes the relation between the transmitted and received signals, based on Kirchhoff diffraction theory, 2) a test function, which is the kernel of a linear operation for producing object images from received signals, and 3) a filter design technique for compressing the durations and suppressing the sidelobe levels of received signals. Numerical image reconstructions are presented for demonstrating high resolution capability of the method.     

Mechanism of Magnetite Seam Formation and its Role for FeO Scale Transformation

The phase transformation behavior of a thermally grown oxide scale of FeO on pure-Fe and an Fe–2wt%Au alloy was investigated. Particular attention was paid to formation of a magnetite seam, which is the Fe₃O₄ layer formed at the FeO/alloy interface at an initial stage of the phase transformation, since it has important effects on the overall phase transformation of FeO scale. A thin Au(Fe) layer was found to develop on the Fe–Au alloy at the FeO/alloy interface after 32 min of oxidation at 750 °C in air. This Au(Fe) layer prevented formation of a magnetite seam and accelerated the FeO eutectoid reaction. The Au(Fe) layer acted as a “chemical diffusion barrier” for inward diffusion of Fe from the FeO to the alloy substrate across the FeO/alloy interface and prevented magnetite seam formation.     

Tensile strength and morphological investigation of SiC-coated carbon fibers

SiC-coated film onto carbon fibers as a barrier of oxidation resistance and reaction between carbon fibers and metals was investigated. The chemical vapor deposition of silicon carbide onto carbon fibers was performed at various temperatures ranging from 700 to 1000°C using triisopropylsilane vapor carried by hydrogen gas. The strength of the SiC-coated carbon fibers was decreased due to deterioration of fibers and chemical attack of hydrogen on the surface of carbon fibers during the coating process. The oxidation and the thermal resistance of the SiC-coated carbon fibers compared to the uncoated carbon fibers were improved at temperature range of 600–800°C and 1000–1200°C, respectively. Morphological change by air oxidation at temperature range of 500–800‡C was also investigated for the SiC-coated and the uncoated carbon fibers, respectively. The SiC-coated film between carbon fiber and aluminum was sufficient as a barrier of reaction on carbon fiber reinforced aluminum at temperature of above 1000°C.     

Degradation characteristics of polylactide in thermophilic anaerobic digestion with hyperthermophilic solubilization condition

To test whether hyperthermophilic treatment promotes polylactide (PLA) dissolution and methane conversion under anaerobic digestion conditions, a single thermophilic control reactor (55 °C) and a two-phase system consisting of a hyperthermophilic reactor (80 °C) and a thermophilic reactor (55 °C) were continuously fed with a mixture of PLA and artificial kitchen garbage. In Runs 1 and 2, the PLA dissolution ratios in the two-phase system were 79.2 ± 6.5% and 85.2 ± 7.0%, respectively, higher than those of the control. Batch experimental results indicated that hyperthermophilic treatment could promote PLA dissolution to a greater degree as compared with single thermophilic treatment and that ammonia addition also had a promotional effect on PLA dissolution. In the two-phase system, after hyperthermophilic treatment, dissolved PLA was converted to methane gas under the subsequent thermophilic condition.     

On the formation of solid solution in Co3−xMnxO4 system

The formation of solid solution in the Co_3−xMn_xO₄ system in atmospheres of oxygen, air and argon was examined at a constant temperature of 1000 °C. In oxygen, a small amount of the NaCl-type compound was found to co-exist with the cubic spinel in the composition rangex≤0.1. A single phase of the cubic spinel was found in the range 0.1 to 1.3 and the tetragonal spinel above 1.9. In the rangex=1.3 to 1.9 where the cubic and tetragonal spinels co-exist they both have very broadened diffraction line profiles. In air, the identified phases and the changes in their lattice constants with composition were very similar to those in oxygen, except that the NaCl-type compound and the cubic spinel co-existed over a larger range. In argon, the cubic spinel was not observed over any of the composition range and the NaCI-type compound and the tetragonal spinel co-existed in the wide range of 1.1 to 2.3. The experimental results are discussed with regard to the cation distribution in the spinel and also to the relative stability of Co³⁺- and Mn³⁺-ions under the low partial pressure of oxygen.     

Synthesis of Cubic Boron Nitride from Boron Nitride Synthesized by Pressure Pyrolysis of Borazine

Cubic BN was synthesized under high-temperature and -pressure conditions from BN powder formed by pressure pyrolysis of borazine below 700°C and 100 MPa. The conversion of BN powder to cubic BN was strongly influenced by the residual hydrogen identified by the BH/BN ratio of IR absorption band. The activation energy for cubic BN synthesis from BN powder-20 mol% AIN was 46 kJ/mol, when the starting BN was synthesized at 250°C. A mixture of BN powder and cubic BN particles was converted to cubic BN in a 100% yield by heat treatment at 1800°C and 6.5 GPa without any catalyst. The presence of cubic BN particles does enhance the conversion to cubic BN from BN powder. The energy required for the transformation of starting BN to cubic BN in the presence of cubic BN seed was 355 kJ/mol.