Effects of Surface Concentration on Drying Behavior of Carbohydrate Solutions

As the surface properties of the drying materials are very important not only for the drying rate but also for the quality change during drying, the effects of surface concentration on the drying behavior of liquid foods (sugar solutions) were investigated by isothermal drying experiments and by numerical calculation experiments. The isothermal drying experiments with gelled sugar solution systems (sucrose and maltodextrin) were carried out at various relative humidity (RH) values (RH = 0 to 84%). Separate experiments were carried out for determination of the desorption isotherms.

The isothermal drying curves of sugar solutions at RH = 0 to 51% were very similar. Numerical simulations also showed that the drying curves of these sugars at the surface concentration = 0 and 0.1 are almost the same, although the concentration distributions are different.

When a small amount of gelatin was added to sugar solutions, the drying rate decreased remarkably as the gelatin might form a thin film (skin) near the surface, and consequently the retention of ethanol increased.     

High Gd Concentration GaGdN Grown at Low Temperatures

GaGdN layers were grown at temperatures below 300°C by radio-frequency plasma-assisted molecular beam epitaxy on sapphire substrates. GaGdN samples with high Gd concentration as high as 12.5% were obtained by lowering the growth temperature. X-ray diffraction results showed no obvious secondary phase, which means that the phase separation can be suppressed by the growth at low temperatures. All samples, including those grown at room temperature, showed ferromagnetic characteristics. Photoluminescence emission was observed, though spectra exhibit broad and sharp luminescence bands related to many kinds of defects. It is suggested that electrons coming from defects, especially, nitrogen vacancy, stabilize ferromagnetism, and that the carrier-induced ferromagnetism occurs in the low-temperature-growth GaGdN.     

Calciothermic reduction of titanium oxide in molten CaCl<Subscript>2</Subscript>

Titanium oxides were reduced to metallic titanium using the liquid calcium floating on the molten CaCl₂. A part of Ca dissolved into CaCl₂ and reacted with TiO₂ settled below CaCl₂. The by-product CaO also dissolved by about 20 mol pct into CaCl₂, which was effective in reducing the oxygen concentration in the obtained Ti particles. The compositional region in the Ca-CaCl₂-CaO system was examined for the less oxygen contamination in Ti and the better handling in leaching. A large amount of the residual calcium oxidized the titanium powder in leaching. The metallic Ti powder less than 1000 mass ppm oxygen could be obtained only for 3.6 ks using 5 to 7 mol pct Ca-CaCl₂ at 1173 K. The powder was slightly sintered like sponge, and contained approximately 1500 ppm Ca. The anatase phae, the intermediate product in the refining process of TiO₂, could be also supplied as raw material as well as rutile.     

Chirality-antimicrobial relationship of quaternary ammonium cationics

Optically active and racemic quaternary ammonium cationics containing a chiral alkyl group, such as N,N-dimethyl-N-(1-phenylethyl)alkylammonium bromides were prepared and showed excellent antimicrobial properties against Gram positive and negative bacteria, with some exceptions, and against fungi. The influence of optical isomerism on their antimicrobial properties showed that the antimicrobial properties between racemic and optically active cationics were obscure. The order of activity of substituted alkyl groups was tetradecyl > dodecyl ° hexadecyl.     

Silicon nitride thin-film deposition by LPCVD with in situ HF vaporcleaning and its application to stacked DRAM capacitor fabrication

Silicon nitride film deposited by LPCVD with newly developed in situ HF vapor cleaning has been studied and applied to fabricate dielectric films for stacked DRAM capacitors. Using this method, an oxide-free surface of underlaid poly-Si can be obtained. Silicon nitride film deposited on this surface has been verified by FTIR measurement to have the stoichiometrically proper composition of Si₃N₄ . However, the film was found to be selectively deposited on poly-Si electrodes. This selective deposition degrades the reliability of the stacked capacitor, because the silicon nitride can not completely cover the periphery of poly-Si electrodes on SiO₂. We propose a simple process that avoids the problem making it possible to apply silicon nitride film to stacked-capacitor fabrication. Stacked capacitors fabricated by this process exhibit very low leakage current and high electrical reliability even for ultra-thin silicon nitride films less than 5 nm thick     

Suppression of photo-induced dilation in cyanide treated hydrogenated amorphous silicon films

Effects of cyanide (CN) treatment with hydrogenated amorphous silicon (a-Si:H) films have been investigated. The decrease of ΔV/V was observed in cyanide treated a-Si:H films and the successive thermal annealing at 200°C after CN treatment induced the further reduction of the ΔV/V. XPS spectra show the indirect evidence that the cyanide species is present within 10 nm from the hydrogenated amorphous silicon surface. The results of CN treatment with a-Si:H solar cells are demonstrated.     

Enhancement of adenovirus-mediated gene transfer to human bone marrow cells

Adenovirus infection of CD34+ hematopoietic stem/progenitor cells is dependent on the multiplicity of infection (MOI), time of incubation, the volume in which the co-incubation occurs and the presence or absence of growth factors. Studies revealed that a brief co-incubation (1-8 hours), resulted in low levels of transgene expression, suggesting that adenovirus infection of CD34+ cells occurs slowly, and optimal transduction requires a 24 hour exposure to adenovirus. Infection by Ad/beta-gal or Ad/p53 at a MOI of 500:1 provided a high transduction efficiency but inhibited hematopoietic function. However, treatment at a MOI of 50-100 resulted in efficient transduction (10.7-15.7% positive) without detectable toxicity. Secondary proof of adenovirus transgene expression was demonstrated by detection of mRNA for p53 in Ad/p53 infected stem cells. We conclude that a 24 hour exposure to recombinant adenovirus encoding p53 or beta-gal, at a MOI of 50-100 is optimal for in vitro gene transfer to BM cells and has no significant effect on hematopoietic function. Adenovirus-mediated transduction of BM cells can also be modulated by growth factors (IL-3, GM-CSF and G-CSF) with improved gene delivery and maintenance of hematopoietic function. In summary, adenovirus vectors can be used to transiently transduce stem cells, and conditions have been defined to maximize expression and limit inhibitory effects on CD34+ cells. These data support continued investigation of this vector for local cytokine delivery and purging of stem cell products.     

Crystallization process and magnetic properties of Fe100−x,B x (10 ≦ × ≦ 35) amorphous alloys and supersaturated state of boron inα-Fe

Amorphous specimens of Fe_100–x B _x were prepared in the range 10 × 35 at % B by a single-roller method. The crystallization process and the boron concentration dependence of the Curie temperature were examined by differential scanning calorimetry, X-ray diffraction, Mössbauer spectroscopy and magnetic measurements. Two-step crystallization was observed in specimens with× < 17: amorphous amorphous + boron-supersaturated b c c phase (-Fe(B)) t-Fe₃B +-Fe. A single-Fe(B) phase was not observed. The transition temperature from t-Fe₃B to stable (-Fe + t-Fe₂B) sensitively depends on the boron content in the alloys. The crystallization temperature (T _x) of the amorphous alloys was almost unchanged for 17 × 31, but increased remarkably at high boron concentrations of× 33, where the decomposition products consisted of t-Fe₂B and o-FeB. The Curie temperature (T _c) of the amorphous phase was as low as 480 K at× = 10, increased with increasing boron content up to 820 K and then decreased in the high boron concentration alloys of× > 28. A single-Fe(B) phase was not detected in the as-quenched specimens of× = 8 and 10. The phase coexisted with the o-Fe₃B and amorphous phases. The lattice parameter of the phase was 0.2861₀ nm which was smaller than that of pure iron by 2/1000, indicating the substitutional occupation of boron atoms in the b c c lattice.     

Taxonomy for protective ability of rust layer using its composition formed on weathering steel bridge

For a quantitative evaluation of the protectiveness of a rust layer formed on a weathering steel bridge, the relationship between the corrosion rate of the bridge and the composition of the rust layers formed on the girders was first investigated. These corrosion rates were clearly classified by the protective ability index (PAI) of α/γ^∗ and (β + s)/γ^∗, where α, γ^∗, β and s are the mass ratio of crystalline α-FeOOH, the total of γ-FeOOH, β-FeOOH and the spinel-type iron oxide (mainly Fe₃O₄), β-FeOOH and spinel-type iron oxide, analyzed by XRD, respectively. The inequality of the former index α/γ^∗ > 1 expressed the protectiveness criterion of the rust layer, while that of the latter index, (β + s)/γ^∗< 0.5 or > 0.5, classified the corrosion rate of the non-protective rust layer. The PAI is useful for a quantitative evaluation of the protectiveness of a rust layer formed on a weathering steel bridge and is an important item for the corrosion assessment of the bridge.