Characterization of anisotropic gas permeability and thermomechanical properties of highly textured porous alumina

Porous alumina with a highly textured microstructure was fabricated by pulse electric current sintering (PECS) using alumina platelets. Highly oriented porous alumina with a porosity of 3%–50% was obtained by a pressure-controlled method of PECS. The properties of the highly textured porous alumina were measured in two directions. The nitrogen gas permeance and thermal conductivity at room temperature were higher in the direction along the platelet length due to the higher continuity of pores and the connectivity of alumina platelets, respectively. The anisotropy of the thermal conductivity at room temperature was investigated and explained by the effect of grain size of platelets as well as morphology and orientation of pores. The bending strength was higher with the loading direction along the platelet thickness. The thermal shock strength was clearly different in the two directions. The difference in the thermal shock strength was investigated by the measurement of properties and thermal stress analysis.     

Consideration of Femtosecond Radiation Generation on NewSUBARU Storage Ring

We studied on realization of short pulse gamma ray and X-ray simultaneously induced by a femtosecond laser on NewSUBARU storage ring. Based on the fact that the transverse dimensions of electron beam are much shorter than the longitudinal one, the laser light is arranged to collide the electron beam at a right angle to generate femtosecond pulse gamma ray, furthermore, the modulated part of the electron bunch gives rise to short pulse X-ray by synchrotron radiation from a downstream bending magnet. The temporal characteristic of the radiation is analyzed in this paper, as well as the performances are estimated.     

Apoptosis occurs in granulosa cells but not cumulus cells in the atretic antral follicles in pig ovaries

The porcine antral follicles, 3-6 mm in diameter, were dissected from the ovaries of mature pigs, and then granulosa and cumulus cells were isolated from each follicle. In atretic follicles, high activity of neutral Ca2+/Mg2+-dependent endonuclease and DNA ladder formation, estimated by electrophoresis, were noted in granulosa cells but not in cumulus cells. Extremely low activity of the endonuclease and no DNA ladder formation were observed in both types of cells obtained from healthy follicles. Moreover, apoptotic cells were observed histochemically among granulosa cells only. A good correlation (r = 0.987) between the endonuclease activity of granulosa cells and the progesterone/estradiol ratio of follicular fluid in each follicle was found. These results suggest that apoptosis occurs in granulosa cells but not cumulus cells in the atretic antral follicles in pigs.     

液闪效率示踪法校正效果的评价

本文评价了Aloka商品液闪仪效率示踪法dpm校正的效果。轻,中度猝灭校正效果理想,具有简便、实用和适用性广泛的特点。严重化学和颜色猝灭样品的校正结果分别随猝灭增加而向增大和减小的方向偏离,形成喇叭状曲线,文中对这一现象给出初步解释。     

Floating-island TFT leakage caused by process step reduction

The leakage mechanism for a top-gate thin-film transistor (TFT) produced using the fewest process steps in the industry is analyzed in order to achieve a high-contrast liquid crystal display (LCD). Using a T-shaped TFT structure, the OFF and ON channel lengths are defined independently, so that the leakage can be reduced with no ON current decrease     

370 W output power GaN-FET amplifier for W-CDMA cellular base stations

A single-ended amplifier using small packaged GaN-FETs exhibits a record 2.14 GHz W-CDMA output power. The amplifier, composed of paralleled 48 mm gate periphery FET die, delivers a peak saturated output power of 371 W with a linear gain of 11.2 dB at a drain voltage of 45 V under 2.14 GHz 3GPP W-CDMA signal input. The output power density (output power/package size) of 1.1 W/mm/sup 2/ is twice as high as that of the existing over 300 W GaAs-FET amplifiers. A low 5 MHz offset ACLR of -36 dBc with a drain efficiency of 24% is also obtained at 8 dB power back off from the saturated output power.     

Effect of Milling on Slip Casting of Partially Stabilized Zirconia

Specimens of partially stabilized zirconia were slip cast from aqueous suspensions and sintered at 1500°C for 3 h. The relative density of the cast specimens and the firing shrinkage of the sintered specimens depend on the milling time for the suspension. Vickers hardness and K_IC values of 11.46±s0.07 GN/m² and 6.10 ±0.04 MN.m^3/2, respectively, were obtained for all sintered specimens. The dispersion of the suspension is important in increasing the relative density of the cast specimens.