Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.     

A mini review on two-dimensional nanomaterial assembly

Two-dimensional (2D) nanomaterials have attracted a great deal of attention since the discovery of graphene in 2004, due to their intriguing physicochemical properties and wide-ranging applications in catalysis, energy-related devices, electronics and optoelectronics. To maximize the potential of 2D nanomaterials for their technological applications, controlled assembly of 2D nanobulding blocks into integrated systems is critically needed. This mini review summarizes the reported strategies of 2D materials-based assembly into integrated functional nanostructures, from in-situ assembly method to post-synthesis assembly. The applications of 2D assembled integrated structures are also covered, especially in the areas of energy, electronics and sensing, and we conclude with discussion on the remaining challenges and potential directions in this emerging field.

     

Structure and electrical properties of Ca2+-doped (Na0.47Bi0.47Ba0.06)TiO3 lead-free piezoelectric ceramics

The lead-free piezoelectric ceramics (Na_.47Bi_.47Ba_.06)_1-xCa_xTiO₃ (x?=?0, 0.01, 0.02, 0.03, 0.05, and 0.08, abbreviated as BNBTC/0, BNBTC/1, BNBTC/2, BNBTC/3, BNBTC/5, and BNBTC/8, respectively) were obtained using the solid-state reaction method. The structure, electric conductivity, and dielectric, ferroelectric, and piezoelectric properties of the Ca²⁺-doped (Na_.47Bi_.47Ba_.06)TiO₃ ceramics were thoroughly investigated. The ceramics sintered at 1200?°C exhibit dense microstructures, having relative densities higher than 96%. The X-ray diffraction results demonstrate that all ceramics have a pure perovskite structure. The mean grain sizes of the ceramics are related to the Ca²⁺ quantity. A small quantity of Ca²⁺ ions (x?≤?0.03) improves the piezoelectric and ferroelectric properties of the samples. The dielectric behavior of the samples is sensitive to the Ca²⁺ content and electric poling. The results demonstrate that the electrical properties of the (Na_.47Bi_.47Ba_.06)TiO₃ lead-free ceramics can be well tuned by varying the Ca²⁺ quantity.     

GIS在深圳市三防指挥信息系统中的应用

深圳市三防指挥信息系统利用GIS技术,结合水利(水务)、防汛、抗旱的具体业务,建立了水情遥测数据处 理分系统、工况监测数据处理分系统、水务行业三防信息管理分系统、决策支持分系统、水源优化调度分 系统,提高了现代化管理水平。     

溶剂浸渍树脂的萃取分离性能研究

介绍了溶剂浸渍树脂的制备及性能,阐述了溶剂浸渍树脂在产物提纯和废水处理等分离过程中的应用,并对使用溶剂浸渍树脂处理含酚废水进行了初步研究.     

H型丝光沸石催化剂催化甲苯与叔丁醇的烷基化反应

针对合成对叔丁基甲苯传统工艺中存在的缺点,采用环境友好、可重复利用的H型丝光沸石催化剂(以下简称催化剂)进行了甲苯与叔丁醇的烷基化反应,并用X射线衍射和氨程序升温脱附等方法对不同焙烧温度下得到的催化剂的物相结构和酸性质进行了表征,研究了各种反应条件对催化剂的催化性能的影响。实验结果发现,在适宜的操作条件下,即催化剂的焙烧温度823K、反应温度180℃、反应时间3h、初始压力1.0MPa、原料与催化剂的质量比为8、叔丁醇与甲苯的摩尔比为4、溶剂环己烷与甲苯的摩尔比为5时,甲苯转化率达42.73%,叔丁基甲苯的选择性为96.30%,对叔丁基甲苯的选择性为80.37%。     

干涉型激光直写技术用于光盘防伪

利用作者研制的干涉型激光直写系统，阐述了干涉型激光直写设计OVD的方法，防伪特征，介绍了应用于光盘防伪的OVD技术和应用前景，给出了实验结果。