Microwave hybrid fast sintering of red clay ceramics

This work aimed to examine the performance of the hybrid sintering of clay ceramic in a microwave furnace, compared to the sintering process in a conventional furnace. The raw materials were subjected to X-ray fluorescence, loss on ignition (LOI), X-ray diffraction, particle size distribution, real specific mass, and thermogravimetric analyses. The red clay ceramic mass was prepared, extruded, pre-sintered in a conventional furnace at 600°C/60 min, and sintered at temperatures between 700 °C and 1100 °C. The sintering conventional (resistive oven) was carried out for 60 min with a heating rate of 10°C/min. In the microwave furnace, the sintering times were 5, 10, and 15 min, with a heating rate of 50°C/min, with a sintering chamber coated with silicon carbide (susceptor). The sintered specimens were characterized according to linear shrinkage, water absorption, apparent porosity, apparent specific mass, X-ray diffraction, Raman spectroscopy analysis, spectroscopy analysis in the ultraviolet and visible regions, microhardness, and scanning electron microscopy. The results showed that microwave sintering promoted an increase in the microhardness and apparent specific mass, and reduction in water absorption and apparent porosity values, due to greater densification in the microstructure. The best results occurred for specimens sintered at 1100°C.     

Migraine: Calcium Channels and Glia

Migraine is a common neurological disease that affects about 11% of the adult population. The disease is divided into two main clinical subtypes: migraine with aura and migraine without aura. According to the neurovascular theory of migraine, the activation of the trigeminovascular system (TGVS) and the release of numerous neuropeptides, including calcitonin gene-related peptide (CGRP) are involved in headache pathogenesis. TGVS can be activated by cortical spreading depression (CSD), a phenomenon responsible for the aura. The mechanism of CSD, stemming in part from aberrant interactions between neurons and glia have been studied in models of familial hemiplegic migraine (FHM), a rare monogenic form of migraine with aura. The present review focuses on those interactions, especially as seen in FHM type 1, a variant of the disease caused by a mutation in CACNA1A, which encodes the α1A subunit of the P/Q-type voltage-gated calcium channel.     

Influence of To?pa Peat Preparation on the phagocytic activity and bactericidal properties of granulocytes in healthy volunteers

It was found, that To?pa Peat Preparation (TPP) administered to healthy volunteers in doses of 100-300 mg/day during 14 days evoked the stimulation of the phagocytic and bactericidal activity of the granulocytes. The dose of 600 mg/day causes only a transient and insignificant increase of phagocytic and bactericidal properties of the granulocytes.     

Transmission Electron Microscopy and Electron Energy-Loss Spectroscopy Characterization of Glass Phase in Sol-Gel-Derived Mullite

Sol-gel-derived mullite ceramics were processed by pressureless sintering at 1600°, 1650°, and 1700°C for 4 h. Microstructural and microchemical characterization of the mullite materials was performed using transmission electron microscopy, in conjunction with energy-dispersive X-ray spectroscopy and electron energy-loss spectroscopy (EELS). Apart from mullite grain diameter and triplepocket size, no major microstructural changes were observed with increasing sintering temperature. Residual glass was present at triple pockets and along two-grain junctions. Not all grain boundaries revealed the presence of a continuous amorphous intergranular film. Clean interfaces were observed only at boundaries with one grain parallel to the [001] orientation (low-energy configuration). Quantitative EELS analysis of mullite grains and glass pockets revealed only small changes in composition with increasing sintering temperature; i.e., the alumina:silica ratio slightly increased for mullite and glass. The analysis implied that mullite with this relatively high aluminum content would not be stable adjacent to residual glass. However, a stable glass-mullite system has been proposed, because impurity cations were detected within glass pockets, which suggested a slight shift of the subsolidus line (glass-mullite/ mullite) to a higher amount of alumina. Energy-loss nearedge structure studies of the Si- L _2,3 edge revealed a similar near-edge structure for the mullite, residual glass, and quartz. Thus, SiO₄ tetrahedra were thought to be the main building units of the glass contained in sintered mullite.     

Compatibility of polysaccharide/maleic copolymer blends. IV. Thermal behavior of hydroxypropyl cellulose‐containing blends

The compatibility of the hydroxypropyl cellulose (HPC) with maleic acid–vinyl acetate copolymer in the solid state was studied by thermogravimetry, thermo‐optical analysis, differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR), and optical microscopy. It was established that physical interactions are prevalent in blends with a high content of HPC, whereas chemical interactions predominate in blends with a medium and low content of HPC. By increasing the temperature, the thermochemical reactions are favored. Thermal properties are dependent on the mixing ratio of the components. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 2585–2597, 2003