Microwave hybrid fast sintering of red clay ceramics

This work aimed to examine the performance of the hybrid sintering of clay ceramic in a microwave furnace, compared to the sintering process in a conventional furnace. The raw materials were subjected to X-ray fluorescence, loss on ignition (LOI), X-ray diffraction, particle size distribution, real specific mass, and thermogravimetric analyses. The red clay ceramic mass was prepared, extruded, pre-sintered in a conventional furnace at 600°C/60 min, and sintered at temperatures between 700 °C and 1100 °C. The sintering conventional (resistive oven) was carried out for 60 min with a heating rate of 10°C/min. In the microwave furnace, the sintering times were 5, 10, and 15 min, with a heating rate of 50°C/min, with a sintering chamber coated with silicon carbide (susceptor). The sintered specimens were characterized according to linear shrinkage, water absorption, apparent porosity, apparent specific mass, X-ray diffraction, Raman spectroscopy analysis, spectroscopy analysis in the ultraviolet and visible regions, microhardness, and scanning electron microscopy. The results showed that microwave sintering promoted an increase in the microhardness and apparent specific mass, and reduction in water absorption and apparent porosity values, due to greater densification in the microstructure. The best results occurred for specimens sintered at 1100°C.     

Protecting against key-exposure: strongly key-insulated encryption with optimal threshold

Key-insulated encryption schemes use a combination of key splitting and key evolution to protect against key exposure. Existing schemes, however scale poorly, having cost proportional to the number t of time periods that may be compromised by the adversary, and thus are practical only for small values of t. Yet in practice t might be large. This paper presents a strongly key-insulated encryption scheme with optimal threshold. In our scheme, t need not be known in advance and can be as large as one less than the total number of periods, yet the cost of the scheme is not impacted. This brings key-insulated encryption closer to practice. Our scheme is based on the Boneh-Franklin identity-based encryption (IBE) scheme [9], and exploits algebraic properties of the latter. Another contribution of this paper is to show that (not strongly) key-insulated encryption with optimal threshold and allowing random-access key updates (which our scheme and all others known allow) is equivalent to a restricted form of IBE. This means that the connection between key-insulated encryption and IBE is not accidental. Supported in part by NSF grants CCR-0098123, ANR-0129617 and CCR-0208842, and by an IBM Faculty Partnership Development Award. Supported in part by an NSF graduate fellowship.     

Transmission Electron Microscopy and Electron Energy-Loss Spectroscopy Characterization of Glass Phase in Sol-Gel-Derived Mullite

Sol-gel-derived mullite ceramics were processed by pressureless sintering at 1600°, 1650°, and 1700°C for 4 h. Microstructural and microchemical characterization of the mullite materials was performed using transmission electron microscopy, in conjunction with energy-dispersive X-ray spectroscopy and electron energy-loss spectroscopy (EELS). Apart from mullite grain diameter and triplepocket size, no major microstructural changes were observed with increasing sintering temperature. Residual glass was present at triple pockets and along two-grain junctions. Not all grain boundaries revealed the presence of a continuous amorphous intergranular film. Clean interfaces were observed only at boundaries with one grain parallel to the [001] orientation (low-energy configuration). Quantitative EELS analysis of mullite grains and glass pockets revealed only small changes in composition with increasing sintering temperature; i.e., the alumina:silica ratio slightly increased for mullite and glass. The analysis implied that mullite with this relatively high aluminum content would not be stable adjacent to residual glass. However, a stable glass-mullite system has been proposed, because impurity cations were detected within glass pockets, which suggested a slight shift of the subsolidus line (glass-mullite/ mullite) to a higher amount of alumina. Energy-loss nearedge structure studies of the Si- L _2,3 edge revealed a similar near-edge structure for the mullite, residual glass, and quartz. Thus, SiO₄ tetrahedra were thought to be the main building units of the glass contained in sintered mullite.     

Compatibility of polysaccharide/maleic copolymer blends. IV. Thermal behavior of hydroxypropyl cellulose‐containing blends

The compatibility of the hydroxypropyl cellulose (HPC) with maleic acid–vinyl acetate copolymer in the solid state was studied by thermogravimetry, thermo‐optical analysis, differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR), and optical microscopy. It was established that physical interactions are prevalent in blends with a high content of HPC, whereas chemical interactions predominate in blends with a medium and low content of HPC. By increasing the temperature, the thermochemical reactions are favored. Thermal properties are dependent on the mixing ratio of the components. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 2585–2597, 2003     

Data collection in global software engineering research: learning from past experience

Global Software Engineering has become a standard in today’s software industry. Research in distributed software development poses severe challenges that are due to the spatial and temporal distribution of the actors, as well as to language, intercultural and organizational aspects. These challenges occur in addition to “traditional” challenges of the domain itself in large-scale software projects, like coordination and communication issues, requirements volatily, lack of domain knowledge, among others. While several authors have reported empirical studies of global software development projects, the methodological difficulties and challenges of this type of studies have not been sufficiently discussed. In this paper, we share our experiences of collecting and analysing qualitative data in the context of Global Software Engineering projects. We discuss strategies for gaining access to field sites, building trust and documenting distributed and complex work practices in the context of several research projects we have conducted in the past 9 years. The experiences described in this paper illustrate the need to deal with fundamental problems, such as understanding local languages and different cultures, observing synchronous interaction, or dealing with barriers imposed by political conflicts between the sites. Based on our findings, we discuss some practical implications and strategies that can be used by other researchers and provide some recommendations for future research in methodological aspects of Global Software Engineering.