The effect of ceria content on the performance of Pt/CeO2/Al2O3 catalysts in the partial oxidation of methane

The effect of CeO₂ loading (1–20 wt.%) on the properties and catalytic behaviors of CeO₂–Al₂O₃-supported Pt catalysts on the partial oxidation of methane was studied. The catalysts were characterized by S_BET, X-ray diffraction (XRD), temperature-programmed reduction (TPR) and oxygen storage capacity (OSC). XRD and TPR results showed that the pretreatment temperature of the support influences on the amount of CeO₂ with fluorite structure. The pretreatment temperature of the support and CeO₂ loading influenced the morphology of Pt. OSC analysis showed a significant increase in the oxygen storage capacity per weight of CeO₂ for samples with high CeO₂ loading (12 and 20 wt.%). TPR analyses showed that the addition of Pt promotes the reduction of CeO₂. This effect was more significant for the catalysts with high CeO₂ loading (≥12 wt.%). The dispersion of Pt, measured by the rate of cyclohexane dehydrogenation, increases with increasing of the pretreatment temperature of the support. It was shown that the kind of the support is very important for obtaining of catalysts resistant to carbon formation. The catalysts with high CeO₂ loading (≥12 wt.%) showed the highest catalytic activity and stability in the reaction of partial oxidation of methane due to a higher Pt–CeO₂ interface.     

Post-processing and visualization techniques in 2D boundary element analysis

Most post-processors for boundary element (BE) analysis use an auxiliary domain mesh to display domain results, working against the profitable modelling process of a pure boundary discretization. This paper introduces a novel visualization technique which preserves the basic properties of the boundary element methods. The proposed algorithm does not require any domain discretization and is based on the direct and automatic identification of isolines. Another critical aspect of the visualization of domain results in BE analysis is the effort required to evaluate results in interior points. In order to tackle this issue, the present article also provides a comparison between the performance of two different BE formulations (conventional and hybrid). In addition, this paper presents an overview of the most common post-processing and visualization techniques in BE analysis, such as the classical algorithms of scan line and the interpolation over a domain discretization. The results presented herein show that the proposed algorithm offers a very high performance compared with other visualization procedures.     

Polar classification with correspondence analysis for fault isolation

Data collected from operating plants can be mined to extract information related to both normal and fault modes of operation. Correspondence analysis (CA), that decomposes a measure of row–column association, to generate the lower dimensional space has been recently proposed [1] for this task. CA represents the association between samples and variables in terms of angle based measures on a biplot. Thus, toward clearer resolution of the faults, polar clustering and classification procedures are necessary. In this paper, we develop a methodology to mine the operating data and build such clusters. We demonstrate the application of this methodology on data generated from simulations and experiments involving representative systems,for detecting parametric changes and resolving sensor and actuator biases.     

COVID-19 and Lung Mast Cells: The Kallikrein–Kinin Activation Pathway

Mast cells (MCs) have relevant participation in inflammatory and vascular hyperpermeability events, responsible for the action of the kallikrein–kinin system (KKS), that affect patients inflicted by the severe form of COVID-19. Given a higher number of activated MCs present in COVID-19 patients and their association with vascular hyperpermeability events, we investigated the factors that lead to the activation and degranulation of these cells and their harmful effects on the alveolar septum environment provided by the action of its mediators. Therefore, the pyroptotic processes throughout caspase-1 (CASP-1) and alarmin interleukin-33 (IL-33) secretion were investigated, along with the immunoexpression of angiotensin-converting enzyme 2 (ACE2), bradykinin receptor B1 (B1R) and bradykinin receptor B2 (B2R) on post-mortem lung samples from 24 patients affected by COVID-19. The results were compared to 10 patients affected by H1N1pdm09 and 11 control patients. As a result of the inflammatory processes induced by SARS-CoV-2, the activation by immunoglobulin E (IgE) and degranulation of tryptase, as well as Toluidine Blue metachromatic (TB)-stained MCs of the interstitial and perivascular regions of the same groups were also counted. An increased immunoexpression of the tissue biomarkers CASP-1, IL-33, ACE2, B1R and B2R was observed in the alveolar septum of the COVID-19 patients, associated with a higher density of IgE⁺ MCs, tryptase⁺ MCs and TB-stained MCs, in addition to the presence of intra-alveolar edema. These findings suggest the direct correlation of MCs with vascular hyperpermeability, edema and diffuse alveolar damage (DAD) events that affect patients with a severe form of this disease. The role of KKS activation in events involving the exacerbated increase in vascular permeability and its direct link with the conditions that precede intra-alveolar edema, and the consequent DAD, is evidenced. Therapy with drugs that inhibit the activation/degranulation of MCs can prevent the worsening of the prognosis and provide a better outcome for the patient.     

Synthesis and Characterization of Ti-Nb2O5 Catalysts for Discoloration Reaction of Bromophenol Blue and Indigo Carmine Dyes

Topics in Catalysis - This work investigated the photodegradation of bromophenol blue (BPB) and indigo carmine (IC) dye under UV–Visible light using pure oxides of titanium and niobium, as...     

Ammonium complex of niobium as a precursor for the preparation of Nb2O5/Al2O3 catalysts

Ammonium oxalate complex of niobium was investigated as an aqueous precursor for the preparation of x% Nb₂O₅/Al₂O₃ (x=5, 10, 20 and 30 wt.%) samples. Catalysts with the same Nb₂O₅ contents were also prepared from the traditional niobium oxalate/oxalic acid aqueous solution. The catalysts were characterized by X-ray diffraction (XRD), diffuse reflectance spectroscopy (DRS), temperature-programmed reduction (TPR), infrared spectroscopy of chemisorbed pyridine and X-ray photoelectron spectroscopy (XPS). A comparison with the preparation method using the niobium oxalate salt was performed. The results showed that the niobium precursor influence the species growing leading to phases with different reducibility. The XPS revealed the presence of multilayers of niobium oxide on the Nb₂O₅/Al₂O₃ samples prepared by using niobium ammonium oxalate complex, while the ones obtained from niobium oxalate led to Nb₂O₅ particles islands. The addition of niobium oxide decreased the fraction of Lewis acid sites and increased the fraction of Brønsted acid sites, independent of the precursor salt. However, the creation of BAS was more pronounced on the Nb₂O₅/Al₂O₃ samples prepared from niobium oxalate.     

Effect of CeO2 and La2O3 on the Activity of CeO2−La2O3/Al2O3-Supported Pd Catalysts for Steam Reforming of Methane

The effect of the addition of CeO₂ or La₂O₃ on the surface properties and catalytic behaviors of Al₂O₃-supported Pd catalysts was studied in the steam reforming of methane. The FTIR spectroscopy of adsorbed CO and the Pd dispersion suggest the partial coverage of Pd⁰ by ceria or lanthana species. This could lead to the formation of an adduct MPd _x O (M = Ce or La) at the surface of the metal crystallites. The addition of ceria or lanthana resulted in an increase of the turnover rate and specific rate for steam reforming of methane. One possible explanation if that the Pd⁰*Pd^δ+O–M interfacial species (M = Ce or La) are oxidized by H₂O or CO₂, promoting the O* transfer to the metal surface. This could facilitate the removal of C* species from the metal surface, resulting in the increase of specific reaction rate and increase of the accessibility of CH₄ to metal active sites.     

Mechanosynthesis of the multiferroic cubic spinel Co2MnO4: Influence of the calcination temperature

Multiferroic materials showing magnetoelectric coupling are required in various technological applications. Many synthetical approaches can be used to improve the magnetic and/or electrical properties, in particular when the materials exhibit cationic valence fluctuations, as in the Co₂MnO₄ cubic spinel. In this compound, Co and Mn ions are in competition at the tetrahedral and octahedral positions, depending on their various oxidation states. The Co₂MnO₄ was prepared following two techniques: by a soft chemical route based on a modified polymer precursor method, and by a mechanoactivation route. Both approaches yield polycrystalline powders, but their crystallites sizes and particles morphologies differ as a function of the calcination conditions. The magnetic characterization (ZFC/FC cycles, ordering temperatures, ferromagnetic coercive fields and saturation magnetizations) showed that the synthesis procedure influenced the physical properties of Co₂MnO₄ mainly through the size of the magnetic domains, which play an important role on the magnetic interactions between the Co/Mn cations.