Physico-chemical properties,morphology and antioxidant activity of film from fish skin gelatin incorporated with root essential oils 总被引:1,自引:0,他引:1
The influences of three root essential oils (ginger, turmeric and plai) at different levels (25%, 50% and 100%, based on protein content) on properties and antioxidative activity of fish skin gelatin-based film were investigated. Films incorporated with all essential oils showed the lower tensile strength (TS) but higher elongation at break (EAB) with increasing amount of essential oils, compared with the control film (without oil incorporated), regardless of types of essential oil (p < 0.05). Water vapor permeability (WVP) of films containing essential oils decreased as the amount of essential oils increased (p < 0.05). Decreases in L*-value and increases in b*-, ΔE*- and transparency value were observed with increasing amount of essential oils incorporated (p < 0.05). FTIR spectra indicated that films added with essential oils, especially from plai root, exhibited higher hydrophobicity than the control film, as evidenced by higher amplitude at wavenunber of 2877–2922 cm−1 and 1732 cm−1. Lower degradation temperature was obtained in films containing essential oils. Microstructural study revealed that bilayer films could be formed when essential oils at level above 50% were incorporated. Film incorporated with plai and turmeric essential oils showed the higher DPPH and ABTS radical scavenging activity, respectively, (p < 0.05), compared with the control film and ginger essential oil added film. Thus, the incorporation of root essential oils directly affected properties of fish skin gelatin-based film, depending on types and levels incorporated. 相似文献
2.
Natthaporn Limpan Thummanoon Prodpran Soottawat Benjakul Surasit Prasarpran 《Journal of food engineering》2010
Effects of the ratios of fish myofibrillar protein (FMP) from bigeye snapper (Priacanthus tayenus) to polyvinyl alcohol (PVA) (FMP:PVA; 10:0, 8:2, 6:4, 5:5, 4:6, 2:8, 0:10) and pH levels (3 and 11) on the properties of resulting films were investigated. Both tensile strength (TS) and elongation at break (EAB) of films increased with increasing PVA content (p < 0.05). When PVA was incorporated up to 40%, films prepared at pH 11 had the higher TS than did those prepared at pH 3 (p < 0.05). However, as PVA content was greater than 40%, films prepared at pH 3 exhibited the higher TS than did those prepared at pH 11 (p < 0.05). Water vapor permeability (WVP) of the films prepared at pH 3 increased when PVA content increased up to 40% and decreased with further increases in PVA content (p < 0.05). PVA films had the higher TS, EAB and WVP than did FMP films and FMP/PVA blend films prepared at both pHs. Films exhibited the increased L∗ and a∗ values but decreased b∗ value with increasing PVA content at both pHs. Films prepared at pH 11 showed higher b∗ value than did those prepared at pH 3 when PVA content was greater than 40% (p < 0.05). FMP/PVA blend films exhibited the negligible transmission to the UV light. At pH 3, light transmission of the films increased as PVA content increased (p < 0.05). At all FMP/PVA ratios, films prepared at pH 11 were less transparent than those prepared at pH 3 (p < 0.05). Therefore, blend composition and pH level influenced the properties of FMP/PVA blend films. 相似文献
3.
Kanokwan Matmaroh Soottawat Benjakul Thummanoon Prodpran Angel B. Encarnacion Hideki Kishimura 《Food chemistry》2011
Acid soluble collagen (ASC) and pepsin soluble collagen (PSC) were extracted from scale of spotted golden goatfish (Parupeneus heptacanthus) with the yields of 0.46% and 1.20% (based on dry weight basis), respectively. Both ASC and PSC were characterised as type I collagen, containing α1 and α2 chains. β and γ components were also found in both collagens. Based on FTIR spectra, the limited digestion by pepsin did not disrupt the triple helical structure of collagen. ASC and PSC contained glycine (336–340 residues/1000 residues) as the major amino acid and had imino acids of 186–189 residues/1000 residues. Maximal transition temperatures (Tmax) were 41.58 and 41.01 °C for ASC and PSC, respectively. From zeta potential analysis, net charge of zero was found at pH 4.96 and 5.39 for ASC and PSC, respectively. Both collagens exhibited high solubility in acidic pH (2–4) and were soluble in the presence of NaCl at concentration up to 20 and 30 g/l for ASC and PSC, respectively. 相似文献
4.
5.
6.
Properties of protein-based film from fish skin gelatin incorporated with different citrus essential oils, including bergamot, kaffir lime, lemon and lime (50% based on protein) in the presence of 20% and 30% glycerol were investigated. Films containing 20% glycerol had higher tensile strength (TS) but lower elongation at break (EAB), compared with those prepared with 30% glycerol, regardless of essential oils incorporated (p < 0.05). Films incorporated with essential oils, especially from lime, at both glycerol levels showed the lower TS but higher EAB than the control films (without incorporated essential oil) (p < 0.05). Water vapour permeability (WVP) of films containing essential oils was lower than that of control films for both glycerol levels (p < 0.05). Films with essential oils had varying ΔE* (total colour difference), where the highest value was observed in that added with bergamot essential oil (p < 0.05). Higher glycerol content increased EAB and WVP but decreased TS of films. Fourier transforms infrared (FTIR) spectra indicated that films added with essential oils exhibited higher hydrophobicity with higher amplitude at wavenumber of 2874–2926 cm−1 and 1731–1742 cm−1 than control film. Film incorporated with essential oils exhibited slightly lower thermal degradation resistance, compared to the control film. Varying effect of essential oil on thermal degradation temperature and weight loss was noticeable, but all films prepared using 20% glycerol had higher thermal degradation temperature with lower weight loss, compared with those containing 30% glycerol. Films added with all types of essential oils had rough cross-section, compared with control films, irrespective of glycerol levels. However, smooth surface was observed in all film samples. Film incorporated with lemon essential oil showed the highest ABTS radical scavenging activity and ferric reducing antioxidant power (FRAP) (p < 0.05), while the other films had lower activity. Thus, the incorporation of different essential oils and glycerol levels directly affected the properties of gelatin-based film from fish skin. 相似文献
7.
Impact of divalent salts and bovine gelatin on gel properties of phosphorylated gelatin from the skin of unicorn leatherjacket 总被引:1,自引:0,他引:1
Phanngam Kaewruang Soottawat Benjakul Thummanoon Prodpran Angel B. Encarnacion Sittipong Nalinanon 《LWT》2014
The impact of zinc chloride (ZnCl2) and calcium chloride (CaCl2) as well as bovine gelatin (BG) on the gel strength of phosphorylated fish gelatin (PFG) from the skin of unicorn leatherjacket was investigated. The gel strength of PFG increased with increasing concentrations of ZnCl2 and CaCl2 (2.5–40 μmol L−1). A higher gel strength was observed with CaCl2, compared with ZnCl2. The gel strength of PFG with 20 μmol L−1 CaCl2 increased by 15.7%, compared to the control gel. Nevertheless, at higher concentration (40 μmol L−1) of both salts, gel strength of PFG decreased. Hardness of gels decreased with increasing PFG content (P < 0.05). Nevertheless, no differences in hardness were found amongst gels with BG/PFG ratios of 4:0 and 3:1 (P ≥ 0.05). Thus, PFG could be used in combination with CaCl2 to substitute for BG at a level of 25%. 相似文献
8.
Avtar Singh Soottawat Benjakul Thummanoon Prodpran 《International Journal of Food Science & Technology》2019,54(10):2831-2838
Effect of chitooligosaccharide from squid pen prepared using lipase (COS-L) at various concentrations (0–30 g kg−1) on gel properties of sardine surimi gel was investigated. Breaking force (BF) and deformation (DF) of gel were increased, when COS-L level was increased up to 10 g kg−1 (P < 0.05). Water holding capacity and whiteness of gel were improved with the addition of COS-L than those of control. Gel added with 10 g kg−1 COS-L had denser network with higher likeness score for all sensory attributes, compared to control. When gel incorporated with 10 g kg−1 COS-L was stored at 4 °C, BF, DF and whiteness were maintained during 10 days of storage. Textural properties of surimi gel added with COS-L were higher than those of control throughout storage. Thus, incorporation of 10 g kg−1 COS-L could improve gel properties of sardine surimi gel and retarded the deterioration of gel properties during refrigerated storage. 相似文献
9.
Gelatin powder from goat skin prepared by spray drying at various inlet temperatures (160–200°C) was characterized. Predominant particle sizes were in the range of 4.65–5.14?µm. Gelatin powder was mostly concave in shape with varying sizes, depending on inlet temperatures used. All gelatin powders were creamy whitish. Powder generally became more yellowish as the inlet temperature of spray drying increased (p?0.05). All gelatins contained α-chain as the dominant constituent. Nevertheless, α-chain of gelatin spray dried at 200°C was almost disappeared. Gel strength of gelatin decreased as the inlet temperature for spray drying increased (p?0.05). Gelatin with inlet temperature of 160°C had the highest gel strength (260?g) (p?0.05), which was comparable to the freeze-dried counterpart (268?g) (p?>?0.05). Goat skin gelatin spray dried with inlet temperatures of 160 or 180°C had higher gel strength than commercial bovine gelatin (p?0.05). All gelatins had solubility greater than 90% in the wide pH ranges (1–10). Therefore, spray drying with appropriate inlet temperature could be an effective means for production of gelatin powder from goat skin, exhibiting the properties equivalent to commercial bovine gelatin. 相似文献
10.
Phakawat Tongnuanchan Soottawat Benjakul Thummanoon Prodpran Ponusa Songtipya 《Food and Bioprocess Technology》2013,6(5):1113-1126
Film from fish protein isolate (FPI) from red tilapia (Oreochromis niloticus) muscle prepared at pH 3 and incorporated with 100 ppm Trolox (FPIT film) was prepared and characterized in comparison with film prepared from unwashed mince film (UWM film) during storage of 40 days at room temperature (28–32°C). FPIT film had higher tensile strength (TS) and elongation at break (EAB) but lower water vapor permeability (WVP) than UWM film (p?<?0.05). During the storage, FPIT film had much lower thiobarbituric acid reactive substances value than UWM film. Furthermore, FPIT was more transparent and had no yellow discoloration, as evidenced by no change in b* and ΔE* values during the storage of 40 days. Both UWM and FPIT films were stabilized mainly by hydrogen bond, followed by hydrophobic interaction, disulfide bond, and nondisulfide covalent bond. Fourier transforms infrared spectra indicated that FPIT film contained the lower amount of lipids with the lower amplitude of amide B band, compared with UWM film. Higher degradation temperature (Td) was observed in FPIT film, indicating a greater protein–protein interaction in film matrix. FPIT film had smoother surface and cross-section than UWM film. After 40 days of storage, both films had the increase in TS and Td but lower EAB, WVP, and protein solubility. This was more pronounced in UWM film and was associated with the formation of nondisulfide covalent bond in the film network, most likely mediated by the interaction between protein and lipid oxidation products via Maillard reaction. Thus, film from FPI incorporated with antioxidant had the improved mechanical and physical properties without yellow discoloration. 相似文献