Dyeing properties of oxygen low-temperature plasma-treated wool and nylon 6 fibres with acid and basic dyes

Wool and nylon 6 fibres treated with oxygen low-temperature plasma were dyed with acid and basic dyes. Despite the increase of electronegativity of the fibre surface caused by the plasma treatment, the rate of dyeing of wool was increased with both dyes, while that of nylon 6 was decreased with the acid dye and increased with the basic dye.     

The effect of sputter etching on the surface characteristics of dyed aramid fabrics

Three kinds of aramid fabrics, Technora (modified p-aramid), Conex (m-aramid) and Kevlar (p-aramid), were subjected to sputter etching and argon low-temperature plasma treatments after dyeing in black with disperse dyes. The depth of shade increased considerably on Technora and Kevlar with the sputter etching treatment, but not on Conex fabrics. Argon low-temperature plasma treatment had virtually no effect on the depth of shade on the aramid fabrics.     

The effect of washing and heat treatment on the surface characteristics of fluorocarbon resin-treated polyester

Polyester fabrics and films treated with two fluorocarbon resins were washed and heat treated. Water repellency, surface tension and ESCA measurements were carried out. Changes in the water repellency of the resin-treated polyester fabric caused by washing and heat treatment are related to modification of the chemical composition of the polyester surface.     

Two-dimensional thickness measurements based on internal reflection ellipsometry

An imaging ellipsometer technique on internal reflection geometry that can measure the thickness distribution of a thin film possessing an assumed refractive index is described. Because a prism is used for the internal reflection geometry, it was theoretically predicted that angular derivation from the normal incidence on the prism surface affects only the psi value by a factor of 0.97 at maximum. Measurements were carried out for an optical system of silica substrate-TiO2 layer-silica layer-protein film-air, with a thin-film array of dried protein as the sample film. Thickness of the protein films was two-dimensionally estimated only from the measured map of the delta value by use of the simulated relationship between the thickness and the delta value. The thickness map obtained was coincident on the whole with the results according to a mechanical scanning. The detection limit was approximately +/- 0.2 nm. These findings validate the optical effect of a high-index additional layer to improve the sensitivity and precision of thickness measurements of the sample film on transparent substrates.     

Basic study of a ship navigator's mental workload using salivary NO\documentclass{article}\usepackage{amsmath}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{amsfonts}\pagestyle{empty}\begin{document}$_{3}^{-}$ \end{document}

Evaluation of the mental workload during training for ship handling has usually depended on professionals (captain, pilot) who have lots of experience on board. We are attempting to evaluate a ship navigator's mental workload based on a physiological index. The physiological indices, namely heart rate variability (R–R interval), nasal temperature, and salivary amylase, are good indices for reading the mental workload during ship handling. Moreover, we find the possibility of using salivary NO$_{3}^{-}$ as a good index for evaluating the ship navigator's mental workload. Salivary NO$_{3}^{-}$ is expected to have a specific characteristic to represent quick response on the spot and the trend. We confirmed the response of students during simulator training, and then carried out the experiment on professionals on a real ship. We propose that salivary NO$_{3}^{-}$ can show a ship navigator's stress for ship handling in the simulator and on a real ship. This work to evaluate the ship navigator's mental workload using salivary NO$_{3}^{-}$ is the first attempt worldwide. © 2013 Institute of Electrical Engineers of Japan. Published by John Wiley & Sons, Inc.     

Modification of wool fibers by atmospheric pressure plasma treatment

Shrink‐proofing processing of wool fabrics by vacuum plasma treatment has been studied for many years. However, as a wool shrink‐proofing processing method, discharge treatment under atmospheric pressure, such as corona and low‐temperature electric plasma treatment, has been studied recently. In this study, an attempt was made to improve shrink‐proofing and other properties of a wool fabric by low‐temperature plasma treatment. The wool fabric was treated by pulsed atmospheric pressure plasma using a dielectric barrier discharge apparatus of the Institute of Textile Technology at Denkendorf by varying the power and flow rate of air. Shrink‐proofing, dyeing yield and water‐absorbing properties increased to a greater degree with the increase in the treatment time. However, the effect was saturated at 3 min. On the other hand, hysteresis of shearing property at large shear angle (2HG5), which is one of the mechanical parameters for measuring fabric hand by the Kawabata evaluation system (KES), becomes larger with the treatment time. It can be concluded that shear hysteresis value is related to the improvement in shrink‐proofing and other properties of the wool fabric.     

Laundering shrinkage of wool fabric treated with low-temperature plasmas under atmospheric pressure

Wool fabrics have been treated with helium/argon and acetone/argon low-temperature plasmas under atmospheric pressure. The plasma-treated fabrics were laundered several times and their shrink resistances investigated according to standard methods. Very high levels of shrink resistance to laundering were obtained through use of these treatments.     

Chemical modification of nylon 6 and polyester fabrics by ozone‐gas treatment

In a previous article, we reported on the ozone‐gas treatment of wool and silk fabrics in relation to the gas‐phase processing of textile fabrics. The treatment incorporated an oxygen element into the fiber surface and contributed to an increase in water penetration into the fabric. In this study, nylon 6 and polyester fabrics were treated with ozone gas in the same way as that of the wool and silk fabrics. The treatment incorporated much more oxygen into the fiber surface in the form of ? COH and ? COOH, as shown by electron spectroscopy for chemical analysis. Water penetration increased considerably with treatment, and the apparent dyeing rate and equilibrium dye uptake were also improved, especially for the polyester fabric, despite an increase in the crystallinity. Therefore, it seemed that the treatment brought about a change not only in the fiber surface but also in the internal structure of the fibers (the crystalline and amorphous regions) with regard to the dyeing behavior. Further, the mechanical characteristics of the ozone‐gas‐treated polyester and nylon 6 fabrics were measured with a Kawabata evaluation system apparatus. The shearing modulus and hysteresis widths increased with treatment, especially for the polyester fabric. Therefore, it was clear that the treatment caused a change in the fabric hand to crisp. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 1344–1348, 2006     

Studies on the surface free energy and surface structure of PTFE film treated with low temperature plasma

The surface free energy and surface structure of poly(tetrafluoroethylene) (PTFE) film treated with low temperature plasma in O₂, Ar, He, H₂, NH₃, and CH₄ gases are studied. The contact angles of the samples were measured, and the critical surface tension γ_c (Zisman) and γ_c (max) were determined on the basis of the Zisman's plots. Furthermore, the values of nonpolar dispersion force γ^a_s, dipole force γ^b_s, and hydrogen bonding force γ^c_s to the surface tensions for the plasma-treated samples were evaluated by the extended Fowkes equation. Mainly because of the contribution of polar force, the surface free energy and surface wettability of PTFE film which was treated with H₂, He, NH₃, Ar, and CH₄ for a short time increased greatly. Electron spectroscopy for chemical analysis (ESCA) shows that the reason was the decrease of fluorine and the increase of oxygen or nitrogen polar functional group on the surface of PTFE. © 1997 John Wiley & Sons, Inc. J Appl Polym Sci 63: 1733–1739, 1997