20钢热水管焊缝爆裂的失效分析 总被引:1,自引:0,他引:1
采用宏观形貌、金相组织和断口观察以及成分分析和力学性能测定等方法,分析了某20钢高温输水管爆裂的原因.结果表明,断裂失效发生在焊缝部位,焊缝组织存在明显蠕变现象,断口起裂处具有典型脆性断裂特征,裂纹内有腐蚀产物,属于典型应力腐蚀裂纹.裂纹扩展后期近外表面处具有蠕变疲劳裂纹特征.应力腐蚀裂纹是该热水管爆裂失效的主要原因. 相似文献
4.
5.
6.
Pitting corrosion of 316L stainless steel(316L SS)under various stress was studied by potentiodynamic polarization,electrochemical impedance spectroscopy(EIS)and Mott-Schottky(M-S)analysis in 3.5% NaCl solution.The results of polarization curves show that,with the increase of the stress,the pitting potentials and the passive current density markedly decrease firstly(180 MPa),and then increase greatly(200 MPa).The corresponding surface morphologies of the samples after the polarization test well correspond to the results.Mott-Schottky analysis proved the least Cl-adsorbed to the surface of passive film with more positive flat potential,indicating that a moderate stress could increase the pitting corrosion resistance of 316L SS in 3.5% NaCl solution. 相似文献
7.
设计一种由单片机构成的无线数显远程温度计,以8051单片机为控制核心,由MICRF102单片发射器芯片、MICRF007单片接收器芯片组成单片机无线串行接口电路,测温传感器使用DS18B20。 相似文献
8.
针对已服役近50 000 h的制氢转化炉炉管,分析了炉管的硬度、壁厚、蠕胀与金相组织,并与炉管运行近25 000 h的性能和已有的研究结果进行比较。结果表明炉管的硬度、壁厚、蠕胀等性能参数均在正常范围内。炉管组织的晶粒没有发生明显的长大,碳化物仍呈弥散分布状态。相对于运行25 000 h炉管的组织,仅发生了碳化物长大与部分晶界粗化。除少量超温炉管有蠕变孔洞外,正常运行的炉管的损伤程度为Ⅱ级,对应的服役寿命损耗在总寿命的20%范围内。 相似文献
9.
基于DSl820的单总线多点测温技术 总被引:1,自引:1,他引:0
阐述了通过单总线测温元件DSl820来实现多点测温的技术,实现方法是利用DSl820和89C51单片机构建单线多点温度测控系统,通过软件对单片机进行控制,从而实现一根总线多点测温,达到理想的测温效果。实验结果表明,该测控技术具有测温系统简单,测温精度高,连接方便,占用口线少等优点。该技术的创新主要在于能够利用一个通信接口同时监测几个甚至几十个温度数据,从而达到节省带宽,简化硬件设施的目的。 相似文献
10.