Room-temperature degradation of o-xylene in simulated air using an online-regenerable plasma-catalysis reactor with low amounts of nanosized noble metals on Co3O4

The plasma catalytic degradation of o-xylene in simulated air was improved by loading low amounts of Pt, Pd, or Au onto Co₃O₄. At room temperature, o-xylene conversion and CO_x selectivity using a0.1 wt% Pt/Co₃O₄ catalyst reached 98.9% and 80%, and the energy efficiency was at the top level in comparison with values in the literature. A stable o-xylene degradation performance could be obtained by online regenerating the heat-insulated reactor...     

CuCr2O4催化剂形貌特征与其SCR脱硝性能的关系

分别制备形貌为多面体状、颗粒状、球状的尖晶石型CuCr₂O₄催化剂,测试对比不同形貌CuCr₂O₄催化剂的SCR脱硝性能. 结果表明,多面体状CuCr₂O₄的催化活性最好,且在157 ℃时脱硝效率达到50%,在225~320 ℃脱硝效率超过99%,具有良好的抗硫、抗水性能. 脱硝活性由大到小依次为多面体状CuCr₂O₄、颗粒状CuCr₂O₄、球状CuCr₂O₄. 采用表征技术分析微观形貌对CuCr₂O₄脱硝性能的影响. N₂吸附-脱附结果显示,多面体状CuCr₂O₄具有最大的比表面积(25.5 m²/g)和最大的孔容积(0.154 cm³/g);X射线光电子能谱(XPS)结果显示,多面体状CuCr₂O₄相较于其他形貌拥有更高比例的表面活性氧(49.5%)和Cu⁺(16.2%);NH₃-程序升温脱附(NH₃-TPD)结果显示,多面体状CuCr₂O₄拥有最高表面酸浓度(0.12 mmol/g)及酸强度;H₂-程序升温还原(H₂-TPR)结果显示,多面体状CuCr₂O₄表面活性物种最易还原且数量最多(3.69 mmol/g),使得SCR反应在低温段更易进行. 多面体状CuCr₂O₄的高表面酸性与氧化还原性,使其具有良好的脱硝性能.     

甲烷等离子体裂解制氢制碳的影响因素研究

甲烷(CH₄)等离子体裂解是一种很有前景的制氢方法。采用针-针式纳秒脉冲火花放电方法研究了放电功率、CH₄含量、CH₄流量、反应温度以及不同背景气氛等对CH₄转化和产物分布的影响，并采用TEM与Raman方法对产物纳米碳的形貌和结构进行表征分析。结果表明：CH₄放电裂解产物主要是氢气(H₂)、纳米碳(C)和乙炔(C₂H₂),另有少量的乙烷(C₂H₆)和乙烯(C₂H₄)生成；在30 mL/min的CH₄/Ar总气体流量和10%的CH₄初始体积分数下，输入60 W功率时实现了CH₄转化率83.56%和H₂选择性70.28%。放电功率的增大有助于CH₄的完全裂解，促进H₂和C的生成；而随着CH_...