快淬Nd—Fe—B粘结磁体矫顽力机制

本文采用x光衍射、透射M(?)ssbauer谱和高分辨电镜,研究了快淬Nd_(13.5)Fe_(81.74)B_(4.76)合金的显微组织。快淬线速度为24 m/sec的粘结磁体性能最佳,作者发现,快淬Nd_(13.5)Fe_(81.74)B_(4.76)合金带的显微组织为单纯的Nd_2Fe_(14)B相微晶,不存在第二相(富Nd相、富B相或α-Fe相)。本合金粘结磁体的高内禀矫顽力(iHc≥14kOe)来源于Nd_2Fe_(14)B相的单畴机制。     

快淬Fe—Cr—Mo—Si—B非晶合金中的相分离

透射电镜观察到非晶Ｆｅ６５Ｃｒ１８Ｍｏ２Ｓｉ１Ｂ１４和Ｆｅ６２Ｃｒ１８Ｍｏ２Ｓｉ１ｂ１７基体中分布着纳米级颗粒状的非晶第二相。磁测量与Ｍｏｓｓｂａｕｅｒ谱显示出非晶样品由少量铁磁相与顺磁基体相组成，并表现出单畴颗粒的高矫顽力。快淬过程中这冷液体里硼的偏聚导致非晶合金中非晶第二相的形成及脆化。     

Coercivity Mechanism of Melt-spun Nd-Fe-B Bonded Magnet

The microstructures of melt-spun Nd_135-Fe_81.74B4.76 ribbons have been investigated bymeans of X-ray diffraction,Mossbauerspectroscopy and HREM.Experimental resultsshow that optimal magnetic properties of the bond-ed magnet can be obtained by melt-spun alloys atwheel velocity of 24m/s,the microstructure ofwhich was single phase Nd_2Fe_(14)B crystallites,andno other phases,such as Nd-rich,B-rich or x-Fephase,were present.It is considered that the highintrinsic coercivity ~iH_c can be attributed to the sin-gle-domain behaviour of Nd_2Fe_(14)B crystallitephase.     

快淬Nd—Fe—B永磁材料的透射电镜研究

用透射电子显微术研究了Nd_(13.5)Fe_(81.74)B_(4.76)快淬永磁材料结构与磁性的关系。从高分辨TEM象和电子衍射分析中证实该材料是单相的多晶Nd_2Fe_(14)B组织。冷速V=24m/s时,晶粒度～100nm,晶内完整无缺陷,晶界无第二相或无定形层。材料的高矫顽力应来源于完整而细小的Nd_2Fe_(14)B晶粒结构。     

Cr 和 Mo 对 Fe-Si-B 非晶磁性和热稳定性的影响

本文研究了3at%的过渡金属 Cr 和 Mo 原子分别取代 Fe_■Si_(11)B_(10)非晶中 Fe 原子对其基本物理性能和热稳定的影响,结果1at%的 Cr 和 Mo 原子分别使σ_s(RT)和T_o 降低约为4.07emu/g、7.30emu/g 和27℃、33℃;Mo 原子提高 Fe_(79)Si_(11)B_(10)非晶的玻璃化温度T_g、晶化温度 T_(xs)和 T_■的效果比 Cr 原子显著;3at%的 Mo 原子较明显地改善 Fe_(79)Si_(11)