排序方式: 共有33条查询结果,搜索用时 15 毫秒
1.
Aero-engine blisk welded by electron beam welding(EBW) method is a complicated structure. Fixtures were used to control the deformation of blisk during its manufacturing process. Finite element method was utilized to study the evolution of the welding residual stress and deformation of this structure. In which an attenuation function was applied to the double ellipsoid heat source model based on the characteristic of EBW, and the effects of fixtures on the welding residual stresses and deforamtion were also reserached. The simulation results showed that the temperature contour of weld cross section vertical to the weld centerline followed a “V” shape. Moreover, large welding residual stress and distortion were found in the interface between blisk and fixtures. The stress concentration was reduced sufficiently in starting and end part of weldment as the fixtures were removed after welding process, while the removing operation had almost no effects on the welding residual stress in the middle section of weld bead. 相似文献
2.
3.
4.
5.
曲伸 《仪表技术与传感器》1988,(2)
美国杂志《激光集锦与光电工艺》1987年第三期发表文章说,通过对有代表性的13家厂商的调查结果表明,光学镀膜设备制造业仍是一个处于兴旺、发展的行业。 一、发展趋势 Danavac公司的Willian F.Murphy指出在镀膜工业中的最新趋势有:采用隔离的净化房、自动化、监控系统、低温泵系统 相似文献
6.
采用多种软件的综合运用建立了整体叶盘的有限元模型,并基于焊接过程中温度之间相互影响程度选取了顺序依次焊接、90°和180°三种典型的焊接顺序,通过有限元分析的方法对不同焊接顺序产生的变形进行计算和分析.结果表明,以往使用的180°最远距离焊接顺序并不是最合理的焊接顺序,在相同的焊接工艺条件下,顺序依次焊接对整体叶盘圆度的影响相对较小.该分析结果说明在材料不同、焊接方法及结构不同的情况下,焊接顺序没有固定的模式,为整体叶盘及大型复杂结构件焊接顺序的合理选择提供了理论依据. 相似文献
7.
研究了不同退火热处理温度对激光沉积修复TA15/TC17钛合金显微组织及力学性能的影响规律。研究表明:TC17基体经退火热处理后双态组织中α片层长度、宽度及长宽比无明显变化。TA15修复区沉积态组织为粗大的原始β柱状晶,晶粒内为α/β网篮组织;当退火温度由610℃,630℃升到650℃后,TA15修复区α片层宽度明显增大,体积分数逐渐减少,长宽比下降,呈短棒状分布。经退火热处理后修复试样抗拉强度与塑性均明显提高,当退火温度为650℃时,抗拉强度最高为1102 MPa,与沉积态相比提高7. 1%,达到TC17锻件的98. 4%;断后伸长率为13. 5%,与沉积态相比明显提高,且高于TC17与TA15锻件标准;退火温度变化对显微硬度影响不大。 相似文献
8.
9.
研究了不同热处理制度对激光沉积DZ125高温合金显微组织、硬度及摩擦磨损性能的影响规律。结果表明:沉积区枝晶形貌为外沿生长的柱状枝晶,平均一次枝晶间距约为10.8μm,经单级时效(870 ℃/20h,AC)和双级时效(1100 ℃/4h,AC to 870 ℃/20h,AC)热处理后,试样的枝晶形貌与沉积态差别不大,γ"相均发生粗化现象,且双级时效热处理后的γ"相粗化程度更高、尺寸分布更为均匀;双级时效热处理制度下,不同低温时效温度γ"相的平均尺寸和含量不同,其中 1100 ℃/4h,AC to 870 ℃/20h,AC制度下,γ"相的平均尺寸和含量最大;经单级时效和双级时效热处理后,碳化物中Ti元素含量均呈下降趋势;双级时效热处理后,析出两种形貌不规则的MC碳化物,分别为富含Cr、Co元素的M23C6型碳化物和富含W、Mo元素的M6C型碳化物;单级时效和双级时效热处理试样的磨损机理均为磨粒磨损,双级时效热处理试样的显微硬度及耐磨性能均优于单级时效。 相似文献
10.
GH4169合金连续驱动摩擦焊接过程三维数值模拟 总被引:6,自引:0,他引:6
在考虑摩擦面上环向摩擦力对摩擦焊接过程影响的基础上,建立了连续驱动摩擦焊接过程的三维刚塑性热力耦合有限元模型。计算了GH4169合金棒材连续驱动摩擦焊接过程中的瞬态温度场、应力场及变形场,预测了焊件轴向缩短量。采用热电偶测温技术对摩擦焊接头外表面焊接过程的温度变化进行了实时测量,并测量了飞边形状和轴向缩短量。结果表明,摩擦焊接头的温度场、飞边形状和轴向缩短量的计算结果和实验结果吻合较好。模型有助于制定合理的焊接工艺规范。 相似文献