An experimental study for the effect of different clearances on burr, smooth-sheared and blanking force on aluminium sheet metal

In this study, an experimental study was carried out to examine the effect of different clearances on smooth-sheared depth, burr height and blanking force. Aluminium sheet metals with 0.8, 1, and 1.5 mm thicknesses were used in the experiments. These experiments were carried out in circular blanking dies to 6, 8, 10, and 12 mm diameters. Six different clearances (0.009, 0.064, 0.12, 0.175, 0.231 and 0.287 mm) were used for every material and diameter. The results of the experiment show that burr, smooth-sheared and punch force is strongly related to the clearance value. The results are in agreement with the results of previous theoretical and experimental work in the literature.     

UV curable lens production using molecular weight controlled PEEK based acrylic oligomer (Ac-PEEK)

We produced UV curable lenses with properties blocking short wave UV light. In the UV-curable formulations, we used an oligomer (Ac-PEEK) with another urethan oligomer (Mw = 2000). Radically active, molecular weight controlled Ac-PEEK was obtained by reacting 2-hydroxyl ethyl methacrylate with molecular- weight- controlled and isocyanate terminated PEEK (Mn = 4500). We characterized all synthesized monomer, oligomer and optical materials with UV/Vis spectrophotometer with interferogram, elemental analyser, mass spectrophotometer, proton nuclear magnetic resonance, Fourier transform infrared spectroscopy, thermal gravimetric analyzer, differential scanning calorimeter, scanning electron microscopy and gas chromatography. Results suggested that newly synthesized oligomer with the structure of PEEK absorbs short wave UV-light. Ageing tests [ISO 11979-5, Ophthalmic implants—intraocular lenses (IOL)—Part 5: Biocompatibility] performed on the IOL materials were successful. High contact angle of the obtained lenses suggests that all lenses were hydrophobic and SEM results revealed that lenses are morphologically homogeneous. Based on all positive properties just mentioned, we safely conclude that the lenses produced in this study are very promising for IOL production.     

Multilayer Graphene Broadband Terahertz Modulators with Flexible Substrate

Fabrication of terahertz modulators as simple devices with high modulation depth across a broad bandwidth is still very challenging. In this study, four different chemical vapor deposition grown multilayer graphene (MLG) modulators based on MLG/ionic liquid/gold sandwich structures have been investigated. Flexible substrates (PVC and PE) were chosen as host materials, and devices were fabricated with three different thicknesses. The resultant MLG devices can be operated at low voltages between 0 and 3.4 V providing nearly complete modulation between 0.2 and 1.5 THz with low insertion losses. Even with such low gate voltages, the devices have been doped significantly inducing 7–11-fold improvement in their sheet conductivities depending on device thickness. In addition, sheet conductivity has been improved more than three times as the graphene layer number increased from 30 to 100. With the demonstration of promising device performances, the proposed modulators can be potential candidates for applications in terahertz and related optoelectronic technologies.     

高亮度LED的高效率电流驱动电路

本文介绍调整高亮度LED电流的简单电路.它包括一个流行的高集成降压开关稳压器,此开关稳压器能精确地控制LED电流.MAX5035是工作在125KHz固定频率的DC/DC转换器,其宽范围的输入电压(7.5V～76V)特别适合于汽车应用.对于亮度控制,它能实现模拟(线性调光)或低频占空比调制(PWM调光).     

A review of cryogenic cooling in machining processes

The cooling applications in machining operations play a very important role and many operations cannot be carried out efficiently without cooling. Application of a coolant in a cutting process can increase tool life and dimensional accuracy, decrease cutting temperatures, surface roughness and the amount of power consumed in a metal cutting process and thus improve the productivity. In this review, liquid nitrogen, as a cryogenic coolant, was investigated in detail in terms of application methods in material removal operations and its effects on cutting tool and workpiece material properties, cutting temperature, tool wear/life, surface roughness and dimensional deviation, friction and cutting forces. As a result, cryogenic cooling has been determined as one of the most favourable method for material cutting operations due to being capable of considerable improvement in tool life and surface finish through reduction in tool wear through control of machining temperature desirably at the cutting zone.     

低噪声APD偏置电路

１ＡＰＤ的特性雪崩光电检测器 (ＡＰＤ)和ＰＩＮ二极管通常被作为接收器用于光通信中。其中ＡＰＤ适合于高灵敏度和高带宽的光接收电路。但这种器件在工作时需要施加一个反向结压 ,这样 ,当接收到射线时产生的电子空穴对会被外加电场收集并转换为电流 ,其电流强度正比于射线强度。另外 ,工作时施加在器件上的反向偏置电压会引发雪崩效应 ,其雪崩增益可通过改变偏压来进行调节。这就有可能对光纤接收器的增益进行优化。然而 ,要得到满意的雪崩增益 ,就必须给ＡＰＤ提供一个比较高的反向偏压。很多ＡＰＤ需要４０Ｖ～６０Ｖ的偏压 ,有些器件…     

Examination of 2-methacryloyloxyethyl phosphorylcholine polymer coated acrylic resin denture base material: surface characteristics and <Emphasis Type="BoldItalic">Candida albicans</Emphasis> adhesion

The aim of this study is to evaluate the effects of 2-methacryloyloxyethyl phosphorylcholine (MPC) polymer coating with various concentrations onto acrylic resin denture base material on surface characteristics such as contact angle and surface roughness and on Candida albicans adhesion which is the major factor of denture stomatitis. Specimens, prepared from heat-polymerized acrylic denture base material, were divided into control and three test groups, randomly. Surfaces of the specimens in test groups were coated with poly(MPC) (PMPC) by graft polymerization of MPC in different concentrations (0.25?mol/L; 0.50?mol/L and 0.75?mol/L), while no surface treatment was applied to the control group. Contact angles and surface roughness were examined, and chemical composition of the surfaces was analyzed by Attenuated Total Reflectance-Fourier Transform Infrared Spectroscopy (FTIR) to verify the presence of PMPC coatings. Then, specimens were incubated with C. albicans for 18?h and the number of adhered cells was determined. Upon PMPC coating, the contact angle values statistically decreased, but no difference was found in surface roughness values. A statistically significant decrease was observed in C. albicans adhesion in parallel with the increase in the MPC polymer concentration. There was no significant difference between 0.50?mol/L and 0.75?mol/L groups in terms of adhesion. These findings indicated that graft polymerization of MPC on acrylic denture base material reduces the adhesion of C. albicans, and may be evaluated as a coating for prevention of denture stomatitis.     

Development of a one-dimensional and semi-empirical model for a high temperature proton exchange membrane fuel cell

High temperature proton exchange membrane fuel cells (HT-PEMFC), which operate between 160 °C and 200 °C, can be generally used in portable and stationary power generation applications. In this study, a one-dimensional, semi-empirical, and steady-state model of a HT-PEMFC fed with a gas mixture consisting of hydrogen and carbon monoxide is developed. Some modeling parameters are adjusted using empirical data, which are obtained conducting experiments on a HT-PEMFC for different values of Pt loading and cell temperature. For adjusting these parameters, the total summation of the square of the difference between the cell voltages found using the experimental and theoretical methods is minimized using genetic algorithm. After finding the values of the adjusted parameters, the effects of different cell temperature, Pt loading, phosphoric acid (PA) percentage, and different binders (PBI and PVDF) on the performance of the fuel cell are examined. It was found that, the performance of the fuel cell using PVDF binder exhibited better performance as compared to that using PBI binder.     

Ni and Cu incorporated mesoporous nanocomposite catalytic materials

Nickel and copper incorporated MCM-41-like mesoporous nanocomposite materials prepared by the direct hydrothermal synthesis and the impregnation procedures showed highly attractive pore structure and surface area results for catalytic applications. The XRD patterns showed that characteristic MCM-41 structure was preserved for the materials synthesized following an impregnation procedure before the calcination step. The surface area of the Cu impregnated material with a quite high Cu/Si atomic ratio (0.19) was 631 m2/g. Very narrow pore size distributions with an average pore diameter of about 2.7 nm were obtained as a result of plugging of some of the smaller pores by Cu nanoballs. For lower metal to Si ratios (for instance for Ni/Si = 0.06) much higher surface area values (1130 m2/g) were obtained. In the case of nanocomposite materials synthesized by the direct hydrothermal route, MCM-41 structure was not destroyed for samples containing metal to Si atomic ratios as high as 0.12. In the case of materials containing Cu/Si and Ni/Si ratios over 0.2 wider pore size distributions and some decrease of surface area were observed.     

Producing CuO and ZnO composite thin films using the spin coating method on microscope glasses

In this work, we have presented a new route to produce pure ZnO and composite ZnO-CuO thin films. In the process we have started with pure ZnO thin films and ended up with CuO by doping Cu in various percentages, ranging from 0% to 100%. We have managed to attain crystal phases in all doping concentrations. All the produced thin films have been crystallized at the annealing temperatures of 600 and 700 °C for 6 h. The X-ray diffraction (XRD) spectra have been performed to see the formation of crystal phases of all pure ZnO and composite ZnO-CuO thin films. These give insight that the two crystal phases related to ZnO and CuO stayed together within the thin film matrices, which were produced in different doping concentrations, i.e. nZnO + mCuO (0 ≤ n, m ≤ 100%). The scanning electron microscopy (SEM) micrographs and UV–vis absorption spectra have also been taken to elucidate the structure and composition of the all films.