Extensions of polyacrylic acid ammonium salts in the adsorption layer to fluidize alumina slurries

An average shell volume occupied in the adsorption layer on alumina by a polyacrylic acid ammonium salts molecule (PAA) defined as the average area occupied by an adsorbed PAA on alumina multiplied by the average thickness of the water layer at the limit of thickening, has been calculated from the adsorbed amount of PAA and from the flow points of alumina in the presence of PAA of different molecular weights. A steric effect of the PAA dispersant on the dispersion of alumina resulted in a flow with no yield stress. This was due to the change of the extension of PAA in the adsorption shell from a sphere to an ellipsoid with a long axis which exceeded the effective distance that the van der Waals attraction force reaches at a molecular weight for the PAA of between 10 000–20 000.     

Osteoclastic features of multinucleated giant cells responding to synthetic hydroxyapatite implanted in rat jaw bone.

Multinucleated giant cells (MGCs) that responded to synthetic hydroxyapatite (HAP) implanted in rat mandibles were studied with electron microscopy. HAP used in this study sintered at 200 degrees C (HAP200) and at 125 degrees C (HAP1250) after the synthesis by a wet method. One to three weeks after the intraosseous implantation of HAP, MGCs responding to HAP200 had not only well-developed ruffled border and the clear zone but well-developed perinuclear Golgi complex, many mitochondria and vesicles in their cytoplasms. MGCs responding to HAP1250 had the clear zone, but not the ruffled border although they showed similar cytoplasmic features to those of MGCs responding to HAP200. They merely extended short slender cytoplasmic processes to HAP1250. These results suggest that although osteoclast-like MGCs respond to HAP implanted in the bone, the development of the ruffled border-clear zone system depends on physicochemical properties of HAP.     

Surface Hardening of Carbon Steel Using High Powered YAG Laser

A high powered YAG laser with kaleidoscope for surface modification was applied to the surface hardening of carbon steels containing 0. 18-0.54 wt% C without the absorbents, and the relationships between laser processing and surface hardening were investigated by hardness and microstructure. The structure of the hardened zone underwent complete martensitic transformation in all of the carbon steels tested, and its hardness increased with greater carbon content. Under identical irradiated conditions, the hardened zone expanded with increasing carbon content. A hardened zone extending from the surface to a depth of 1.0 mm was obtained at a laser power of 1.0 kW and a scanning speed of 1 mm/sec. It was found that in the surface hardening of carbon steels, a high powered YAG laser can be used to control the hardened zone by selecting the appropriate irradiation conditions, however, the hardened zone was affected by the assistant gas and the flow rate.     

Net shape formation of sub-micron alumina with reduced flaws by high-speed centrifugal compaction process

A new compacting method for powder materials is presented. High-Speed Centrifugal Compaction Process (HCP) utilizes centrifugal force of about 10,000 g for the compaction. HCP is suitable for net shape compaction of fine sub-micron and nano-powders. HCP possesses a unique compacting mechanism that is different from other colloidal processes including Pressure Casting (PC), and has a number of useful characteristics. HCP has a higher compacting speed than PC, wide applicability for net shape formation, as well as a defect removing function. Because of homogeneous and flawless green microstructure, HCP alumina shows superior sinterability and higher strength and hardness than most of other aluminas. This article is based on a presentation made in the symposium “The 3rd KIM-JIM Joint Symposium on Advanced Powder Materials“, held at Korea University, Seoul, Korea, October 26–27, 2001 under auspices of The Korean Institute of Metals and Materials and The Japan Institute of Metals.     

The Effect of Lanthanum on the Scales Developed on Thin Foils of Fe-20Cr-5Al at Very High Temperatures

A study has been undertaken of the effects oflanthanum on the oxidation of thin foils of Fe-20Cr-5Alin air at 1150°C. The addition of lanthanum causesthe time to breakaway to increase from about 24 hr for Fe-20Cr-5Al to over 400 hr. Oxidationof the lanthanum-containing alloy occurs in threestages. During the first stage, an-Al₂O₃ layer is establishedand thickens with time until the aluminum in the foil is depleted sufficiently for alayer of Cr₂O₃ to become stableand develop at the scale-alloy interface. This continuesto thicken at a relatively slow rate until breakawayoccurs. The main emphasis in the present paper has been anexamination and analysis of the scale established on thelanthanum-containing alloy in cross section in theanalytical transmission electron microscope (TEM), after an exposure period that coincides with thesecond stage of oxidation, prior to breakaway. The scaleat that time consists of three layers. The outer layeris composed of equiaxed Al₂O₃grains. The intermediate and inner layers consist of columnarAl₂O₃ grains and equiaxedCr₂O₃ grains, respectively.Numerous voids are observed in the oxide grainboundaries and at the intermediate-inner layerinterface. Lanthanum segregates in the oxide grain boundaries andits concentration increases toward the outermost surfaceof the scales. These results are consistent with thedynamic segregation model to account for the effects of reactive elements on thegrowth of Al₂O₃ scales.     

Lysozyme requires fluctuation of the active site for the manifestation of activity

Mutations around His15 which lie far away from the active site,stimulated glycol chitin activity of lysozyme at physiologicaltemperature. Del-Argl4Hisl5 lysozyme, a mutant lysozyme whoseArgl4 and Hisl5 were deleted together, and has the highest activityamong these mutant lysozymes, had a similar binding abilityto a trimer of N-acetyl-glucosamine, a substrate analogue, relativeto native lysozyme. This suggests that the increased activitywas due to an increased k_cat in the catalysis reaction. TheH-D exchange rate of the N-1 proton in the Trp63 which is locatedin the active site cleft, was enhanced in the Del-Argl4Hisl5lysozyme, while 2-D proton NMR analysis revealed no conformationalchange around Trp63. We conclude that some sort of fluctuationat the active site might be required for the manifestation ofactivity. This theory is supported by the finding that the Del-Argl4Hisl5lysozyme showed a shift in temperature dependency of activityto lower temperatures compared with that of native lysozyme.     

Effective renaturation of reduced lysozyme by gentle removal of urea

To increase the folding yield of concentrated reduced lysozyme,we developed a renaturation method by means of dialysis fromconcentrated urea with redox agents. After lysozyme was incubatedin the reducing buffer (8 M urea solution) with oxidized glutathione,renaturation of reduced lysozyme was started by dialysis againstthe dialyzing buffer containing 8 M urea with redox agents.The urea concentration of the dialyzing bottle was graduallydiluted with dialyzing buffer without urea at a flow rate of0.1 ml/min by high pressure pump. Using this systematic dialysis,a concentration as high as 5 mg/ml of reduced lysozyme couldbe renaturated in 80% yield, while the folding yield was <5%even at a concentration of 1 mg/ml using a conventional rapiddilution method [Goldberg et al. (1991) Biochemistry, 30, 2790–2797].Therefore, it was concluded that gentle removal of urea fromdenatured proteins, dissolved in concentrated urea solution,by means of dialysis should be useful to renature denaturedproteins effectively.     

Effect of temperature on humido-sensitive conducting polymer actuators

Temperature dependence of water vapor sorption and electro-active polymer actuating behavior of free-standing films made of poly(3,4-ethylenedioxythiophene) doped with poly(4-styrenesulfonate) (PEDOT/PSS) was investigated by means of sorption isotherm and electromechanical analyses. The non-porous PEDOT/PSS film, having a specific surface area of 0.13 m² g^?1, sorbed water vapor of 1080 cm³(STP) g^?1, corresponding to 87 wt%, at relative water vapor pressure of 0.95. A temperature rise from 25 °C to 40 °C lowered sorption degree, indicative of an exothermic process, where isosteric heat of sorption decreased with increasing water vapor sorption and the value reached 43.9 kJ mol^?1, being consistent with the heat of water condensation (44 kJ mol^?1). Upon application of 10 V, the film underwent contraction of 2.46% at 5 °C caused by desorption of water vapor due to Joule heating, which slightly decreased to 2.10% at 45 °C. The speed of contraction was one order of magnitude faster than that of expansion and less dependent on the temperature since water vapor sorbed in the film were forced to desorb by Joule heating. In contrast, the higher the temperature the faster the film expansion because diffusion coefficient increased as the temperature became higher.     

Wide-gap layered oxychalcogenide semiconductors: Materials, electronic structures and optoelectronic properties

Applying the concept of materials design for transparent conductive oxides to layered oxychalcogenides, several p-type and n-type layered oxychalcogenides were proposed as wide-gap semiconductors and their basic optical and electrical properties were examined. The layered oxychalcogenides are composed of ionic oxide layers and covalent chalcogenide layers, which bring wide-gap and conductive properties to these materials, respectively. The electronic structures of the materials were examined by normal/inverse photoemission spectroscopy and energy band calculations. The results of the examinations suggested that these materials possess unique features more than simple wide-gap semiconductors. Namely, the layered oxychalcogenides are considered to be extremely thin quantum wells composed of the oxide and chalcogenide layers or 2D chalcogenide crystals/molecules embedded in an oxide matrix. Observation of step-like absorption edges, large band gap energy and large exciton binding energy demonstrated these features originating from 2D density of states and quantum size effects in these layered materials.     

Cooperative behavior of various agents in dynamic environment

The multi-agent model is a model in which agents with limited ability cooperate each other to accomplish a goal. In this paper, we introduce a multi-agent model in which agents are created to imitate real ants. There are two different type of agents, each type of which has a particular task. We designed agents to communicate each other by using pheromone considering noise. On this model, we observed cooperative behavior of agents and evaluated conditions to make an order of behavior in the model.