Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

Nacre-Inspired,Liquid Metal-Based Ultrasensitive Electronic Skin by Spatially Regulated Cracking Strategy

The realization of liquid metal-based wearable systems will be a milestone toward high-performance, integrated electronic skin. However, despite the revolutionary progress achieved in many other components of electronic skin, liquid metal-based flexible sensors still suffer from poor sensitivity due to the insufficient resistance change of liquid metal to deformation. Herein, a nacre-inspired architecture composed of a biphasic pattern (liquid metal with Cr/Cu underlayer) as “bricks” and strain-sensitive Ag film as “mortar” is developed, which breaks the long-standing sensitivity bottleneck of liquid metal-based electronic skin. With 2 orders of magnitude of sensitivity amplification while maintaining wide (>85%) working range, for the first time, liquid metal-based strain sensors rival the state-of-art counterparts. This liquid metal composite features spatially regulated cracking behavior. On the one hand, hard Cr cells locally modulate the strain distribution, which avoids premature cut-through cracks and prolongs the defect propagation in the adjacent Ag film. On the other hand, the separated liquid metal cells prevent unfavorable continuous liquid-metal paths and create crack-free regions during strain. Demonstrated in diverse scenarios, the proposed design concept may spark more applications of ultrasensitive liquid metal-based electronic skins, and reveals a pathway for sensor development via crack engineering.     

薄层罩面在高速公路预防性养护中的应用

结合广珠西高速路面超薄磨耗层的具体应用,论述了超薄磨耗层对原材料技术要求、配合比设计、施工工艺和施工关键技术控制等。     

In situ Raman spectroscopic study towards the growth and excellent HER catalysis of Ni/Ni(OH)2 heterostructure

The electrochemical water splitting to produce H₂ in high efficiency with earth-abundant-metal catalysts remains a challenge. Here, we describe a simple “cyclic voltammetry + ageing” protocol at room temperature to activate Ni electrode (AC-Ni/NF) for hydrogen evolution reaction (HER), by which Ni/Ni(OH)₂ heterostructure is formed at the surface. In situ Raman spectroscopy reveals the gradual growth of Ni/Ni(OH)₂ heterostructure during the first 30 min of the aging treatment and combined with polarization measurements, it suggests a positive relation between the Ni/Ni(OH)₂ amount and HER performance of the electrode. The obtained AC-Ni/NF catalyst, with plentiful Ni–Ni(OH)₂ interfaces, exhibits remarkable performance towards HER, with the low overpotential of only 30 mV at a H₂-evolving current density of 10 mA/cm² and 153 mV at 100 mA/cm², as well as a small Tafel slope of 46.8 mV/dec in 1 M KOH electrolyte at ambient temperature. The excellent HER performance of the AC-Ni/NF could be maintained for at least 24 h without obvious decay. Ex situ experiments and in situ electrochemical-Raman spectroscopy along with density functional theory (DFT) calculations reveal that Ni/Ni(OH)₂ heterostructure, although partially reduced, can still persist during HER catalysis and it is the Ni–Ni(OH)₂ interface reducing the energy barrier of H1 adsorption thus promoting the HER performance.     

埋地管道泄漏内封堵装置设计与研究

针对流体输送埋地管道泄漏问题,设计了一种利用管道机器人携带封堵气囊进行快速应急封堵修复的埋地管道泄漏内封堵装置。采用矩阵变换方法建立了牵引系统驱动轮过弯方程,利用MATLAB软件对过弯方程进行了验证,同时利用ADAMS软件仿真分析过弯路径与驱动轮转角对牵引系统行走速度的影响。研究结果表明:由两个串联封堵器组成的应急封堵系统可满足复杂工况下的管道泄漏封堵要求;牵引系统驱动轮在弯管内部行走时,单轮速度呈周期性变化,但三个驱动轮整体周期运动特性一致;驱动轮转角在25°~40°时,牵引系统行走速度与驱动轮转角成正比,且转角为30°时驱动效果最好。该内封堵装置的结构设计可为管道泄漏应急封堵领域装备的研发提供重要参考。     

SO4^2-／ZrO2固体超强酸的制备及其催化合成ETBE的研究

采用沉淀一浸渍法制备了负载型SO4^2-／ZrO2固体超强酸催化剂，运用IR、XRD等方法表征所制备催化剂的物化性质。结果表明，所制备的催化剂具有固体超强酸催化剂的特征，酸性与焙烧温度有关，适当提高焙烧温度有利于样品酸强度的提高，但焙烧温度过高会导致脱硫；浸渍液H2SO4浓度高有利于提高催化剂的硫含量，但是浓度过高，会在催化剂上形成硫酸盐，从而降低催化剂的比表面积和酸性。采用制备的催化剂气相催化乙醇与叔丁醇合成乙基叔丁基醚反应，乙基叔丁基醚的选择性为54．71％。     

负载型复合载体及其镍基催化剂的性能

采用溶胶-凝胶法制备了负载型ZrO_2/Al_2O_3和ZrO_2/Al_2O_3-SiO_2复合载体,研究了不同复合载体对Ni基催化剂CO_2重整甲烷反应和性能的影响,并用XRD、IR、TPR、TPD和BET等方法对复合载体及催化剂进行了表征。结果表明,ZrO_2负载在基载体后比表面积、碱性、活性组分Ni的分散度和Ni与ZrO_2的相互作用增大。NiO在复合载体表面的分散容量与ZrO_2的负载量有关,ZrO_2的负载量为37．5%时NiO的分散容量达最高值(24．0%)。与Ni/ZrO_2相比,Ni/ZrO_2/Al_2O_3-SiO_2和Ni/ZrO_2/Al_2O_3催化剂对CO_2的吸附能力增大,CO_2吸附量增加,酸强度降低,CO_2重整CH_4反应活性提高,其中以Ni/ZrO_2/Al_2O_3催化剂的活性最好。     

热声制冷机及其改进实验研究

热声制冷作为一种很有前途的制冷方法，在国内外相关领域引起了极大兴趣。热声制冷机由声发生器、共振管、板叠及高、低温换热器等部分组成。对声驱动器的振动膜及其冷却系统、气体弹簧系统、高、低温换热器进行了初步改进，使制冷机冷端温降从原来的12℃提高到27℃左右，这是目前国内报道的最大温降。     

类胡萝卜素的命名

本根据国际理论与应用化学协会(IUPAC)所制定的命名规则和国际上认可的习惯名称，对类胡萝卜素的命名进行了详细的说明。