Damage evolution in polymer due to exposure to high-pressure hydrogen gas

The use of hydrogen as a fuel is increasing exponentially, and the most economical way to store and transport hydrogen for fuel use is as a high-pressure gas. Polymers are widely used for hydrogen distribution and storage systems because they are chemically inert towards hydrogen. However, when exposed to high-pressure hydrogen, some hydrogen diffuses through polymers and occupies the preexisting cavities inside the material. Upon depressurization, the hydrogen trapped inside polymer cavities can cause blistering or cracking by expanding these cavities. A continuum mechanics–based deformation model was deployed to predict the stress distribution and damage propagation while the polymer undergoes depressurization after high-pressure hydrogen exposure. The effects of cavity size, cavity location, and pressure inside the cavity on damage initiation and evolution inside the polymer were studied. The stress and damage evolution in the presence of multiple cavities was also studied, because interaction among cavities alters the damage and stress field. It was found that all these factors significantly change the stress state in the polymer, resulting in different paths for damage propagation. The effect of adding carbon black filler particles and plasticizer on the damage was also studied. It was found that damage tolerance of the polymer increases drastically with the addition of carbon black fillers, but decreases with the addition of the plasticizer.     

Electrical and optical properties of MoO3-V2O5 mixed oxide films

Vacuum deposited MoO₃-V₂O₅ films of different molar concentrations have been used for DC electrical conductivity studies at different temperatures. The optical absorption spectra of MoO₃-V₂O₅ films of different molar concentrations have been measured. From these measurements it is found that optical band gap and activation energy vary with molar concentration of MoO₃-V₂O₅ films.     

Tyrosine kinase inhibition produces specific alterations in axon guidance in the grasshopper embryo

Tyrosine kinase signaling pathways are essential for process outgrowth and guidance during nervous system development. We have examined the roles of tyrosine kinase activity in programming growth cone guidance decisions in an intact nervous system in which neurons can be individually identified. We applied the tyrosine kinase inhibitors herbimycin A and genistein to whole 40% grasshopper embryos placed in medium, or injected the inhibitors into intact grasshopper eggs. Both inhibitors caused interneuronal axons that normally would grow along the longitudinal connectives to instead leave the central nervous system (CNS) within the segmental nerve root and grow out toward the body wall muscles. In addition, herbimycin A produced pathfinding errors in which many longitudinal axons crossed the CNS midline. To study how this drug affected guidance decisions made by individual growth cones, we dye-filled the pCC interneuron, which normally extends an axon anteriorly along the ipsilateral longitudinal connective. In the presence of herbimycin A, the pCC growth cone was redirected across the anterior commissure. These phenotypes suggest that tyrosine kinase inhibition blocks a signaling mechanism that repels the growth cones of longitudinal connective neurons and prevents them from crossing the midline.     

Catalytic Materials for High-Temperature Combustion

Catalytic combustion, as an alternative to conventional thermal combustion, has received considerable attention during the past decade. Research efforts have been promoted by the need to meet governmental demands concerning pollution and the wish to use energy sources more efficiently. The two main advantages offered by catalytic combustors over flame combustors apply to these goals:

1. Catalytic combustion can be carried out over a wide range of fuel concentrations in air and at low temperatures.
2. These low temperatures result in attaining NO, emission levels substantially lower than possible with conventional combustors.

     

Synthesis and characterization of aromatic copolyesters containing siloxane linkages in the polymer backbone

A new series of aromatic copolyesters containing siloxane linkages were prepared by the melt polymerization of bisphenol A (BPA) with eugenol end‐capped siloxane (EuSi), diphenyl terephthalate (DPT), and diphenyl isophthalate (DPI) in varying ratio in the temperature range 220–290°C under reduced pressure in the presence of dibutyl tin dilaurate (DBTL) catalyst. The siloxane copolyesters prepared were characterized by FTIR, ¹H‐NMR spectroscopy, solution viscosity, thermogravimetric analysis, differential scanning calorimetry, and X‐ray diffraction. The effect of incorporation of eugenol end‐capped siloxane was studied on the properties of BPA/DPI/DPT copolyesters. The glass‐transition temperature of copolyester was decreased from 184 to 70°C by incorporation of 20% of eugenol end‐capped siloxane. All copolyesters were found to be soluble in commonly used aprotic polar solvents and had film‐forming properties. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 3222–3228, 2006     

Creep and Stress Rupture Behavior of an Advanced Silicon Nitride: Part I, Experimental Observations

Cylindrical buttuohead specimens of an advanced silicon nitride were tested in uniaxial tension at temperatures between 1422 and 1673 K. In the range 1477 to 1673 K, creep deformation was reliably measured using high-temperature contact probe extensometry. Extensive scanning and transmission electron microscopy has revealed the formation of lenticular cavities at two-grain junctions at all temperatures (1422–1673 K) and extensive triple-junction cavitation occurring at the higher temperatures (1644–1673 K). Cavitation is believed to be part of the net creep process. The stress rupture data show stratification of the Monkman–Grant lines with respect to temperature. Failure strain increased with increase in rupture time or temperature, or decrease in stress. Fractography showed that final failure occurred by subcritical crack growth in all specimens.     

Microwave-Hydrothermal Processing of BiFeO3 and CsAl2PO6

Microwave-hydrothermal (M-H) processing was compared with conventional-hydrothermal (C-H) processing in the crystallization of BiFeO₃ and CsAl₂PO₆ phases. The presence of the microwave field led to accelerated kinetics of the crystallization of both these phases as detected by powder X-ray diffraction. The acceleration of reaction rates under microwave field is expected to lead to energy savings during ceramic processing.