我国铸造有色合金及其特种铸造技术发展现状

结合我国在铸造有色合金领域的发展概况,从合金发展、应用和有色合金熔体技术以及特种铸造在有色合金中的应用角度,分析了五十年来我国在该领域所取得的成绩和存在的问题,以引起广大科技工作者和生产技术人员对这方面自主创新的重视,不断提高铸造有色合金的技术水平,扩大其应用领域。     

Microstructure and mechanical properties of high strength as—cast Ti—15—3 alloy

The effects of heat treatment and solidification cooling rate on the microstructure and mechanical properties of as-cast Ti-15-3 alloy prepared by induction skull melting method were investigated.Results show that the microstructure of as-cast Ti-15-3 alloy changes from the features of simplified and larger size of beta grains to finer grain size with increasing solidification cooling rate.After solution treatment and different ageing treatment,alpha phase precipitates in grains interior as well as in grain boundaries.Due to the modification of the precipitate phase,the tensile stength and elongation of the alloy are improved simultaneously.A good combination of the values of 1.406GPa of σb and 4.5% of δ was obtained,which will be satisfied the use of this kind of alloy in critical areas.     

钛合金冷坩埚电磁约束铸造工艺研究

针对液态下化学性质相对活泼的钛合金,采用冷坩埚技术对电磁约束铸造工艺过程进行了试验研究,考察了工艺条件对成形坯件表面质量和内部组织的影响.结果表明:试样抽拉速度变化对表面质量和宏观组织的影响明显,加热功率虽然对组织变化影响不大,但对表面质量影响较为显著.通过优化工艺,可以获得既有较光滑铸造表面又具有一次定向凝固组织的钛合金铸件.讨论了铸造过程裂纹和组织缺陷的形成机理,获得到了表面光滑无裂纹,宏观组织为柱状晶的钛合金大尺寸圆坯.     

冷坩埚熔铸技术的研究及开发现状

综述了冷坩埚技术的原理和特点、目前的研究及开发现状。冷坩埚具有无污染，可熔化高熔点金属，制备的材料组织均匀等优点。冷坩埚技术在以下领域得到广泛的研究和应用：与熔化技术相结合能高纯均匀熔炼活性金属，通过起熔材料能制备陶瓷材料；与连铸技术相结合能进行冷坩埚电磁连铸技术，提高铸锭表面质量，改善内部组织；与定向凝固和连铸技术相结合的冷坩埚定向凝固技术已成功进行钛合金的定向凝固；与多晶硅制备技术相结合能连续制备多晶硅，杂质含量少；与雾化沉积技术相结合的冷坩埚雾化沉积技术具有熔化合金种类多、适用范围广的优点。冷坩埚的自身特点决定了其必将更受重视和广阔发展前景。     

Equivalent heat transfer coefficient at casting/Cu mould interface and temperature field simulation

1　INTRODUCTIONThesolidifiedmicrostructuresofalloysdependontheirsolidifyingprocesswhoseprimarycharacteristicsarethetemperaturedropofthesuperheatedmeltandthere leaseofthelatentheat.Sothestudyontheheattransferduringthesolidificationprocessistheessentialprobleminthesolidificationtheorystudy .Theresearchersworkingonthenumericalsimulationofthesolidificationprocessallknowthattheinterfacialheattransfercoefficientatthecasting/mouldisavariablechangingwithtime .Thusthedeterminationoftheinterfacialh…     

光纤SINS/GPS组合导航系统分析

为提高光纤陀螺捷联惯导系统的精度,以光纤陀螺捷联惯导系统与全球定位系统（GPS Globle Position System）为研究对象,采用联邦卡尔曼滤波算法,构成了SINS/GPS（Strap-down Inertial Navigation Systerm/Globle Position System）组合导航系统。仿真结果表明,该算法能及时修正子滤波器的偏差,大大降低子滤波器的模型误差,进而提高整个滤波器的精度,并有效克服了滤波发散现象。     

工艺参数对冷坩埚连续铸造Ti6Al4V表面的影响

为消除冷坩埚连续成形钛合金铸棒表面缺陷，了解工艺参数对表面质量影响规律，并制备出无裂纹铸棒，通过正交试验和理论分析的方法，研究了不同工艺参数对表面质量的影响，研究表明：表面质量随功率和线圈匝数的增加而变坏，随抽拉速度和拉锭高度的增加先变好后变坏；各参数影响程度不同，线圈匝数影响最大，功率次之，抽拉速度再次，拉锭高度影响最小；铸造表面质量良好钛合金棒的工艺参数为：抽拉速度5mm／min，功率50kW，线圈3匝，拉锭高度30mm。     

Ti-13Al-29Nb-2.5MoISM过程中Al元素的挥发损失速率

借助于Kohler三元溶液模型和Miedema二元溶液生长热模型 ,计算了Ti -1 3Al -2 9Nb -2 .5Mo合金中Ti、Al及Nb组元的活度系数 ,并在此基础上计算了合金中组元的平衡分压及Al元素的挥发损失速率 .结果表明 ,组元的活度系数、平衡分压及Al元素的挥发损失速率均随温度的升高而增大 .存在一个临界外压 (约为 1 3 3Pa) ,当外压大于此值 ,挥发损失速率急剧减小并趋于一稳定值 .这给合金熔炼过程中合金成分控制提供了理论指导 .     

工艺参数影响冷坩埚熔铸Ti6Al4V温度场计算

为有效利用冷坩埚,更优控制工艺参数,获得良好冶金质量的铸棒,计算了冷坩埚连续熔铸与定向凝固Ti6Al4V温度场,对冷坩埚熔凝条件下的边界条件、驼峰和运动单元作相应处理.计算结果表明:在52kW,抽拉速度为1.2、3、4.8、6mm/min时,随抽拉速度增加,送料棒熔化量减小,驼峰过热度变小,凝固界面位置下移,形状变凹;抽拉速度为1.2mm/min时为平凝固界面.在抽拉速度为3mm/min,功率为44、48、52kW和56kW时,随功率增大,送料棒熔化区域变大且过热度增加,驼峰体积增大且过热度增加,凝固界面位置下移,形状变凹;48kW时为平凝固界面.工艺参数对凝固界面的影响计算结果与实验结果基本一致.     

钛合金熔体活度计算及合金与铸型的界面反应

在深入分析Miedema合金生成热模型的基础之上,运用化学反应和溶液热力学理论对钛熔体中溶质元素的活度系数进行了理论计算,进而评述了钛合金熔体的化学活性变化程度,通过对Ti6A14V合金和Ti15V3Cr3Sn3Al合金与所选择的耐火氧化物类铸材料的实验研究结果分析,可以认为添加合金元素以后钛熔体的化学活泼性并没有发生实质性的改变,由于熔体仍然具有相当高的化学活性,导致合金与铸型之间的界面反应是严重的,计算与实验结果吻合,同时所进行的理论分析和实验研究对于铸用高稳定性铸型材料的选择,铸优质的钛合金铸件具有一定的理论和实际指导作用。