Synthesis and properties of UV-curable hyperbranched polyurethane and its application in the negative-type photoresist

UV-curable hyperbranched polyurethane(UV-HBPU) containing carboxyl groups was synthesized from isophorone diisocyanate(IPDI), diethanolamine(DEOA), polyethylene glycol(PEG-400), hydroxyethyl acrylate(HEA), and 2,2-bis(hydroxymethyl) propionic acid(DMPA). The UV-HBPU was used as a negative-type photoresist for a printed circuit board(PCB). Fourier-transform infrared spectroscopy(FTIR) and proton nuclear magnetic resonance(1HNMR) spectroscopy of UV-HBPUs indicated that the synthesis was successful. Differential scanning calorimetry(DSC) and thermogravimetric analysis(TGA) showed that the thermal stability of the UV-HBPUs decreased as the HEA content increased. The polymer exhibited excellent photoresist properties, and the resolution of circuits based on this negative-type photoresist reached 10 μm.     

巯-烯光聚合制备氨基酸基光固化涂层的研究

在碱催化条件下,L-苯丙氨酸与L-酪氨酸分别与溴丙烯反应,合成了烯丙基苯丙氨酸(AP)和烯丙基酪氨酸(AT)光敏树脂,然后将AP与AT树脂分别与多官硫醇混合,通过UV固化制备了氨基酸基光固化涂层。采用傅里变换叶红外光谱(FT-IR)、核磁共振氢谱(¹H NMR)表征了树脂的分子结构,利用实时红外(ATR-FTIR)测试了树脂的巯-烯光聚合速率,并对涂层的性能进行了测试。结果表明:光聚合速率较快,巯基转化效率与硫醇的官能度呈负相关,硫醇的官能度越大,所带来的位阻影响越大,反应效率越低;AP树脂所得涂层的玻璃化转变温度为21～29℃;AT树脂所得涂层对钢板的附着力为0级,耐冲击性较优,具有较高的透明度,玻璃化转变温度为11～15℃;此外,这些涂层热失质量10%时所对应温度均在300℃左右,热稳定性较好。     

高职计算机教育中学生实践能力培养方式

文章首先针对当前高职计算机专业开展学生时间能力培养所遇到的难点进行总结,在此基础上分析了提升学生实践能力的有效教学方法,结合高职学生的实际状况对实训教学规划进行总结,并整理出未来的高职计算机教育专业学生实践能力培养方法,为学生未来的就业竞争能力提升创造有利条件.     

Preparation and characterization of carboxylterminated poly (butadiene-co-acrylonitrile) -epoxy resin prepolymers for fusion-bonded-epoxy powder coating

Liquid carboxyl-terminated poly(butadiene-co-acrylonitrile)(CTBN)-epoxy resin(EP) prepolymers were prepared with different contents of CTBN.The chemical reactions between EP and CTBN were characterized by Fourier ransform infrared(FTIR) spectroscopy and gel permeation chromatography(GPC).The scanning electron micrograph(SEM) and dynamic mechanical analysis(DMA) of curing films showed phase separation,and the rubber particles were finely dispersed in the epoxy matrix.Mechanical properties analysis of curing films showed that impact strength and elongation at break increased significantly upon the addition of CTBN,indicating good toughness of the modified epoxy resins.Thermogravimetric analysis(TGA) showed that the incorporation of CTBN had little effect on the thermal stability of EP.Fusion-bonded-epoxy(FBE) powder coatings modified with CTBN-EP prepolymers were prepared.The experimental results demonstrate the ability of CTBN-EP prepolymers,toughening technology to dramatically enhance the flexibility and impact resistance of FBE coatings without compromising other key properties such as corrosion protection.     

248nm光刻胶用丙烯酸酯共聚物的合成与性能EI北大核心CSCD

以对乙酰氧基苯乙烯(ASM)、丙烯酸叔丁酯(TBA)、丙烯酸四氢呋喃酯(TA)和2-甲基-2-金刚烷基甲基丙烯酸酯(MAM)为单体,偶氮二异丁腈(AIBN)为引发剂,通过自由基聚合制备了不同MAM含量的丙烯酸酯类共聚物P(ASMco-TBA-co-TA-co-MAM)(PATTM),加入一定量的甲醇钠和甲醇进行醇解,制得丙烯酸酯类共聚物PATTM-A。用傅里叶变换红外光谱、核磁共振氢谱、凝胶渗透色谱、差示扫描量热法等方法对共聚物PATTM和PATTM-A的结构与性能进行了表征;以PATTM-A为基体树脂配制了光刻胶,利用扫描电子显微镜测试了光刻胶分辨率。结果表明,随着MAM含量升高,PATTM-A的相对分子质量下降,玻璃化转变温度升高,耐碱性增强,所制备的光刻胶分辨率可达0.5μm。     

试论高职计算机教育的现状及发展方向

文章首先针对高职院校开展计算机教育教学现状进行介绍,在此基础上重点探讨计算机类教育教学的有效方法,并针对计算机类学科的教学体系改进方法做出整理.最后分析了高职院校计算机教育的未来发展方向,帮助高职教育工作人员明确未来的教学方法完善目标,为学生营造更高效的技能学习环境.     

高分子纳米复合气敏材料研究进展

综述了近年来高分子纳米复合气敏材料的研究进展,主要介绍了聚合物/碳纳米管、聚合物/金属氧化物和碳纳米管/金属或金属氧化物3类气敏材料的研究结果,指出今后研究的重点并对其研究前景作出了展望。     

光敏纳米SiO2制备及在光致抗蚀材料中的应用

经溶胶-凝胶法制得纳米SiO2,用不同结构的双键硅烷偶联剂对其表面进行原位接枝改性,得到两种光敏纳米SiO2(M70SiO2和M50SiO2),并将其添加到紫外光固化丙烯酸酯预聚物中,制得杂化光致抗蚀材料。通过测定光敏参数(D0n.5)考察其光敏性知,杂化光致抗蚀材料光敏性明显增加,当光敏纳米SiO2的质量分数增至13.7%～15.8%时,光敏参数达25 mJ/cm2～27 mJ/cm2;用差示扫描量热仪(DSC)及热机械分析(TMA)考察抗蚀材料的热性能,结果显示,随光敏纳米SiO2用量增加Tg升高,热膨胀系数减小,同时分辨率和精密性并未因光敏纳米SiO2的加入而降低。     

生物基光固化涂料研究进展

以生物质原料部分或完全替代石化原料,并利用快速高效的光固化技术来制备生物基光固化涂料已经成为涂料领域一个重要研究方向。本文从结构出发,总结了植物油、腰果酚、木质素、单宁酸、松香、异山梨醇、衣康酸等生物质原料的化学改性路径,并通过配方调控使其应用于光固化涂料领域。总结对比了一些石油基和生物基光固化涂料的基本性能,并对未来生物基光固化原料代替石油基化学品的发展趋势进行了展望。     

支化型苯乙烯-马来酸酐共聚物超细包覆碳黑的制备

采用相分离技术在炭黑表面包覆支化型苯乙烯-马来酸酐共聚物(BPSMA)制备超细包覆炭黑,探讨了相分离剂滴加速度、BPSMA用量、pH、炭黑质量分数以及分散时间对超细包覆炭黑粒径的影响。FTIR、TEM和对水接触角测试结果证实,炭黑表面包覆了BPSMA,超细包覆炭黑较佳的制备工艺为:相分离剂滴加速度3 mL/min,BPSMA用量为炭黑质量的20%,pH=10,炭黑质量分数为8%,超声波处理时间10 min。与线型苯乙烯-马来酸酐共聚物包覆炭黑分散体相比,相同条件下,BPSMA超细包覆炭黑分散体的粒径较小,稳定性较高,其印花织物的K/S值和摩擦牢度较高。