排序方式: 共有41条查询结果,搜索用时 15 毫秒
1.
2.
研究了La位Dy掺杂对La0.7~xDyxSr0.3MnO3(x=0.00、0.10、0.15、0.20、0.30、0.40、0.50、0.60、0.70)体系输运行为的影响.实验结果表明:随Dy掺杂的增加,体系由长程铁磁有序向自旋团簇玻璃态、反铁磁状态转变.高掺杂时的输运性质在其磁背景下发生异常,在x=0.50时,发现了在ABO3结构中很少出现过的在Tc附近发生绝缘体-金属相变之后又发生从金属一绝缘体相变的现象;对x=0.60,0.70,在远离Tc的温区体系表现为绝缘体. 相似文献
3.
4.
Large Magnetic Entropy Effect in La2/3Ca1/3MnO3 总被引:2,自引:0,他引:2
彭振生 《中国稀土学报(英文版)》2004,22(2):232-234
The magnetocaloric effect in the colossal magnetoresistance material La2/3Ca1/3MnO3 was studied. From the measurements of temperature dependence of magnetization in various magnetic fields, the large magnetic entropy change associated with the ferromagnetic-paramagnetie transition was discovered. This result suggests that perovskite manganites are suitable candidates as working substance in magnetie refrigeration technology. 相似文献
5.
6.
用固相反应法将Ag引入La0.7Ca0.3MnO3颗粒表面,形成(1-x)La0.7Ca0.3MnO3/xAg(x=0.00,0.10,0.20,0.25,0.30,0.35)。通过XRD谱、扫描电子显微镜(SEM)照片及SEM能谱(EDS)、ρ-T曲线、ρ-T拟合曲线、MR-T曲线,研究电输运性质及MR温度稳定性。结果表明:随复Ag量增大,电阻率急剧下降,高复Ag(x≥0.3)的电阻率比低复Ag(x≤0.10)的电阻率下降2个数量级;发现x=0.00,0.10用ρ-T2公式拟合比较合理,是单磁子散射作用;x=0.20,0.25用ρ-T2.5公式拟合比较合理,是自旋波散射作用;x=0.30,0.35,分别在97,93 K以上用ρ-T4.5公式拟合比较合理,说明是电子-磁子散射作用;所有复Ag样品,在250~20 K温区MR表现出很好的温度稳性,特别是x=0.10的样品,在220~150 K温区MR保持(13.8±0.2)%。提出磁电阻稳定性的机制:Ag与钙钛矿颗粒形成电输运二元通道,钙钛矿颗粒通道产生的低场磁电阻与Ag通道产生的正常磁电阻共同作用,产生MR温度稳定性。 相似文献
7.
8.
9.
通过电阻率-温度(temperature dependence of resistivity,ρ-T)曲线、磁化强度-温度(temperature dependence of magnetization ,M-T)曲线、ESR谱线的测量,研究了La0.45Ca0.55MnO3样品的电磁特性.结果表明,样品在整个测量温区呈现绝缘体行为,输运机制满足可变程跃迁模型.样品存在电荷有序(charge ordering,CO)相,相变温度TCO≈240K,并随温度降低发生顺磁(paramagnetism,PM)→电荷有序(CO)→反铁磁(antiferromagnetism,AFM)变化.值得注意的是,由于样品低温下存在多种复杂的磁相互作用,在40K发生自旋玻璃转变,表现为再入型自旋玻璃行为. 相似文献
10.
采用固相反应法制备了样品La0.67Sr0.33-xNaxMnO3(x=0.05,0.10,0.15,0.20,0.25,0.33)。通过实验测出了样品的X射线衍射谱图、M-T曲线、p-T曲线和MR-T曲线,研究了Sr位掺Na对La0.67Sr0.33MnO3的晶格结构和磁电特性的影响。结果表明,样品呈菱面体结构,当x≥0.20时,Mn^3+/Mn^4+〈1,体系在反铁磁态,但实验中所有样品表现为顺磁-铁磁相变伴随绝缘体.金属相变;随X增加,巨磁电阻MR增大,Tc降低,当x=0.33时,在室温区获得了很大的磁电阻MR=241%。 相似文献