排序方式: 共有11条查询结果,搜索用时 15 毫秒
1.
2.
Amorphous Er2O3 films have been fabricated on p-type Si(001) substrates using radio frequency magnetron sputtering technique. Vacuum ultraviolet spectra were employed to investigate the samples. An optical gap of 6.17 eV for Er2O3 films was obtained from the ab-sorption coefficient spectra. A possible reason was put forward to explain the inconsistent results about the band gap of Er2O3 in literatures. Emission spectra exhibited a strong emission band at 494 nm with the incident ultraviolet light of 249 nm. The observed high density of emission bands of Er2O3 films in the visible wavelength indicated that Er2O3 films could be used in Si solar cells for increasing conversion efficiency. 相似文献
3.
用磁控溅射的方法在透明导电氧化物衬底上制备了CdS薄膜,制备时的衬底温度为30~200℃.X射线衍射测试结果表明在这一条件下制备的CdS薄膜是六角纤锌矿的多晶结构.扫描电子显微镜结果显示薄膜具有较好的晶体质量,这一结论也和拉曼光谱、紫外-可见吸收光谱、光致发光光谱的结果一致.拉曼光谱显示CdS薄膜内部的压应力随着制备温度的提高而增大. 相似文献
4.
5.
6.
采用HSE杂化势计算了Cd1-xZnxTe合金的性质,并获得了较传统GGA更为准确的光学带隙和形成焓.在构建超胞计算合金体系时,采用SQS模型.计算分析得出Cd1-xZnxTe合金的光学带隙下凹参数为0.266 eV,这与已报道实验结果0.254 eV非常吻合.同时,计算得出的形成焓较高,特别是在Cd0.5 Zn0.5 Te合金组分时(25.60 meV/atom).对合金中键长的分析后得出Cd-Te键和Zn-Te键的局域键长与CdTe和ZnTe体材料的值非常接近,但二者之间相差较大,从而导致合金材料中各个原子存在较大的弛豫,这也是该合金具有较大形成焓的主要原因. 相似文献
7.
Er2O3-Al2O3 film was deposited on the Si(001) substrate by radio frequency magnetron technique at room temperature.The samplewas annealed at 450,600 and 750 oC for 30 min in O2 ambience,respectively.The optical constants were studied by spectroscopic ellipsometryfor both the as-deposited and the annealed samples.The proper values of refractive index indicated that it could be a useful material for solar cells. 相似文献
8.
9.
采用大功率高重复频率准分子激光溅射热解石墨靶制备了类金刚石膜,研究了激光功率密度和重复频率对类金刚石膜的结构及场发射性能的影响.保持重复频率不变,提高激光功率密度可提高膜中sp3键碳的含量和膜的场发射性能;在最佳激光功率密度下,当重复频率由200 Hz提高到500 Hz,膜中sp3键碳的含量和膜的场发射性能先提高,后降低,在300 Hz时达到最佳.在300 Hz重复频率、1010W/cm2激光功率密度下.膜的发射阈值电场为26 V/μm,在34 V/μm的电场下测得电流密度为14μA/cm2.根据类金刚石膜的场发射机理对上述结果进行了分析解释. 相似文献
10.
采用微波等离子体化学气相沉积(MPCVD)方法制备了100μm米厚高质量(100)定向金刚石薄膜. 利用(100)定向金刚石薄膜成功制备了α粒子探测器, -100V偏压下电荷平均收集效率为37.7%, 最大的电荷收集效率达到60%以上. 在此基础上, 通过在α粒子探测器条状电极面蒸镀一层合适厚度的硼(10B)膜转化层, 成功研制了金刚石中子探测器. 镀硼之后探测器对中子有明显的响应, 在1V/μm电场下, 对252Cf中子的能量分辨率达到9.3%,探测效率达到1.67%. 同时还研究了电场强度和硼(10B)层厚度对器件探测效率的影响规律. 在厚度<1.5μm时, 随着厚度的增加, 探测效率上升, 当厚度>1.5μm时, 探测效率下降. 相似文献