植酸对镁合金微弧氧化膜性能影响

在18g／L的碱性硅酸钠溶液中，加入7．5gm的环保无毒植酸，研究它对镁合金氧化膜表面形貌、成分、颜色、厚度以及耐蚀性影响。加入植酸后，氧化膜孔的直径范围由1～5μm增加到1～8μm，但氧化膜表面单位面积孔的个数由0.05个／μm^2减少到0．02个／μm^2。植酸参与氧化膜的形成过程，并使氧化膜颜色随着植酸加入量的增加逐渐加深。植酸使氧化膜的厚度由11gm增加到16μm。浸泡实验表明，植酸可进一步提高氧化膜耐蚀性，产生第一个腐蚀点时间由24h延长到50h。     

电解质对镁合金阳极氧化膜性能影响的研究进展

综述了电解质对氧化膜性能影响，为设计、选用阳极氧化工艺提供参考。随着人类环保意识的增强，未来镁合金阳极氧化电解质研究重点在于开发更多、对环境和人类友好且能较大提高氧化膜耐蚀性的物质。     

Deposition of photocatalytic TiO2 and N-doped TiO2 films by arc ion plating

TiO2 and N-doped TiO2 films were deposited on the glass substrates by arc ion plating method. The results show that the deposition rate does not change with the increasing deposition time. The increase of mass flow rate of N2 gives rise to the increase of deposition rate. All as-deposited TiO2 and N-doped TiO2 films are amorphous. The anatase TiO2 phase with preferred orientation （101） is acquired by post-annealing at 400 ℃ for 2 h. The incorporation of N into the TiO2 films and the heat treatment extensively shift the band edge to the visible light region.     

基体对镁合金氧化膜性能影响的研究进展

阐述了镁合金应用前景,介绍了阳极氧化特点以及影响氧化膜性能的因素,主要包括基体材料、电参数、电解液的组成及其浓度等.全面综述了基体对镁合金氧化膜成膜过程、成分、表面形貌以及耐蚀性的影响,提出了由于工业上使用的材料绝大多数为镁合金而不是纯镁,因此,开展合金元素对氧化膜性能影响的研究非常必要.     

Oxidation resistance of （Ti,Al,Cr）N coatings at 800℃

The composite metastable （Ti0.5Al0.5）N, （Ti0.45Al0.45Cr0.1）N and （Ti0.35Al0.35Cr0.3）N coatings were respectively deposited on a wrought martensite steel 1Crl 1 Ni2W2MoV for aero-engine compressor blades by arc ion plating technique with pulse substrate bias. All the coatings have B1NaCl phase with a （200） preferred orientation and dense structures. The results show that the introduction of Cr into （Ti,Al）N gives rise to a minute shrinkage of crystal lattice. The incorporation of chromium into the coatings dramastically improves the oxidation-resistance of the coatings. For （Ti0.5Al0.5）N, a layered oxide scale forms after 100 h oxidation and the outer layer is the blend oxide of TiO2 and Al2O3, and the middle layer is rich in AI and the inner layer is rich in Ti. For （Ti0.45Al0.45Cr0.1）N, the oxide scale possesses a double-layered structure and the outer layer is rich in Ti. For （Ti0.35Al0.35Cr0.3）N, a Cr-rich compound oxide scale of Ti, AI and Cr forms, and a out-diffusion of Fe from steel to the nitride coating and oxide film during the oxidation takes place.     

电解质对镁合金阳极氧化膜性能影响的研究进展

综述了电解质对氧化膜性能影响,为设计、选用阳极氧化工艺提供参考.随着人类环保意识的增强,未来镁合金阳极氧化电解质研究重点在于开发更多、对环境和人类友好且能较大提高氧化膜耐蚀性的物质.