排序方式: 共有31条查询结果,搜索用时 0 毫秒
1.
提高PET/PHB的无规性是近年来人们很关心的问题,因为它涉及到如何进一步提高 PET/PHB 的性能,我们以前的研究结果表明用 PET 齐聚物为原料制备的TPA/EG/PHB 三元液晶共聚酯比 PET/PHB 具有更高的无规性。本文进一步研究了TPA/EG/PHB 的液晶行为,并与 PET/PHB 进行了对比。 相似文献
2.
由对苯二甲酰氯(TPC)和二甲基联苯胺(DMBD)和双酚A(BPA)合成了三元无规全芳聚酯酰胺(PEA)。用DSC、X光衍射分析和偏光显微镜等手段表征了该类聚合物的热致液晶性质,确认了不同单体的比例的PEA均为热致向列型液晶聚合物,且不出现液晶相转变温度直至聚合物分解。由于PEA中聚酰胺链段之间的氢键作用,PEA为熔融温度随DMBD的比例增加而升高,即使DMBD链单元为20%(mol)的PEA,其 相似文献
3.
Fluorescent microspheres of polystyrene-based Eu(Ⅲ) complexes were prepared from TentaGel resin,2,6-bisbenzimidazolylpyri-dine and europium nitrate. The microspheres were characterized by FTIR spectroscopy, elemental analysis, XPS measurements and fluores-cence spectroscopy. Characteristic red emission under irradiation of365nm light from a hand-held UV lamp was observed for the micro-spheres either in a solution or solid-state.Fluorescent quenching was observed when the microspheres were exposed to a trace amount of di-ethyl chlorophosphate (DCP)in the dispersion. The material and property can be potentially used to fabricate chemosensor in the detection of organophosphates. 相似文献
4.
3,4-乙撑二氧噻吩的原位化学氧化受限聚合动力学研究 总被引:1,自引:0,他引:1
利用紫外-可见光谱,分别研究了3,4-乙撑二氧噻吩在45、65和85℃条件下的原位化学氧化受限聚合动力学规律。结果表明,温度的升高可以非常显著地加快单体的聚合速度,反应体系在45、65和85℃下完成聚合反应的时间分别为600、240和8min。温度对聚合反应的进程也有较显著的影响,在相对较低温度下(45和65℃),反应进程基本相同,都有比较明显的3个阶段(反应开始、稳定反应和反应终了阶段),而在相对较高温度下(85℃),反应进程则更简单,只有快速反应阶段和反应终了阶段。这些动力学数据可以为3,4-乙撑二氧噻吩在某些应用领域如固体电容器制备工艺中确定聚合温度和时间等工艺条件提供参考依据。 相似文献
5.
季铵盐型抗菌纤维素纤维的辐射接枝聚合 总被引:3,自引:1,他引:2
固相表面接触抗菌材料应用于水的表面接触消毒是一项新的水处理技术,提高材料表面抗菌基团含量将有利于抗菌性能的提高。本研究采用直接辐射接枝和预辐射接枝两种方法,在纤维素纤维表面引入具有抗菌功能的季铵盐聚合物,详细探讨了两种辐射接枝聚合技术以及温度、时间、单体浓度、辐射剂量等具体辐射接枝聚合工艺参数对接枝聚合反应的影响。利用红外光谱(FTIR)、扫描电子显微镜(SEM)对接枝纤维素纤维进行了表征。结果表明,采用预辐射接枝技术可制得接枝率55%以上的高接枝率抗菌纤维素纤维。 相似文献
6.
7.
8.
9.
烷氧基对聚对苯撑发光性能的影响EI 总被引:4,自引:0,他引:4
:采用 Scholl反应 ,以硝基苯作溶剂 ,无水三氯化铁为催化剂 ,合成了系列可溶性烷氧基对称二取代的聚对苯撑 (DAO- PPP) ,并用多种手段对其结构进行了表征 ,研究了聚合物的光致发光性能。实验表明 ,烷氧基的引入不但明显改善了 PPP的溶解加工性能 ,而且随烷氧基侧链链长的改变 ,聚合物的最大紫外吸收峰、带隙 Eg、光致发光(PL)最大发射峰及其发射强度都呈现规律性的变化 。 相似文献
10.