AuGe和AuGeNi/n-GaAs欧姆接触的透射电镜观察

用断面透射电镜技术,直接观察了实际欧姆接触工艺中AuGe/GaAs和AuGeNi/GaAs的横断面组织,并用选区电子衍射方法测定其反应产物。     

碲化铅镀膜材料中的微缺陷

碲化铅镀膜材料中的微缺陷王葛亚，施天生，张素英（中国科学院上海冶金研究所，上海２０００５０）（中国科学院上海技术物理所，上海２０００８３）化合物半导体材料碲化铅（ＰｂＴｅ）已广泛用作波长大于３．８μｍ范围高折射率膜层材料。１９７７年严义埙等人采用富Ｔ...     

快淬Nd—Fe—B粘结磁体矫顽力机制

本文采用x光衍射、透射M(?)ssbauer谱和高分辨电镜,研究了快淬Nd_(13.5)Fe_(81.74)B_(4.76)合金的显微组织。快淬线速度为24 m/sec的粘结磁体性能最佳,作者发现,快淬Nd_(13.5)Fe_(81.74)B_(4.76)合金带的显微组织为单纯的Nd_2Fe_(14)B相微晶,不存在第二相(富Nd相、富B相或α-Fe相)。本合金粘结磁体的高内禀矫顽力(iHc≥14kOe)来源于Nd_2Fe_(14)B相的单畴机制。     

Coercivity Mechanism of Melt-spun Nd-Fe-B Bonded Magnet

The microstructures of melt-spun Nd_135-Fe_81.74B4.76 ribbons have been investigated bymeans of X-ray diffraction,Mossbauerspectroscopy and HREM.Experimental resultsshow that optimal magnetic properties of the bond-ed magnet can be obtained by melt-spun alloys atwheel velocity of 24m/s,the microstructure ofwhich was single phase Nd_2Fe_(14)B crystallites,andno other phases,such as Nd-rich,B-rich or x-Fephase,were present.It is considered that the highintrinsic coercivity ~iH_c can be attributed to the sin-gle-domain behaviour of Nd_2Fe_(14)B crystallitephase.     

快淬Nd—Fe—B永磁材料的透射电镜研究

用透射电子显微术研究了Nd_(13.5)Fe_(81.74)B_(4.76)快淬永磁材料结构与磁性的关系。从高分辨TEM象和电子衍射分析中证实该材料是单相的多晶Nd_2Fe_(14)B组织。冷速V=24m/s时,晶粒度～100nm,晶内完整无缺陷,晶界无第二相或无定形层。材料的高矫顽力应来源于完整而细小的Nd_2Fe_(14)B晶粒结构。     

NdFeB永磁材料氧化行为的研究SCIEI

用透射电镜、Auger能谱,X射线和Mossbauer等方法研究了烧结NdFeB永磁材料在90℃潮湿空气中的氧化行为。结果表明,黑色氧化组织先在富Nd晶界相处形成。沿晶界深入和扩展进入基体相Nd_2Fe_(14)B晶粒,形成表面氧化层。黑色组织内富O和Nd而贫Fe。经500h氧化后,粉末组成仍以Nd_2Fe_(14)B粒子为主,余为Fe_3O_4,Nd_2O_3和少量a-Fe_2O_3,立方Fe_2O_3。经氧化的Nd_2Fe_(14)B相四方晶格内Fe原子分布发生变化,c晶位Fe原子大部分逸失,这是氧化导致材料磁化强度降低的重要原因。     

高JcMTG-YBCO的透射电镜分析

在高磁场下,块样YBa_2Cu_3O_7的临界电流密度Jc值的高低是该材料能否实际应用的关键问题。融熔织构法(MTG)明显提高Jc达10~4～10~5A/cm~2(77K,2T)。因此搞清楚材料的微结构与Jc的关系,探索改善Jc的方法是很有意义的。