With CALPHAD(calculation of phase diagrams) method, calculated with Scheil--Gulliver model in the Thermo-calc software the solidification paths of several Al-rich Al-Mg-Er alloys were And the amounts of several phases formed during solidification were also calculated. Synchronously, the heat-treatment temperatures of the same alloys were predicted by thermodynamic calculation. The calculated results show that by adding 0.4%Er (mass fraction), the strength effect of Er in Al-Mg alloy is better. This result is in agreement with the experimental investigations. 相似文献
2.
热镀锌烘烤硬化钢板合金化退火过程中镀层表面合金相形成过程的研究 总被引:1,自引:0,他引:1
对热镀锌烘烤硬化钢板进行了合金化处理, 用扫描电镜观察合金化镀层表面的组织形貌, 并用X射线衍射仪分析了镀锌层的表面相组成, 对所研究的结果用相图计算进行了解释。研究表明, 450 ℃时在合金化退火开始时间段镀层为η相, 20 s左右部分ζ相长至镀层表面, 30 s后表面主要为ζ相, 随着退火时间的延长到300 s镀层大部分为δ相, 不再发生相变, 合金化结束; 500 ℃时合金化过程基本与450 ℃一致, 但退火3 s后表面就已出现少量的ζ相, 而9 s后表面基本由δ相和ζ相混合组成, 退火时间达到20 s后表面已完全为δ相; 550 ℃时退化3 s后表面出现少量的δ相, 到9 s后镀层几乎全部由δ相组成。 相似文献
3.
通过对试样微观组织及力学性能进行实验,研究了在线退火温度对TiNi合金丝材组织和性能的影响。实验表明,TiNi合金丝材经过(750~830℃)×2.3min在线退火处理后,丝材抗拉强度均大于960MPa,屈服强度均大于460MPa,延伸率均大于24.5%,断面收缩率均达到25%以上,830℃×2.3min在线退火处理后延伸率和断面收缩率最高,分别为54.5%和64.0%;说明经过830℃×2.3min在线退火处理后丝材塑性得到改善,达到最优。随着在线退火温度的升高,丝材的显微硬度逐渐降低。由微观组织可以看出,830℃×2.3min在线退火处理后丝材晶粒得到了细化。 相似文献
4.
借助金相显微镜、拉伸实验和弯曲回复法等手段研究了近等原子比钛镍形状记忆合金氩弧焊接接头的组织和性能。研究结果表明,近等原子比钛镍形状记忆合金氩弧焊接接头的显微组织可分为三个区,分别是粗大柱状晶区、细小柱状晶区和热影响区。由于焊接接头显微组织与母材之间的差别,在相同的应变下,近等原子比钛镍形状记忆合金氩弧焊接接头的回复温度明显高于母材,记忆性能变差。焊接后的近等原子比钛镍形状记忆合金的屈服强度与母材相近,但抗拉强度和延伸率远低于母材。氩弧焊接近等原子比钛镍合金的显微组织在热处理后不会发生明显变化,经过形变后,焊接接头的回复温度与母材仍有差别,显微组织的不同是造成这一现象的原因之一。 相似文献
5.
6.
研究了大气退火、真空退火和在线氩气保护退火三种热处理方式对Ti-4A1-22V钛合金丝材组织及性能的影响。结果表明,大气退火形成均匀的β相组织,塑性较好;真空退火采用炉冷,冷速慢导致β相时效,塑性急剧降低;真空退火采用氩气冷却,β相晶粒较大,塑性较低;在线氩气保护退火,β晶粒均匀细小,塑性高,固溶处理效果最好。 相似文献