以ZIF-8及La掺杂ZIF-8为前驱体,经高温煅烧制备ZnO及La掺杂ZnO纳米颗粒.研究了La掺杂对ZnO纳米颗粒的形貌、晶体结构及气敏性能的影响.利用X射线衍射仪、扫描电子显微镜对材料的微结构进行表征,结果表明:La掺杂有利于获得更小粒径的类球形纳米结构,但La掺杂未改变ZIF-8及衍生ZnO纳米结构的晶体结构.... 相似文献
3.
Clarification of the oxygen adsorption properties of YBaCo_4O_7 at high temperature by thermogravimetry 总被引:1,自引:0,他引:1
The oxygen adsorption/desorption properties of YBaCo4O7 at high temperature were investigated by thermogravimetry(TG) method,in which two types of oxygen adsorption were combined.The first type adsorbed oxygen at about 700 °C and released the adsorbed oxygen at 880 °C.After the first type oxygen desorption,even the temperature and oxygen flow were kept the same,a second type oxygen adsorption at about 880 °C occurred and the adsorbed oxygen were released at above 980 °C.The combination of these two types of oxygen adsorption/desorption was responsible for the difference in TG curves obtained by different heating programs. 相似文献
4.
采用脉冲激光沉积技术,在以c轴取向ZnO作为缓冲层的金刚石/硅基底上制备出了结晶良好的高c轴取向LiNbO3薄膜。利用X射线衍射对薄膜的结晶质量和c轴取向性进行了研究,结果表明制得的LiNbO3薄膜具有高度c轴取向且结晶质量良好。采用扫描电子显微镜和原子力显微镜对薄膜的表面形貌进行了分析,发现薄膜表面光滑,晶粒尺寸均匀,薄膜表面粗糙度约为20nm。 相似文献
5.
6.
7.
用固相反应法制备了RBaCo2O5+δ(R=Y、Dy、Gd、Pr、Nd、Sm和Eu)系列陶瓷.用标准四探针法测量了它们从室温到600℃之间的电阻率变化.在温度较低时,它们的电阻率都随着温度的升高而减小,显示为半导体特征.当电阻率在某一温度达到最大值后,电阻率开始随着温度升高而缓慢增加,显示为半金属特征.进一步研究了RBaCo2O5+δ系列陶瓷在高温恒温时的电阻率随着环境气氛的变化情况.结果表明RBaCo2O5+δ陶瓷是一类潜在的氧阻传感器材料,并且它们的响应速率从快到慢顺序是YBaCo2O5+δ>DyBaCo2O5+δ>GdBaCo2O5+δ>PrBaCo2O5+δ>NdBaCo2O5+δ>SmBaCo2O5+δ>EuBaCo2O5+δ.以YBaCo2O5+δ陶瓷为例,在700℃恒温时,当从氧气氛切换到氮气氛时,由于晶格中氧的脱附导致电阻率先是快速上升,然后缓慢上升,并在90 s内达到最大平衡值.反之,当从氮气氛切换为氧气氛时,由于氧的吸附,电阻率迅速降低,约30 s内达到最小平衡值. 相似文献
8.
9.
10.
YBaCo4O7是一种具有奇特氧吸附行为的材料,它在300℃左右的较低温度时就可以吸附其自身质量3%的氧,并且所吸附的氧在400℃可以快速脱附,同时具有稳定的循环特性,是一种非常有潜力的氧分离材料。介绍了YBaCo4O7的晶体结构及在外界温度变化时所产生的独特氧吸附/脱附特性;综述了晶格中不同位置的元素掺杂替代对其氧特性的影响;并对此类材料在透氧膜、脱氧纯化剂等方面的潜在应用进行了初步探索,最后总结了当前存在的一些问题并展望了可能的解决途径。 相似文献