研究了压铸镁合金AZ91D在去离子水和3.5%NaCl溶液中的腐蚀行为.采用失重法测定镁合金的腐蚀速率,扫描电子显微镜观察腐蚀后试样的表面形貌,分别测定其在去离子水和3.5%NaCl溶液中20℃和50℃下的开路电位及极化曲线.结果表明,随着温度的升高压铸镁合金的开路电位降低,耐蚀性能下降,相同温度下其在含有C1-溶液中的开路电位低于无Cl-溶液中的开路电位.在3.5%.NaCl溶液中,随着温度升高压铸镁合金的腐蚀电位明显负移,耐蚀性降低;AZ91D的腐蚀形貌以点蚀为主,腐蚀速率随时间的延长而降低. 相似文献
2.
3.
4.
5.
对比研究了普通白口铁、镍硬铸铁、高铬铸铁、硼白口铁的砂蚀磨损性,并从碳化物结构类型分析入手,探讨影响砂蚀磨损性的主要因素。试验结果表明:影响砂蚀磨损性的主要因素为电化学性能和硬度。 相似文献
6.
7.
Electroless nickel-plating on die cast magnesium alloy AZ91D was investigated. Growth of the electroless nickel-plating coating was characterized using scanning electron microscopy. Corrosion resistance of the coating was evaluated by open circuit potential and potentiodynamic polarization curves in 3.5% (mass fraction) NaC1 solution. The results show that plating deposition is initiated on the crevices and then spread onto primary a phase. The corrosion potentials for die cast magnesium alloy AZ91D and nickel-plating coating are about -1.45 V and -0.36 V (vs. SCE), respectively. No discoloration, cracks, blisters, or peeling appear by heat-quench test. The results show that the corrosion potential of Ni-P coating is increased by 1 000 mV and corrosion resistance for die cast magnesium alloy AZ91D is improved. The adhesion between the coating and the substrate is excellent. Electroless nickel plating is a promising method to enhance magnesium alloys resistance for attacking. 相似文献
8.
机械合金化制备Ti3AlC2陶瓷材料的研究 总被引:1,自引:0,他引:1
采用Ti,Al和C元素粉末为反应物原料,通过机械合金化法成功地制备出高含量三元碳化合物Ti3AlC2陶瓷粉体.按Ti3AlC2化学计量比为起始反应原料配比(Ti∶Al∶C=3∶1∶2)的元素混合粉末,经3 h的机械合金化后,Ti、Al和C单质混合粉末发生化学反应,生成以Ti3AlC2为主晶相,并含有少量TiC的混合粉体和小块体;粉体中Ti3AlC2的含量达到83%(质量分数,下同).产物合成的原因是在Ti-Al-C体系中发生了一种机械诱发自蔓延反应. 相似文献
9.
10.
机械合金化合成Ti_3SiC_2导电陶瓷的形貌特征研究 总被引:1,自引:0,他引:1
以Ti、Si、C单质为原料,添加微量的Al为助剂,采用高能球磨的方法合成了以Ti3SiC2为主相、含有一定量的TiC等杂质的混合粉体.球磨8h后,得到了相对纯度较高的Ti3SiC2粉体;同时,在粉体中发现了直径为0.5~1cm扁平的坚硬块体.采用XRD和SEM分析了混合粉体和小块体中Ti3SiC2等组成相的形貌特征.通过分析在不同时间内制备的粉体Ti3SiC2的成分变化和块体断口形貌,发现了Ti3SiC2的块体产物断口表面具有"鸟巢状结构"特征,并对具有该特征的Ti3SiC2块状产物的生成过程进行了讨论. 相似文献