This paper explores the linkage between the entrepreneurial orientation of established firms and the development of radical innovation. Through five case studies in firms involved in radical innovation, three propositions are developed, suggesting that proactiveness, risk‐taking and autonomy stimulate the development of radical innovation, whereas competitive aggressiveness does not necessarily do so, as radical innovations are directed towards the creation of entirely new arenas of business, where existing competitors are not present.     

Impact Fracture of Thermally Tempered Glass Helicopter Windshields

In-service fracture of helicopter windshields was studied. Simulated catastrophic fracture tests were conducted by firing alumina and steel spheres onto stationary tempered and as-received glass panels. The results were studied by Hertzian analysis and modified Auerbach's relations. Thermally tempered glass shows much higher impact resistance than that estimated from superposition of residual stresses. Subcritical impact sites exhibit slow crack growth in tempered plates, eventually leading to fracture of the entire plate.     

Modeling tool wear in end-milling using enhanced GMDH learning networks

This paper presents an enhanced approach to predictive modeling for determining tool-wear in end-milling operations based on enhanced-group method of data handling (e-GMDH). Using milling input parameters (speed, feed, and depth-of-cut) and response (tool wear), the data for the model is partitioned into training and testing datasets, and the training dataset is used to realize a predictive model that is a function of the input parameters and the coefficients determined. In our approach, we first present a methodology for modeling, and then develop predictive model(s) of the problem being solved in the form of second-order equations based on the input data and coefficients realized. This approach leads to some generalization because it becomes possible to predict not only the test data obtained during experimentation, but other test data outside the experimental results can also be used. Moreover, this approach makes it easy to present the realized solution in a form that can be further optimized for the input parameters using some optimization techniques. The results realized using our e-GMDH method are promising, and the comparative study presented shows that the e-GMDH outperforms polynomial neural network (PNN); moreover, it is more flexible than the conventional GMDH, which tends to produce nonlinear solutions even for simple problems. In the investigation, the extended particle swarm optimization (PSO) technique was applied to obtain the optimal parameters. Consequently, the modeling approach is extremely useful in realizing a computer-aided process-planning system in an advanced manufacturing environment.     

A Web-based Kanban system for job dispatching, tracking, and performance monitoring

A Kanban system facilitates lean principles in a simple and effective way. While reportedly successful in many manufacturing firms, the conventional Kanban systems using physical cards suffer from human errors, limited tracking capability, and so on. To make the information flow leaner, software providers add new features to their existing programs for manufacturing systems to computerize Kanban activities. As Web-based technologies advance rapidly, developing an entirely Web-based Kanban system appears to be feasible and promising. This paper presents the advantages, limitations, and challenges of Web-based Kanban systems. An experimental program has been developed based on PHP+MySQL, a popular Web programming platform. The server-executed program features cross-platform compatibility, real-time tracking and performance monitoring, and greatly enhanced information contents compared to physical Kanbans. Human errors are minimized by the automated transactions; nevertheless, the interfacing and data maintenance require further research efforts.     

Simultaneous sulfide and acetate oxidation under denitrifying conditions using an inverse fluidized bed reactor

BACKGROUND: Simultaneous removal of sulfur, nitrogen and carbon compounds from wastewaters is a commercially important biological process. The objective was to evaluate the influence of the CH₃COO^?/NO₃^? molar ratio on the sulfide oxidation process using an inverse fluidized bed reactor (IFBR). RESULTS: Three molar ratios of CH₃COO^?/NO₃^? (0.85, 0.72 and 0.62) with a constant S^2?/NO₃^? molar ratio of 0.13 were evaluated. At a CH₃COO^?/NO₃^? molar ratio of 0.85, the nitrate, acetate and sulfide removal efficiencies were approximately 100%. The N₂ yield (g N₂ g^?1 NO₃^?‐N consumed) was 0.81. Acetate was mineralized, resulting in a yield of 0.65 g inorganic‐C g^?1 CH₃COO^?‐C consumed. Sulfide was partially oxidized to S⁰, and 71% of the S^2? consumed was recovered as elemental sulfur by a settler installed in the IFBR. At a CH₃COO^?/NO₃^? molar ratio of 0.72, the efficiencies of nitrate, acetate and sulfide consumption were of 100%, with N₂ and inorganic‐C yields of 0.84 and 0.69, respectively. The sulfide was recovered as sulfate instead of S⁰, with a yield of 0.92 g SO₄^2?‐S g^?1 S^2? consumed. CONCLUSIONS: The CH₃COO^?/NO₃^? molar ratio was shown to be an important parameter that can be used to control the fate of sulfide oxidation to either S⁰ or sulfate. In this study, the potential of denitrification for the simultaneous removal of organic matter, sulfide and nitrate from wastewaters was demonstrated, obtaining CO₂, S⁰ and N₂ as the major end products. Copyright © 2008 Society of Chemical Industry     

The MiniWiD-Coater. III. Effect of Application Temperature on the Dissolution Profile of Sustained-Release Theophylline Pellets Coated with Eudragit Rs 30 D

Theophylline pellets were coated with Eudragit RS 30 D in a miniature fluid-bed pan coater called MiniWiD developed recently. The dispersions were plasticized with varying amounts of triethyl citrate (TEC), dibutyl phthalate (DBP), and polyethylene glycol 6000 (PEG) and applied at different temperatures ranging from 25 to 45 °C. Theophylline release was tested by dissolution using the USP Apparatus 2 (paddle) in 0.1 N hydrochloric acid under sink conditions over 6 hours.

At a coating level of 4 % (0.7 mg/cm²) sustained-release profiles were obtained from dispersions plasticized with TEC or DBP. By reducing the amount of plasticizer from 20 to 10%, films with higher permeabilities were obtained. This effect was compensated by tempering the pellets at 50 deg;C for 24 hours. The coating temperature had little effect on the dissolution profiles of TEC-plasticized films and no effect on films with DBP.

Coatings plasticized with 20% PEG were applied at temperatures ranging from 25 to 45 °C. These films required a coating level of about 18 % (3.3 mg/cm²) to provide comparable sustained-release properties. In contrast to DBP and TEC, a strong influence of the coating temperature on the release rates was observed in which higher temperatures led to slower release rates. This behavior can be explained by the minimum film-forming temperature (MFT). Since PEG does not lower the MFT of Eudragit RS 30 D, the application of these films below the MFT of 45 °C is associated with a lower degree of film formation.     

Analysis of the effect of shrinkage on macrosegregation in alloy solidification

Numerical calculations based on a continuum model are used to examine the effects of solidification shrinkage on the redistribution of solute in a Pb-19.2 pct Sn mixture which is convectively cooled at a sidewall. For each of three different cooling rates, separate calculations are performed for shrinkage and buoyancy-induced flows, as well as for the combined influence of shrinkage and buoyancy effects. The calculations reveal that flow and macrosegregation patterns are more strongly influenced by buoyancy effects over a wide range of solidification rates. Although extremely large solidification rates yield small regions near the chilled wall in which shrinkage-induced flows control the redis-tribution of solute, the overall effect on macrosegregation is small relative to that associated with buoyancy. Scaling analysis of the governing equations produces reference shrinkage and buoyancy velocities which can be used to extend the current numerical results to other binary systems.