Microwave hybrid fast sintering of red clay ceramics

This work aimed to examine the performance of the hybrid sintering of clay ceramic in a microwave furnace, compared to the sintering process in a conventional furnace. The raw materials were subjected to X-ray fluorescence, loss on ignition (LOI), X-ray diffraction, particle size distribution, real specific mass, and thermogravimetric analyses. The red clay ceramic mass was prepared, extruded, pre-sintered in a conventional furnace at 600°C/60 min, and sintered at temperatures between 700 °C and 1100 °C. The sintering conventional (resistive oven) was carried out for 60 min with a heating rate of 10°C/min. In the microwave furnace, the sintering times were 5, 10, and 15 min, with a heating rate of 50°C/min, with a sintering chamber coated with silicon carbide (susceptor). The sintered specimens were characterized according to linear shrinkage, water absorption, apparent porosity, apparent specific mass, X-ray diffraction, Raman spectroscopy analysis, spectroscopy analysis in the ultraviolet and visible regions, microhardness, and scanning electron microscopy. The results showed that microwave sintering promoted an increase in the microhardness and apparent specific mass, and reduction in water absorption and apparent porosity values, due to greater densification in the microstructure. The best results occurred for specimens sintered at 1100°C.     

Radiation therapy of giant aggressive keratoacanthomas

BACKGROUND AND DESIGN: Giant aggressive keratoacanthoma is a rare destructive subset of keratoacanthoma that frequently involves the facial region, grows rapidly to a large size, and often recurs after surgical management. The effectiveness of ionizing radiation therapy was examined in a retrospective study involving 16 patients; 14 of the tumors had recurred after surgical therapy. RESULTS: All tumors resolved with satisfactory cosmetic results and without recurrence following a fractionated course of superficial radiation therapy. CONCLUSIONS: Radiation therapy is an effective therapeutic modality for giant aggressive keratoacanthomas.     

Induction of a Citrus gene highly homologous to plant and yeast thi genes involved in thiamine biosynthesis during natural and ethylene-induced fruit maturation

In response to a light pulse, hamsters normally generate phase advances that are positively correlated with the length of their circadian period (tau). To determine whether this is a general property of the phase-shifting oscillator, the present study looked for a correlation between tau and phase-advance size not only for photic but also for nonphotic shifts. Syrian hamsters, Mesocricetus auratus, were entrained to light-dark cycles with a periodicity of either 23.67 h (the short-T group) or 24.33 h (the long-T group); after release into constant darkness, the short-T and long-T groups exhibited short and long taus, respectively. These animals were then induced to run in a novel exercise wheel for 3 h, starting at circadian time (CT) 7, or were exposed to 20 min of light, starting at CT 19. The size of the ensuing phase advances did not differ between the short-T and long-T groups not only for the nonphotic stimulus but also for the photic one, an unexpected result for the photic stimulus. Within the short-T groups for photic and nonphotic stimuli, the shorter tau was, the larger the phase advances were, another unexpected relationship. Another experiment where phase delays were induced by light pulses at CT 15 also failed to yield significant differences between the short-T and long-T groups. Independently of their after-effects on tau, T cycles may influence the capacity of the pacemaker to phase shift in ways that are still unclear but at least similar for both photic and nonphotic shifts.     

Cavitation Damage of the single-crystal nickel-base superalloy SRR99 during creep at 850°C

Various heat treatments of the single-crystal nickel-base superalloy SRR99 have been carried out to produce a wide range of initial γ′ phase morphology. The cavitation damage has been studied after creep fracture at 850°C and stresses between 400MPa and 650 Mpa. The crep fracture surfaces and longitudinal sections of crept specimens have been examined by image analysing system in order to determine the size distribution and the area fraction of (001)-planes cracks on fracture surface characterise the creep crack damage level. The cracking morphology in fractured material as a function of stress and γ′-phase size has also been investigated. The results show, that crack propagation occurred anisotropically on (001) crystallographic planes perpendicular to the aplied stress along the γ/γ′ interfaces. It was found, that creep cracks dependent on the shape and size of γ′-phases developing at the temperature and stress level.     

Transmission Electron Microscopy and Electron Energy-Loss Spectroscopy Characterization of Glass Phase in Sol-Gel-Derived Mullite

Sol-gel-derived mullite ceramics were processed by pressureless sintering at 1600°, 1650°, and 1700°C for 4 h. Microstructural and microchemical characterization of the mullite materials was performed using transmission electron microscopy, in conjunction with energy-dispersive X-ray spectroscopy and electron energy-loss spectroscopy (EELS). Apart from mullite grain diameter and triplepocket size, no major microstructural changes were observed with increasing sintering temperature. Residual glass was present at triple pockets and along two-grain junctions. Not all grain boundaries revealed the presence of a continuous amorphous intergranular film. Clean interfaces were observed only at boundaries with one grain parallel to the [001] orientation (low-energy configuration). Quantitative EELS analysis of mullite grains and glass pockets revealed only small changes in composition with increasing sintering temperature; i.e., the alumina:silica ratio slightly increased for mullite and glass. The analysis implied that mullite with this relatively high aluminum content would not be stable adjacent to residual glass. However, a stable glass-mullite system has been proposed, because impurity cations were detected within glass pockets, which suggested a slight shift of the subsolidus line (glass-mullite/ mullite) to a higher amount of alumina. Energy-loss nearedge structure studies of the Si- L _2,3 edge revealed a similar near-edge structure for the mullite, residual glass, and quartz. Thus, SiO₄ tetrahedra were thought to be the main building units of the glass contained in sintered mullite.