Improved visible-light responsive photocatalytic activity of N and Si co-doped titanias

Thermal reaction of titanium tetraisopropoxide and tetraethyl orthosilicate in 1,4-butanediol afforded nanocrystalline silica-modified titanias having large surface area and superior thermal stability. In this study, the thus-obtained silica-modified titanias were treated in an NH₃ flow at high temperatures, and their physical and photocatalytic properties were investigated. Compared with NH₃-treated TiO₂ without silica modification, the NH₃-treated silica-modified titanias showed a stronger absorption in the visible region (400–500 nm) and had a larger peak at 396 eV in the N 1s XPS spectrum. These results indicate that a larger amount of nitrogen was stably doped in the silica-modified titania. The obtained products exhibited a high photocatalytic activity for degradation of Rhodamine B and decomposition of acetaldehyde under visible light irradiation. Electronic supplementary material The online version of this article (doi:) contains supplementary material, which is available to authorized users.     

Aging and availability of binocular disparity and pictorial depth cues in 3D graphics contents

Some stereoblind observers do not perceive depth of 3D stimuli that depends on binocular disparity. These individuals, who have no disabilities, comprise over 5% of the general population. In addition, 17–30% of nonstereoblind young and young–middle people do not use disparity information in certain 3D environments, a phenomenon known as pseudo‐stereoblindness. This study aimed to investigate the relationship between aging and the proportion of pseudo‐stereoblindness in the general population. In an experiment, 134 nonstereoblind participants, ranging in age from 17 to 83 years, judged subjective depth of 3D stimuli containing binocular disparity and pictorial depth cues. Results showed that the proportion of pseudo‐stereoblindness among young (17–24 years old) and young–middle aged observers (25–39 years old) was 29%, in both cases. However, the proportion of pseudo‐stereoblind observers increased in older populations: 65% and 82% in the middle (40–54 years old) and senior (55–83 years old) age groups, respectively. These results suggest that a number of people, especially in elderly populations, have trouble perceiving depth from binocular disparity in 3D graphic contents despite their essential ability to use disparity information.     

Fabrication of piezoelectric multilayer thin-film actuators

In this study, we fabricated multilayer ceramics (MLCs) composed of multilayered Pb(Zr,Ti)O₃ (PZT) piezoelectric thin films with internal electrodes and evaluated their dielectric and piezoelectric properties. The stack of PZT ferroelectric layers (550 nm) and SrRuO₃ (SRO, 80 nm) electrodes were alternatively deposited on Pt/Ti-coated silicon-on-insulator substrates by radio-frequency magnetron sputtering. The MLCs composed of one, three, and five PZT layers were fabricated by the alternate sputtering deposition of PZT ferroelectric layers and SRO electrodes through the movable shadow mask. The capacitances of MLCs were proportionally increased with the number of PZT layers, while their relative dielectric constants were almost same among the each MLC. The MLCs exhibited symmetric and saturated P–E hysteresis loops similar to the conventional PZT thin films. We estimated that the piezoelectric properties of MLCs by FEM simulation, and confirmed that the effective transverse piezoelectric coefficients (d _31,eff ) increased with the number of PZT layers. The piezoelectric coefficients calculated to be d _31,eff  = ?2964 pC/N at 25 PZT layers, which is much higher than those of conventional single-layer piezoelectric thin films.     

Sol–Gel‐Derived High‐Performance Stacked Transparent Conductive Oxide Thin Films

Single‐ and multi‐layer transparent conductive oxide (TCO) thin films exhibiting high performance, good packing density and low surface/interface roughness are deposited on silica glass substrates by the sol–gel method. The crystal and microstructural properties of the TCO thin films are evaluated as an alternate to films prepared by ultra‐high vacuum deposition. Tin‐doped indium oxide (ITO) thin films produced using a two‐step drying process showed low surface roughness because of dense packing structure not only horizontal but also vertical directions. As a result, electrical conductivity, carrier concentration, carrier mobility, and optical transmittance of 2.3 × 10³ S/cm, 8 × 10²⁰ cm^?3, 18 cm²/Vs, and over 98% at 500 nm, respectively, were achieved. A multilayer ZnO/ITO stacked structure was also fabricated using the sol–gel process. Our findings suggest that solution‐based methods show promise as an alternative to existing ultra‐high vacuum methods to fabricate TCO thin films.     

GPC Profile Change of Potato Starch with Extrusion Processing

Native potato starch (moisture content 15%) was treated by twin screw extruder under four operating conditions with varying barrel temperatures (110°C–230°C). These modified starch samples were compared to native and drum-dried starch. Starch sample solution for gel chromatography was prepared by the three methods (acidic, alkaline, and neutral methods). They were subjected to gel chromatography on Toyopearl HW-75, and some difference was found among the three gel chromatographic patterns obtained from the same starch solution. This discrepancy among GPC patterns suggests formation of some types of anhydro-bonds between chains of amylopectin and or amylose in the extrusion process. Elevating barrel temperature increases degree of depolymerization. The size of fragments formed with the treatment is bigger than that of oligosaccharides but smaller than that of amylose.