Investigation of the changes in physical properties of PES/PVC fabrics after aging

The aim of this work was to investigate the physical and mechanical performance of architectural polyester (PES)–poly(vinyl chloride) (PVC) membranes exposed to different artificial aging conditions. Two commercially available architectural membranes were chosen as research objects. The durability of the PES/PVC fabrics was evaluated by the loss in mechanical performance, scanning electron microscopy, and X-ray diffraction analysis in order to understand the effect of the degradation agents on the surface of the membranes. The mechanical performance of the PES/PVC membranes was unchanged. Scanning electron microscopy images of the tested materials showed initial cracks after aging. The X-ray fluorescence analysis showed that at the time of aging, the amount of Cl and Si decreased slightly, while Ti decreased by half, and Ca by volume increased twice. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47523.     

Synthesis of Long-Chain β-Lactones and Their Antibacterial Activities against Pathogenic Mycobacteria

In the quest for new antibacterial agents, a series of novel long- and medium-chain mono- and disubstituted β-lactones was developed. Their activity against three pathogenic mycobacteria—M. abscessus, M. marinum, and M. tuberculosis—was assessed by the resazurin microtiter assay (REMA). Among the 16 β-lactones synthesized, only 3-hexadecyloxetan-2-one (VM005) exhibited promising activity against M. abscessus, whereas most of the β-lactones showed interesting activities against M. marinum, similar to that of the classical antibiotic, isoniazid. Regarding M. tuberculosis, six compounds were found to be active against this mycobacterium, with β-lactone VM008 [trans-(Z)-3-(hexadec-7-en-1-yl)-4-propyloxetan-2-one] being the best growth inhibitor. The promising antibacterial activities of the best compounds in this series suggest that these molecules may serve as leads for the development of much more efficient antimycobacterial agents.     

Evaluation of the effect of processing on cocoa polyphenols: antiradical activity,anthocyanins and procyanidins profiling from raw beans to chocolate

The content and composition of anthocyanins and procyanidins in fermented cocoa beans (from different geographic origins: Ecuador, Cameroon, Ivory Coast, Ghana and Nigeria), roasted nibs, cocoa mass and chocolate were determined, beside the determination of the total antiradical capacity. Concerning geographic origin, cocoa beans and processed products from Ecuador showed the highest levels of anthocyanins, followed by Nigeria and Cameroon. Generally, as cocoa beans were further processed, the levels of anthocyanins and flavan‐3‐ols decreased. The largest observed losses of phenolics occurred during roasting. A progressive decreasing trend in polyphenol concentration was observed in the other processed samples as well. Despite the original content of polyphenols in raw cocoa beans, technological processes imply a significant impact on cocoa quality, confirming the need of specific optimisation to obtain high value chocolate.     

X-ray electron spectroscopic investigation of the structure of double lead silicate glasses

The method of x-ray electron spectroscopy is used to investigate lead silicatexPbO(1 -x) · SiO₂ (x - 0.3, 0.4, 0.5, 0.55, 0.667) glasses. The concentration dependences of the spectra of inner Pb4f, Si2p, and Ols levels led to the conclusion that for low contents of PbO, lead is present in the glass in the form of modifying ions, whereas in high concentrations, it plays the role of glass former. Restructuring in the glass occurs for about 50% molar concentration of PbO. The Pb - O bond in the glass is more ionic than in PbO. With an increase in the PbO content in the glass, the Pb - O bond becomes closer to that of lead monoxide, i.e., is more covalent.     

The new intra-urban dynamics: Suburbanisation and functional specialisation in French cities

This article examines the relationships between the employment suburbanisation from central cities towards their suburbs, and the process of intra-urban specialisation that occurred simultaneously in the fifty largest French metropolitan areas. A methodology is proposed to identify urban subcentres and to analyse the effects of the intra-urban specialisations on suburbanisation patterns. We conclude that the specialisation of both subcentres and central cities has a significant effect on suburbanisation rates. Lastly, an intra-metropolitan shift/share analysis provides additional insights into the employment dynamics of central cities and suburbs during the last twenty years. Received: 25 July 2000 / Accepted: 29 May 2001     

Macroscopic and crystallographic density of solid-state extruded polyethylene

Summary The influence of draw ratio on macroscopic and crystallographic density of polyethylene with different initial morphologies, has been investigated by solid-state extrusion. An initial drop followed by an increase in macroscopic density as a function of draw ratio has been observed. Since precision X-ray measurements of unit cell parameters showed no variation of crystallographic density, it was concluded that plastic deformation of polyethylene upon drawing proceeds with a decrease of the degree of crystallinity. This was confirmed by differential scanning calorimetry.     

Influence of halide ions and alloy microstructure on the passive and localized corrosion behavior of alloy 22

Alloy 22 (N06022) is the current candidate alloy used to fabricate the external wall of the high-level nuclear waste containers for the Yucca Mountain repository. It was of interest to study and compare the general and localized corrosion susceptibility of Alloy 22 in fluoride and chloride solutions at 90 °C. Standard electrochemical tests such as cyclic potentiodynamic polarization, amperometry, and electrochemical impedance spectroscopy were used. Studied variables included the solution pH and the alloy microstructure (thermal aging). Results show that Alloy 22 is highly resistant to general corrosion in all the solutions tested. Thermal aging is not detrimental and even seems to be slightly beneficial for general corrosion at the higher solution pHs. Pitting corrosion was never observed. Crevice corrosion was found only for high chloride-containing solutions after anodic polarization. The presence of fluoride ions together with chloride ions seems to increase the susceptibility of Alloy 22 to crevice corrosion compared to pure chloride solutions. This article is based on a presentation made in the symposium “Effect of Processing on Materials Properties for Nuclear Waste Disposition,” November 10–11, 2003, at the TMS Fall meeting in Chicago, Illinois, under the joint auspices of the TMS Corrosion and Environmental Effects and Nuclear Materials Committees.