Characterization of two-phase nickel aluminides produced by pressure-assisted combustion synthesis

Two-phase (B2+L1₂) nickel aluminide intermetallic compounds were synthesized by the pressure-assisted volume combustion synthesis (CS). The production and characterization of the samples containing NiAl+Ni₃Al were investigated. Aluminum (99% pure, 15 μm) and carbonyl nickel (99.8 pure, 4-7 μm) powders were used. The production of intermetallic compound was carried out at 1050 °C under 150 MPa uniaxial pressure in open air atmosphere in an electrical resistance furnace for 60 min. The formation temperature of intermetallic compound was determined by differential scanning calorimeter (DSC) analysis, and exothermic temperature of powder mixture was determined as 653 °C. The characterization of samples was confirmed by optical microscope, SEM and XRD analysis. It was observed that the structure of compound has very low porosity and the formation of NiAl was completed successfully. The relative density of test materials measured according to Archimedes’ principle was 98.04%. The microhardness of test materials was about 351 HVN₁.     

Growth morphology and phase analysis of titanium-based coating produced by thermochemical method

In the present study, high-speed tool steel was used to coat titanium by pack cementation technique. Coatings show a growth morphology similar to that of the chemical vapor deposition method. Time and temperature of the coating affects its growth morphology. Coating obtained at low temperature (900 °C) yields morphology with growth of tiny particles while coating produced at high temperature (1000 °C) has a morphology with coarser particles. Phase structure of the layers also varies depending on the process time and temperature. Short coating duration yields TiC_0.3N_0.7 phase structure, whose composition is close to TiN whereas long coating duration combined with high temperature yields TiC_0.7N_0.3, whose composition is close to TiC. Mechanical properties such as hardness and resistance to abrasion also reflect changes in phase structures of different types of coating.     

An evaluation of Al2O3-ZrO2 composites produced by coprecipitation method

The objective of this work is to produce Al₂O₃-ZrO₂ composite from nano-sized powders processed by coprecipitation method. Al₂O₃ and mixture of Al₂O₃ + 10 wt.% ZrO₂ precipitated successfully by chemical route from aluminum sulfate and zirconium sulfate were pressed under uniaxial compression of 170 MPa and sintered at 1600 °C for 1 h. SEM investigations revealed that, pure alumina sample has a microstructure with coarse grains which anisotropically grown up to 30-40 μm in size. In alumina-zirconia composite, the structure consists of very fine equiaxed grains of typically 2 μm in which zirconia precipitates were uniformly dispersed. By adding zirconia to alumina, hardness and indentation fracture toughness were increased from 11.6 GPa to 16.8 GPa and from 3.2 MPa m^1/2 to 4.9 MPa m^1/2, respectively. Improvement in fracture toughness was attributed to bridging effects of zirconia particles as well as transformation toughening.     

Effect of Boron and Heat Treatment on Mechanical Properties of White Cast Iron for Mining Application

 Heat treatment methods were applied to white cast iron for improving the impact and wear resistance. Additionally, chemical composition optimization was made. Furthermore, the effect of boron addition on such applications was investigated. Samples were investigated by using optical and electron microscope methods. Hardness, wear and impact tests were conducted. The results showed that the secondary carbides in the standard alloy were iron-enriched, needle-like carbides M3C when the boron-added alloy contained Fe23(C,B)6 type, globular secondary carbides. It was concluded that heat treatment B provided higher wear and hardness properties, compared to the standard heat treatment. Optimum mechanical properties were obtained by lower destabilisation temperatures and increasing temperature reduced the wear resistance and hardness.     

Characterization of cryogenic heat treated Vanadis 4 PM cold work tool steel

The amount of retained austenite in the quenched cold work tool steel sample is 17.7%, in the condition of sub-zero heat treated and double tempered samples following by quenching is 1.9% determined by XRD analysis. The types of carbides (MC, M₇C₃, M₂₃C₆) present in the structure was determined by XRD and SEM-EDS analysis. The hardness of test samples were 865 HV(0.1) for quenched sample and 785 HV(0.1) forth sample subjected to sub-zero treatment and double tempered after the quenching.     

Investigation of dual phase transformation of commercial low alloy steels: Effect of holding time at low inter-critical annealing temperatures

Dual phase steels are a class of steels characterized by a microstructure consisting of a soft ferrite matrix with hard martensite islands at the grain boundaries. The temperature in the dual phase (α + γ) region and the holding time are two important parameters in the intercritically annealing process. In this study, different grades of commercial low alloy steels have been heat treated to a constant annealing temperature by changing the holding time. It is observed that the effect of holding time is dependent on the steel composition. In this context, a microstructural examination has been carried out using optical, scanning electron microscope and electron probe micro-analysis and hardness values have been determined.     

Effect of Intercritical Annealing Parameters on Dual Phase Behavior of Commercial Low-Alloyed Steels

 It is known that dual phase (DP) heat treatments and alloying elements have a strong effect on martensitic transformations and mechanical properties. In the present work, the effects of some intercritical annealing parameters (heating rate, soaking temperature, soaking time, and quench media) on the microstructure and mechanical properties of cold rolled DP steel were studied. The microstructure of specimens quenched after each annealing stage, was analyzed using optical microscopy. The tensile properties, determined for specimens submitted to complete annealing cycles, are influenced by the volume fractions of multi phases (originated from martensite, bainite and retained austenite), which depend on annealing processing parameters. The results obtained showed that the yield strength (YS) and the ultimate tensile strength (UTS) increase with the increasing intercritical temperature and cooling rate. This can be explained by higher martensite volume ratio with the increased volume fraction of austenite formed at the higher temperatures and cooling rates. The experimental data also showed that, for the annealing cycles carried out, higher UTS values than ~ 800 MPa could be obtained with the S3 steel grade.     

The first Flaviviridae symposium

The first annual Flaviviridae Symposium, sponsored by ICN Pharmaceuticals Inc., was held in Lyon, France, on 9 October, 1997, to communicate current understanding on the Flaviviridae. This multidisciplinary symposium attracted over 300 international delegates and presentations covered virology, viral pathogenesis, potential therapies and strategies for vaccine development. The symposium reviewed the research area that may lead to the discovery and design of human and veterinary medicines against members of this virus family.