Sintering studies of nano-crystalline zinc oxide

Sintering and grain growth of nano-crystalline undoped ZnO has been studied in detail over a wide range of temperature and holding time. Below 800 °C, sintering of over 70% theoretical density is not observed, irrespective of particle size. At 900 °C for 6 h, the nano-crystalline sample sinters to 99% of theoretical density whereas the density for as received sample is 93% of theoretical density. However, at 1300 °C or higher, the densification is found to be much faster and after a few hours becomes independent of holding time. Grain growth studies reveal a similar feature of attaining saturation over holding time. The average saturated grain size is found to be ∼1.5 and ∼2.2 μm at 800 and 900 °C, respectively, while at 1300 °C or higher, it is in between 12 and 13 μm.     

Cardiorespiratory effects of conventional and high frequency ventilation in rabbits with bilateral pneumothoraces and surfactant depleted lungs

We compared high frequency ventilation (HFV) to conventional mechanical ventilation (CMV) under normoxic and normocapnic condition in surfactant depleted rabbits with bilateral pneumothoraces. We hypothesized that lower airway pressures would be required with HFV under these conditions. We applied CMV and HFV in 8 anaesthetized rabbits with a prototype ventilator at frequencies of 30, 100, 200, and 300 cycles/min. A positive end-expiratory pressure (PEEP) just below the pressure sufficient to open the air leak from the pneumothoraces was applied at all frequencies. Airway pressures, gas exchange, heart rate, and mean arterial pressure were recorded. Peak airway pressure decreased significantly from 2.50 to 2.10 kPa when the frequency of ventilation was increased from 30 to 300 cycles/min. There were no significant changes in mean airway pressure, PaO2, arterial pH, heart rate, and mean arterial pressure when HFV was compared to CMV. In conclusion, during HFV peak airway pressures measured at the mouth were decreased. Our ability to maintain adequate gas exchange in the face of ongoing pulmonary air leaks may reflect lower alveolar pressures.     

Anhydrous esterification of myristic acid with propylene: Ion exchange resin and acid-treated clay as catalysts

Anhydrous esterification of myristic acid with propylene was carried out in the temperature range of 110–145°C and pressure from 190–195 psig in the presence of Amberlyst-15 (cation exchange resin) and Filtrol-24 (acid-treated clay) as catalysts. The product ester, isopropyl myristate finds use in cosmetic and topical medicinal preparations where good absorption through the skin is desired. Filtrol-24 is the catalyst of choice, and the recommended operating temperature is 130°C with a pressure of 190 psig.     

Studies on the synthesis of SAPO-5

Silicoaluminophosphate (SAPO-5) molecular sieves have been synthesised from reaction mixtures having a molar composition of: 0.7–1.0 Al₂O₃:0.7–1.0 P₂O₅:0.01–2.0 SiO₂:xR:40 H₂O (where R = (C₂H₃)₃N or (C₂H₃)₄NOH and x = 1.5–2.5 for (C₂H₅)⁵N and 0.5 for (C₂H₅)₄NOH, at 473 K using various sources of alumina and silica. The effects of (i) varying the crystallinity of the alumina source (boehmite) and (ii) the use of different silica sources such as freshly prepared silica either from sodium silicate or paddy husk extract, silica gel from commercial water-glass, and tetraethyl orthosilicate have been studied. The crystallinity of boehmite has been found to have a strong effect on its reactivity towards the formation of SAPO-5. The activity of boehmite for SAPO-5 formation increased with a decrease in its crystallinity (or with increase in its moisture content). Any silica source devoid of sodium ions could be employed for the synthesis of SAPO-5. The process of crystallisation started as early as within 1.5 h of reaction and incorporation of silicon into the AlPO₄ framework has been noted at this stage. Formation of some tridymite phase as impurity has been observed under conditions such as (i) SiO₂ concentration > 1.7 mole and (ii) x > 2.0 when R = (C²H₅)₃N.     

Corrosion failure of Zn–Al detonator housing

Some batches of detonator housings made up of Chromium plated Zn–Al alloy were found in an extensively cracked condition after few months of storage at room temperature. An analysis of the failure showed that the cracks were due to intergranular corrosion facilitated by segregation of lead at the grain boundaries. Improper chromium plating further aggravated the corrosion problem. This failure case emphasises the need for strict control of chemical composition for components made from Zn–Al alloy and the process of Cr plating of the components.