Laboratory Studies to Determine Suitable Chemicals to Improve Oil Recovery from Garzan Oil Field

Garzan oil field is located at the south east of Turkey. It is a mature oil field and the reservoir is fractured carbonate reservoir. After producing about 1% original oil in place (OOIP) reservoir pressure started to decline. Waterflooding was started in order to support reservoir pressure and also to enhance oil production in 1960. Waterflooding improved the oil recovery but after years of flooding water breakthrough at the production wells was observed. This increased the water/oil ratio at the production wells. In order to enhance oil recovery again different techniques were investigated. Chemical enhanced oil recovery (EOR) methods are gaining attention all over the world for oil recovery. Surfactant injection is an effective way for interfacial tension (IFT) reduction and wettability reversal. In this study, 31 different types of chemicals were studied to specify the effects on oil production. This paper presents solubility of surfactants in brine, IFT and contact angle measurements, imbibition tests, and lastly core flooding experiments. Most of the chemicals were incompatible with Garzan formation water, which has high divalent ion concentration. In this case, the usage of 2-propanol as co-surfactant yielded successful results for stability of the selected chemical solutions. The results of the wettability test indicated that both tested cationic and anionic surfactants altered the wettability of the carbonate rock from oil-wet to intermediate-wet. The maximum oil recovery by imbibition test was reached when core was exposed 1-ethly ionic liquid after imbibition in formation water. Also, after core flooding test, it is concluded that considerable amount of oil can be recovered from Garzan reservoir by waterflooding alone if adverse effects of natural fractures could be eliminated.     

Diluted chemical bath deposition of CdZnS as prospective buffer layer in CIGS solar cell

In this study, dilute chemical bath deposition technique has been used to deposit CdZnS thin films on soda-lime glass substrates. The structural, morphological, optoelectronic properties of as-grown films have been investigated as a function of different Zn²⁺ precursor concentrations. The X-ray diffractogram of CdS thin-film reveals a peak corresponding to (002) plane with wurtzite structure, and the peak shift has been observed with the increase of the Zn²⁺ concentration upon formation of CdZnS thin film. From morphological studies, it has been revealed that the diluted chemical bath deposition technique provides homogeneous distribution of film on the substrate even at a lower concentration of Zn²⁺. Optical characterization has shown that the transparency of the film is influenced by Zn²⁺ concentration and when the Zn²⁺ concentration is varied from 0 M to 0.0256 M, bandgap values of resulting films range from 2.42 eV to 3.90 eV while. Furthermore, electrical properties have shown that with increasing zinc concentration the resistivity of the film increases. Finally, numerical simulation validates and suggests that CdZnS buffer layer with composition of 0.0032 M Zn²⁺ concentration would be a promising candidate in CIGS solar cell.     

纳米药物非临床药代动力学的研究策略及关注要点

随着纳米技术的迅速发展，纳米药物的研发已成为目前药物创新的发展方向之一。纳米药物具有基于纳米结构的尺度效应，其药代动力学特征与普通药物相比存在明显差异，其药代动力学研究与普通药物相比也有其特殊性。本文着重探讨纳米药物的非临床药代动力学的研究策略及关注要点，包括受试物、体内/外试验、生物样本分析、数据评价分析等，期望为研发者提供参考。     

Polysorbate identity and quantity dictate the extensional flow properties of protein-excipient solutions

While protein medications are promising for treatment of cancer and autoimmune diseases, challenges persist in terms of development and injection stability of high-concentration formulations. Here, the extensional flow properties of protein-excipient solutions are examined via dripping-onto-substrate extensional rheology, using a model ovalbumin (OVA) protein and biocompatible excipients polysorbate 20 (PS20) and 80 (PS80). Despite similar PS structures, differences in extensional flow are observed based on PS identity in two regimes: at moderate total concentrations where surface tension differences drive changes in extensional flow behavior, and at small PS:OVA ratios, which impact the onset of weakly elastic flow behavior. Undesirable elasticity is observed in ultra-concentrated formulations, independent of PS identity; higher PS contents are required to observe these effects than in analogous polymeric excipient solutions. These studies reveal novel extensional flow behaviors in protein-excipient solutions, and provide a straightforward methodology for assessing the extensional flow stability of new protein-excipient formulations.     

Synthesis and performance evaluation of a new drag reducer based on acrylamide/12-allyloxydodecyl acid sodium

Hydraulic fracturing with slickwater is a field-proven stimulation technology used in tight reservoirs. Because of the high pumping rate associated with slickwater fracturing, drag reduction (DR) is critical in minimizing pressure drop and the success of oilfield operations. In this paper, a new type of drag reducer (SPR) was synthesized with acrylamide and 12-allyloxydodecyl acid sodium, and its drag reduction performance was evaluated. The results showed that the new drag reducer features low molecular weight, fast-dissolving rate and low interfacial tension. The algorithm of estimating the drag reduction rate of non-Newtonian fluid SPR was proposed and validated. Empirical or semianalytical models for estimating the friction ratio (σ) or friction factor (λ or f) were used to simulate the turbulence behavior of the SPR drag reducer under different Reynolds numbers (Re). The modified Virk's correlation could accurately model the turbulent behavior of the SPR drag reducer. A unified calculation formula was established in this study for different pipe diameters.     

煤矸石粉/聚酯纤维沥青混合料盐冻损伤研究EI北大核心CSCD

针对煤矸石粉替代率50%、聚酯纤维掺量0.4%的沥青混合料,开展盐冻耦合作用(NaCl溶液质量分数为0%、7.0%、13.0%、26.5%,冻融循环次数为0、2、4、6、8)下的半圆弯曲(SCB)试验,分析了盐冻耦合作用对SCB试件内部损伤劣化过程的影响.结果表明:NaCl溶液质量分数为13.0%、冻融循环为8次时,盐冻耦合作用对沥青混合料的侵蚀破坏作用最强,试件内部损伤最严重;在煤矸石粉与矿粉质量比为1∶1、聚酯纤维掺量为0.4%的条件下,沥青混合料能够形成高黏性、致密、厚实的沥青膜以及由纤维形成的三维网状结构,从而显著降低盐冻侵蚀对沥青混合料的损伤.通过Poly2D模型对SCB试件的极限拉应力损伤量进行拟合,拟合系数为0.944.     

Organofluorine Hydrazone Derivatives as Multifunctional Anti-Alzheimer's Agents with CK2 Inhibitory and Antioxidant Features

A set of novel hydrazone derivatives were synthesized and analyzed for their biological activities. The compounds were tested for their inhibitory effect on the phosphorylating activity of the protein kinase CK2, and their antioxidant activity was also determined in three commonly used assays. The hydrazones were evaluated for their radical scavenging against the DPPH, ABTS and peroxyl radicals. Several compounds have been identified as good antioxidants as well as potent protein kinase CK2 inhibitors. Most hydrazones containing a 4-N(CH₃)₂ residue or perfluorinated phenyl rings showed high activity in the radical-scavenging assays and possess nanomolar IC₅₀ values in the kinase assays.     

The structure,vacancy characteristics,and magnetic properties of GdMn1-xCrxO3 ceramics

To investigate the evolution of the structural and enhanced magnetic properties of GdMnO₃ systems induced by the substitution of Mn with Cr, polycrystalline GdMn_1-xCr_xO₃ samples were synthesized via solid-state reactions. XRD characterization shows that all GdMn_1-xCr_xO₃ compounds with single-phase structures crystallize well and that Cr³⁺ ions entering the lattice sites of GdMnO₃ induce structural distortion. SEM results indicate that the grain size of the synthesized samples (a few microns) decreases as the Cr substitution concentration increases. Positron annihilation lifetime spectroscopy reveals that vacancy-type defects occur in GdMn_1-xCr_xO₃ ceramics and that the vacancy size and concentration clearly change with the Cr content. The temperature and field dependence of the magnetization curves show that Cr substitution significantly influences the magnetic ordering of the gadolinium sublattice, improving the weak ferromagnetic transition temperature and magnetization of GdMn_1-xCr_xO₃. The enhanced magnetization of GdMn_1-xCr_xO₃ is closely related to the vacancy defect concentration.     

Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

Composites based on hafnium carbide and reinforced with continuous naked carbon fiber with and without PyC interface were prepared at low temperature by precursor infiltration and pyrolysis and chemical vapor deposition method. The microstructure, mechanical property, cyclic ablation and fiber bundle push-in tests of the composites were investigated. The results show that after three times ablation cycles, the bending strength of samples without PyC interface decreased by 63.6 %; the bending strength of samples with PyC interface only decreased by 37.8 %. The force displacement curve of the samples with PyC interface presented a well pseudoplastic deformation state. The mechanical behavior difference of two kinds of composites was due to crucial function of PyC interface phase including protection of fiber and weakening of fiber/matrix interface.     

Research and development of liquid hydrogen (LH2) temperature monitoring system for marine applications

Monitoring the temperature in liquid hydrogen (LH₂) storage tanks on ships is important for the safety of maritime navigation. In addition, accurate temperature measurement is also required for commercial transactions. Temperature and pressure define the density of liquid hydrogen, which is directly linked to trading interests. In this study, we developed and tested a liquid hydrogen temperature monitoring system that uses platinum resistance sensors with a nominal electrical resistance of approximately 1000 Ω at room temperature, PT-1000, for marine applications. The temperature measurements were carried out using a newly developed temperature monitoring system under different pressure conditions. The measured values are compared with a calibrated reference PT-1000 resistance thermometer. We confirm a measurement accuracy of ±50 mK in a pressure range of 0.1 MPa–0.5 MPa.