Diameter controlled chemical vapor deposition synthesis of single-walled carbon nanotubes

In this study, we systematically investigated the influence of catalyst preparation procedures on the mean diameter of single-walled carbon nanotubes (SWNTs) synthesized by the alcohol catalytic chemical vapor deposition (ACCVD) process. It was found that the SWNT diameter is dependent upon both reduction temperature and time, with lower reduction temperature and/or shorter reduction time resulting in smaller diameter SWNTs. The morphology of the SWNTs also changed from vertically aligned to randomly oriented when the reduction temperature was below 500 degrees C. We also found that introducing a small amount of water during the catalyst reduction stage significantly decreased the mean diameter of the SWNTs. Lastly, we report on the use of a new binary catalyst system in which rhodium was combined with cobalt. This new Co/Rh combination produced SWNTs of smaller diameter than the conventional Co/Mo catalyst.     

Diameter-controlled and nitrogen-doped vertically aligned single-walled carbon nanotubes

Diameter controlled and vertically aligned single-walled carbon nanotubes were synthesized from pure and mixed ethanol/acetonitrile feedstock. With increasing acetonitrile concentration in the feedstock, nitrogen incorporation into the sp² carbon network increased until saturating at approximately one atomic percent. The incorporation of nitrogen correlates with a significant diameter reduction from a mean diameter of 2.1 nm down to 0.7 nm. Heteroatom-mediated diameter control is independent of catalyst preparation and represents a versatile tool for the direct synthesis of tailored single-walled carbon nanotubes.