Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Impact of gypsum on flotation of scheelite and fluorite using sodium oleate as collector

ABSTRACT

In this study, effect of calcium and gypsum on scheelite and fluorite was investigated using sodium oleate as collector. Micro-flotation and contact angle results showed that the adsorption of calcium could inhibit the hydrophobicity of scheelite and fluorite. Moreover, sulfate could enhance the inhibition. FT-IR results showed that calcium could be priori precipitated into calcium oleate and adsorb on mineral surface. The adsorption of calcium could increase the scheelite potential to IEP, while it showed limited effect on fluorite potential. However, the interaction of calcium on scheelite and fluorite in gypsum solution was more complex than that in calcium solution.     

Controlled Secure Direct Communication Protocol via the Three-Qubit Partially Entangled Set of States

In this paper, we first re-examine the previous protocol of controlled quantum secure direct communication of Zhang et al.’s scheme, which was found insecure under two kinds of attacks, fake entangled particles attack and disentanglement attack. Then, by changing the party of the preparation of cluster states and using unitary operations, we present an improved protocol which can avoid these two kinds of attacks. Moreover, the protocol is proposed using the three-qubit partially entangled set of states. It is more efficient by only using three particles rather than four or even more to transmit one bit secret information. Given our using state is much easier to prepare for multiqubit states and our protocol needs less measurement resource, it makes this protocol more convenient from an applied point of view.     

Microwave drying performance of lignite with the assistance of biomass-derived char

Microwave lignite drying with assistance of biomass-derived char was addressed and effect of bio-char on drying rate and energy consumption was investigated in this work. Effective diffusion coefficient and activation energy for the drying process were also analyzed. The results indicated the drying process was largely dependent on the variation of sample temperature. Bio-char originated from pine wood was most favorable for lignite drying, considering its better promoting effect and advanced security. There existed an optimal bio-char addition ratio for drying process at different power. The corresponding optimal ratio was 10% at 231?W and 15% at 385?W, at which the biggest drying rate and the least energy consumption were reached. It was compared lignite drying initiated at 385?W was better for energy conservation. Effective diffusivity was improved and activation energy was simultaneously reduced, with the addition of bio-char. The minimum activation energy was 15.54?W?·?g^?1, which was gained at bio-char addition ratio of 10%. The results revealed the effect of bio-char on depressing activation energy could rival that of metal-based additives. The drying process with assistance of microwave and bio-char could present technical and economical benefits on lignite upgrading.     

A facile method for preparation of PGS@ZB‐N and gas‐sol alternating synergistic effect for fire resistance of EVA

Through the simple precipitation of palygorskite (PGS) by zinc borate (ZB) (to make PGS@ZB) and the decoration of PGS@ZB by dodecylamine (N), a novel organic‐inorganic@inorganic hybrid flame retardant of PGS@ZB‐N was prepared and was incorporated with ethylene vinyl acetate copolymer (EVA) to improve its flame retardance. The structure and morphology of PGS@ZB‐N were characterized by Fourier transform infrared (FTIR) spectroscopy, X‐ray diffraction (XRD), and scanning electron microscopy (SEM), and it was confirmed that the PGS@ZB‐N hybrid had been successfully prepared. The flame retardancy and burning behavior of EVA/PGS@ZB‐N/EG (EG = expandable graphite) composite were studied through thermogravimetric analysis (TGA), limiting oxygen index (LOI), UL‐94 (by the vertical burning test), and cone calorimeter test (CCT) characterizations. The prepared EVA/PGS@ZB‐N/EG composite obtained an LOI value of 41.2% with the addition of 30 wt% PGS@ZB‐N/EG. It was found that EVA/PGS@ZB‐N/EG was protected through a gas phase and condensed phase alternating synergistic effect mechanism.